Background: In this study, the light output of a cadmium tungstate (CdWO₄) single crystal was measured under various X-ray radiographic energies. Methods: A CdWO₄ single crystal (10 × 10 × 10 mm³) was exposed to X-rays in the 50–130 kVp range. Measurements were evaluated against published data for single crystals of equal dimensions (CaF₂:Eu and Lu₃Al₅O₁₂:Ce). Since the crystal was examined for application in medical imaging detectors, the emitted optical spectrum was classified with respect to the spectral compatibility of numerous commercial optical sensors. Results: The luminescence efficiency (LE) was found to constantly increase with X-ray energy and was higher than that of CaF₂:Eu for energies above 90 kVp. However, the efficiency of the previously published Lu₃Al₅O₁₂:Ce was found to be constantly higher than that of CdWO₄. The light emitted from CdWO₄ can be optimally detected by certain charge-coupled devices (CCDs), amorphous silicon photodiodes, and photocathodes. Conclusions: The high density (7.9 g/cm³) of CdWO₄ and the luminescence signal of this material make it suitable for medical imaging (such as dual energy), high-energy physics or for applications of scintillators in harsh environments.

The aim of this article is to evaluate optical characteristics, such as the intrinsic conversion efficiency and the inherent light propagation efficiency of three polymethyl methacrylate (PMMA)/methyl methacrylate (MMA) composite ZnCuInS/ZnS (core/shell) nanocrystal flexible films. The concentrations of these were 100 mg/mL, 150 mg/mL, and 250 mg/mL, respectively. Composite films were prepared by homogeneously diluting dry powder quantum dot (QD) samples in toluene and subsequently mixing these with a PMMA/MMA polymer solution. The absolute luminescence efficiency (AE) of the films was measured using X-ray excitation. A theoretical model describing the optical photon propagation in scintillator materials was used to calculate the fraction of the generated optical photons passed through the different material layers. Finally, the intrinsic conversion efficiency was calculated by considering the QD quantum yield and the optical photon emission spectrum.

Quantum dots (QDs) are quite interesting materials due to their unique chemical and physical properties. ZnCuInS/ZnS QDs can be produced either in hydrophobic or hydrophilic form, are non-toxic, and thus favorable for studies in the area of biology. Poly(methyl methacrylate) (PMMA) is a well-known biocompatible resin which is widely used in dentistry, ophthalmology, and orthopedic surgery. Four composite PMMA films of ZnCuInS/ZnS nanocrystals with maximum emission at 530 nm and concentrations of 1.0, 4.0, 6.0, and 10.0 %w/v, were prepared. X-ray irradiation was used to evaluate the volume homogeneity of the final samples, as a measure of QD dispersion. The luminescent efficiency was evaluated, under ultraviolet (UV) irradiation. The process of UV irradiation involved the experimental measurement of the forward luminescent light, as well as the backward luminescent light, in order to accurately calculate the energy quantum efficiency (EQE) of ZnCuInS/ZnS QDs. Reflected UV radiation was also measured, and results showed that it ranges from 2% to 6% approximately as the QD concentration rises from 1.0 %w/v to 10.0 %w/v. Beyond 6.0 %w/v, the reflected UV radiation remains essentially unchanged. Additionally, the reflected UV radiation remained unaffected as the power of the incident UV increased. Approximately 9% of incident UV radiation passed through the 1.0 %w/v sample, whereas for the samples with higher ZnCuInS/ZnS concentration, 0% UV radiation passed through. The EQE reached a maximum of about 45% with the 10.0 %w/v sample, while it remained practically unaffected relative to the increase of the emitted UV power. The homogeneity measurements revealed that the coefficient of variation (CV) increased with increasing concentration, for the 1.0, 4.0, and 6.0 %w/v samples. The minimum CV was obtained for the sample of 10.0 %w/v due to the incorporation of sonication in the final product, during the fabrication process.

Background: In this research, the response of a 10 × 10 × 10 mm³ commercially available PbF₂ crystal was experimentally assessed under X-ray and gamma ray radiation to verify the possible application of this material in X-ray medical imaging. Methods: The measurements were performed under X-ray from 50 to 130 kVp and gamma ray excitation (Tc-99m 140 keV and I-131 365 keV). The PbF₂ response was experimentally assessed by the determination of the absolute luminescence efficiency (AE), X-ray luminescence efficiency (XLE), and the stopping power of this scintillating crystal in terms of the energy absorption efficiency (EAE). The results were compared with bismuth germanate (BGO) crystal, which is commonly used in medical imaging modalities. Results: The AE of PbF₂ gradually decreased from 50 kVp up to 130 kVp. The maximum value was 0.61 efficiency units (EU) at 140 keV, and the minimum value was 0.03 EU at 71 keV (130 kVp). Similarly, low values appeared for the XLE, where the maximum value was 16.9 × 10⁻⁵ at 140 keV. Conclusions: These findings show that the PbF₂ scintillator has unacceptably low luminescence efficiency. Although PbF₂ can effectively absorb radiation, the scintillation light, at room temperatures, is negligible, and, thus, it could not be used in medical imaging applications in the examined energy range.

This study examines the luminescence performance of two single-crystal scintillators under X-ray excitation, as a function of temperature. Two identical cubic samples of bismuth germanate (Bi₄Ge₃O₁₂-BGO) and barium fluoride (BaF₂) crystals are irradiated by a medical-type X-ray source, and their luminescence output is collected and measured while they are heated from room temperature up to 174 °C. The luminescence efficiencies of BGO and BaF₂ scintillators decreased by 87.5% and 79.48%, respectively, with increasing temperature. BGO showed higher luminescence efficiency results in most of the examined temperature range; however, BaF₂ minimized the differences at temperatures approaching 174 °C. The combination of economic accessibility and thermal performance at higher temperatures renders BaF₂ a good choice for harsh environments and large-scale applications where budget and durability are as critical as performance.