In this work we demonstrate comprehensive studies on graphene oxide (GO) and reduced graphene oxide (rGO) based saturable absorbers (SA) for mode-locking of Er-doped fiber lasers. The paper describes the fabrication process of both saturable absorbers and detailed comparison of their parameters. Our results show, that there is no significant difference in the laser performance between the investigated SA. Both provided stable, mode-locked operation with sub-400 fs soliton pulses and more than 9 nm optical bandwidth at 1560 nm center wavelength. It has been shown that GO might be successfully used as an efficient SA without the need of its reduction to rGO. Taking into account simpler manufacturing technology and the possibility of mass production, GO seems to be a good candidate as a cost-effective material for saturable absorbers for Er-doped fiber lasers.

The nitrogen doping of titanium dioxide nanotubes (TiO₂ NTs) was investigated as a result of well-controlled plasma nitriding of TiO₂ NTs at a low temperature. This way of nitrogen doping is proposed as an alternative to chemical/electrochemical methods. The plasma nitriding process was performed in a preparation chamber connected to an X-ray photoelectron spectroscopy (XPS) spectrometer, and the nitrogen-doped TiO₂ NTs were next investigated in situ by XPS in the same ultrahigh vacuum (UHV) system. The collected high-resolution (HR) XPS spectra of N 1s, Ti 2p, O 1s, C 1s, and valence band (VB) revealed the formation of chemical bonds between titanium, nitrogen, and oxygen atoms as substitutional or interstitial species. Moreover, the results provided a characterization of the electronic states of N–TiO₂ NTs generated by various plasma nitriding and annealing treatments. The VB XPS spectrum showed a reduction in the TiO₂ band gap of about 0.6 eV for optimal nitriding and heat-treated conditions. The TiO₂ NTs annealed at 450 or 650 °C in air (ex situ) and nitrided under UHV conditions were used as reference materials to check the formation of Ti–N bonds in the TiO₂ lattice with a well-defined structure (anatase or a mixture of anatase and rutile). Scanning electron microscopy microscopic observations of the received materials were used to evaluate the morphology of the TiO₂ NTs after each step of the nitriding and annealing treatments.