Tungsten trioxide is the second most commonly used semiconducting metal oxide in gas sensors. Semiconducting metal oxide (SMOX)-based sensors are small, robust, inexpensive and sensitive, making them highly attractive for handheld portable medical diagnostic detectors. WO₃ is reported to show high sensor responses to several biomarkers found in breath, e.g., acetone, ammonia, carbon monoxide, hydrogen sulfide, toluene, and nitric oxide. Modern material science allows WO₃ samples to be tailored to address certain sensing needs. Utilizing recent advances in breath sampling it will be possible in the future to test WO₃-based sensors in application conditions and to compare the sensing results to those obtained using more expensive analytical methods.

In order to increase their stability and tune-sensing characteristics, metal oxides are often surface-loaded with noble metals. Although a great deal of empirical work shows that surface-loading with noble metals drastically changes sensing characteristics, little information exists on the mechanism. Here, a systematic study of sensors based on rhodium-loaded WO₃, SnO₂, and In₂O₃—examined using X-ray diffraction, high-resolution scanning transmission electron microscopy, direct current (DC) resistance measurements, operando diffuse reflectance infrared Fourier transform (DRIFT) spectroscopy, and operando X-ray absorption spectroscopy—is presented. Under normal sensing conditions, the rhodium clusters were oxidized. Significant evidence is provided that, in this case, the sensing is dominated by a Fermi-level pinning mechanism, i.e., the reaction with the target gas takes place on the noble-metal cluster, changing its oxidation state. As a result, the heterojunction between the oxidized rhodium clusters and the base metal oxide was altered and a change in the resistance was detected. Through measurements done in low-oxygen background, it was possible to induce a mechanism switch by reducing the clusters to their metallic state. At this point, there was a significant drop in the overall resistance, and the reaction between the target gas and the base material was again visible. For decades, noble metal loading was used to change the characteristics of metal-oxide-based sensors. The study presented here is an attempt to clarify the mechanism responsible for the change. Generalities are shown between the sensing mechanisms of different supporting materials loaded with rhodium, and sample-specific aspects that must be considered are identified.

WO₃ is a commonly used material for gas sensing. Although a great deal of research has been done on how to tune sensors based on WO₃, no clear consensus exists on what characteristics are inherent to the metal oxide: This work looks at six different WO₃ samples and aims to identify which characteristics are common to all materials. Specifically, the interaction of the samples with humidity is examined.

In this work, we have succeeded in synthesizing monoclinic and hexagonal La₂O₂CO₃ using two different routes and revealed that both of them are sensitive to CO₂ to the same degree. Moreover, we observed that the resistance of the sensor based on hexagonal phase is much higher and more stable than the one of the sensors based on the monoclinic phase. Using Operando and time resolved XRD measurements, we have also demonstrated that the resistivity of the sensor based on monoclinic La₂O₂CO₃ increases because of the material transformation into the hexagonal phase during an exemplarily aging process.

Industrial pollution and traffic emissions emit dangerous amounts of O₃, NO₂, VOCs and PM into environment, bringing higher incidence of morbidity and mortality in respiratory sicknesses [1].