In line with sustainable construction goals, this study investigates the synergistic use of amine-based grinding aids (GAs), triethanolamine (TEA), and triisopropanolamine (TIPA) to enhance grinding performance and cement properties. GAs were physically blended at varying TEA/TIPA ratios, and their effects on grinding efficiency, CO₂ emissions, and environmental footprint were assessed based on energy consumption per target Blaine fineness. The interaction of blended GAs with Ca²⁺ ions was modeled to understand adsorption behavior. Cement particle size distribution (PSD), Hausner ratio, Carr index, and angle of repose were analyzed to evaluate powder flowability. Scanning electron microscopy (SEM) was employed to examine microstructural changes. Finally, the Taguchi method statistically analyzed the effective parameters influencing system performance. Results demonstrated that the optimized blend containing 25% TEA and 75% TIPA improved grinding performance, enhanced polymer–ion interactions, refined PSD, and significantly increased powder flowability. Overall, the study underscores the potential of amine-based polymeric GAs in producing environmentally friendly, high-performance cement composites. Using a Taguchi design with the larger-is-better S/N criterion, the optimal formulation was determined to be 25% TEA and 75% TIPA at a dosage of 0.10%. ANOVA results indicated that the TEA content was the most significant factor, while the dosage had no statistically significant effect.

This study investigated the effects of waste steel fiber and high-volume blast furnace slag (BFS) substitution on the mechanical and physical properties of three-dimensional printable concrete (3DPC) to improve its environmental performance. BFS was substituted for cement at 0%, 25%, 50%, and 75% by volume. Waste steel fibers were added to the mixtures at three lengths (5, 10, and 15 mm) and two volumetric ratios (0.5% and 1.0%). Twenty-eight mixtures were optimized based on extrudability, buildability, and shape stability criteria. Parameters such as compressive and flexural strength, surface moisture content, and drying shrinkage were evaluated. The results showed that using up to 0.5% waste steel fibers increased compressive strength by up to 23%, but decreased it to a level of 1%. Fiber reinforcement improved the flexural strength of all blends by up to 53% at both ages, regardless of fiber ratio or length. Increasing the BFS substitution rate generally increased surface moisture however, this value decreased in mixtures containing 75% BFS and silica fume. Furthermore, using steel fibers and in-creasing fiber length significantly improved the drying shrinkage performance of the mixtures.