In this study, the corrosion behavior of Cu_XCoCrMoNi (x = 0.3, 0.6, 0.9) high-entropy alloys (HEAs) in 3.5% NaCl solution is systematically investigated. The alloy samples show a strong link between copper content and corrosion resistance. It is noteworthy that an increase in copper content promotes element segregation, resulting in an increase in corrosion current density from 2.138 × 10⁻⁷ μA/cm² to 1.8989 × 10⁻⁶ μA/cm² and a decrease in charge transfer resistance from 182.6 Ω·cm² to 42.34 Ω·cm². In addition, electrochemical experiments demonstrate that lowering the copper content in the alloys reduces the spread and depth of corrosion. All alloys exhibit n-type semiconductor behavior, with donor density increasing from 4.792 × 10²³ cm⁻³ to 5.581 × 10²³ cm⁻³ with increasing copper content. Notably, the passive film is characterized by the presence of Cr₂O₃ and Cu₂O as its main constituents. As the copper content in the HEA increases, higher levels of copper oxides in the passive film inhibit the formation of chromium oxides. This degrades the passive film quality, thereby diminishing the overall corrosion resistance.

AlCoCrFeNi high-entropy alloy coatings reinforced with different TiN contents (2 wt.%, 4 wt.%, and 6 wt.%) were fabricated on 304 stainless steel by laser cladding. The effects of TiN addition on the microstructure, hardness, friction behavior, and wear resistance of the coatings were investigated. Dry reciprocating sliding tests were conducted under a load of 10 N, a frequency of 5 Hz, a stroke length of 5 mm, and a duration of 20 min using GCr15 bearing steel balls as the counterpart. The results showed that the 2 wt.% TiN coating exhibited the best tribological performance within the investigated composition range, with a microhardness of 579.6 HV_0.5, a relatively low and stable friction coefficient of approximately 0.30–0.35, and a wear rate of 2.9 × 10⁻⁴ mm³/(N·m). When the TiN content increased to 4 wt.% and 6 wt.%, the wear resistance decreased, which was mainly associated with particle agglomeration, local stress concentration, and brittle spalling. These results indicate that appropriate TiN addition can improve the load-bearing capacity and wear resistance of laser-cladded AlCoCrFeNi coatings, providing a potential surface-strengthening strategy for 304 stainless steel components under dry sliding conditions.