Flexible plastic substrates are widely used in printed electronics; however, they cause major climate impacts and pose sustainability challenges. In recent years, paper-based electronics has been studied to increase the recyclability and sustainability of printed electronics. The aim of this paper is to analyze the printability and performance of metal conductor layers on different paper-based substrates using both flexography and screen printing and to compare the achieved performance with that of plastic foils. In addition, the re-pulpability potential of the used paper-based substrates is evaluated. As compared to the common polyethylene terephthalate (PET) substrate, the layer conductivity on paper-based substrates was found to be improved with both the printing methods without having a large influence on the detail rendering. This means that a certain surface roughness and porosity is needed for the improved ink transfer and optimum ink behavior on the surface of the substrate. In the case of uncoated paper-based substrates, the conductivity and print quality decreased by preventing the formation of the proper and intimate ink-substrate contact during the ink transfer. Finally, the re-pulpability trials together with layer quality analysis detected very good, coated substrate candidates for paper-based printed electronics competing with or even outperforming the print quality on the reference PET foil.

Printed flexible hybrid electronics (FHE) is finding an increasing number of applications in the fields of displays, sensors, actuators and in energy harvesting and storage. The technology involves the printing of conductive and insulating patterns as well as mounting electronic devices and circuits on flexible substrate materials. Typical plastic substrates in use are, for example, non-renewable-based poly(ethylene terephthalate) (PET) or poly(imides) (PI) with high thermal and dimensional stability, solvent resistance and mechanical strength. The aim of this study was to assess whether renewable-based plastic materials can be applied on sheet-to-sheet (S2S) screen-printing of conductive silver patterns. The selected materials were biaxially oriented (BO) bio-based PET (Bio-PET BO), poly(lactic acid) (PLA BO), cellulose acetate propionate (CAP BO) and regenerated cellulose film, NatureFlex™ (Natureflex). The biaxial orientation and annealing improved the mechanical strength of Bio-PET and PLA to the same level as the reference PET (Ref-PET). All renewable-based substrates showed a transparency comparable to the Ref-PET. The printability of silver ink was good with all renewable-based substrates and printed pattern resistance on the same level as Ref-PET. The formation of the printed pattern to the cellulose-based substrates, CAP BO and Natureflex, was very good, showing 10% to 18% lower resistance compared to Ref-PET and obtained among the bio-based substrates the smallest machine and transverse direction deviation in the S2S printing process. The results will open new application possibilities for renewable-based substrates, and also potentially biodegradable solutions enabled by the regenerated cellulose film and PLA.

In our research on sustainable solutions for printed electronics, we are moving towards renewable materials in applications, which can be very challenging from the performance perspective, such as printed circuit boards (PCB). In this article, we examine the potential suitability of wood-based materials, such as cardboard and veneer, as substrate materials for biodegradable solutions instead of the commonly used glass-fiber reinforced epoxy. Our substrate materials were coated with fire retardant materials for improved fire resistance and screen printed with conductive silver ink. The print quality, electrical conductivity, fire performance and biodegradation were evaluated. It was concluded that if the PCB application allows manufacturing using screen printing instead of an etching process, there is the potential for these materials to act as substrates in, e.g., environmental analytics applications.

The demand for printed electronics (PE) is expected to increase for improved functionality and autonomy of products in the context of the Internet of Things, especially for sensing and communication. With this trend, the environmental performance of novel technologies is of growing importance, and researchers are exploring ways to make them more environmentally friendly using bio-based substrates and additive printing methods. Conductive inks have the highest environmental impact in the life cycle of PE, and there are two options to decrease the impact: increase recycling rates or replace commonly used silver inks with less impactful materials such as copper or graphite. With the current mixed waste management system, a higher recycling rate for silver is not achievable. Copper and graphite have a lower environmental impact than silver, however, the electrical conductivity of copper and graphite inks is lower than silver ink. This article introduces a double-parameter comparison to simultaneously assess the environmental and electrical conductivity of PE using three inks of silver, copper, and graphite inks. Then based on the technical feasibility, this study proposes suitable applications for each substrate and ink combination.

The increasing environmental awareness is driving towards novel sustainable high-performance materials applicable for future manufacturing technologies like additive manufacturing (AM). Cellulose is abundantly available renewable and sustainable raw material. This work focused on studying the properties of thermoplastic cellulose-based composites and their properties using injection molding and 3D printing of granules. The aim was to maximize the cellulose content in composites. Different compounds were prepared using cellulose acetate propionate (CAP) and commercial cellulose acetate propionate with plasticizer (CP) as polymer matrices, microcellulose (mc) and novel cellulose-ester additives; cellulose octanoate (C8) and cellulose palmitate (C16). The performance of compounds was compared to a commercial poly(lactic acid)-based cellulose fiber containing composite. As a result, CP-based compounds had tensile and Charpy impact strength properties comparable to commercial reference, but lower modulus. CP-compounds showed glass transition temperature (Tg) over 58% and heat distortion temperature (HDT) 12% higher compared to reference. CAP with C16 had HDT 82.1 °C. All the compounds were 3D printable using granular printing, but CAP compounds had challenges with printed layer adhesion. This study shows the potential to tailor thermoplastic cellulose-based composite materials, although more research is needed before obtaining all-cellulose 3D printable composite material with high-performance.

Thermoplastic composite materials containing wood fibers are gaining increasing interest in the manufacturing industry. One approach is to use nano- or micro-size cellulosic fibrils as additives and to improve the mechanical properties obtainable with only small fibril loadings by exploiting the high aspect ratio and surface area of nanocellulose. In this study, we used four different wood cellulose-based materials in a thermoplastic polylactide (PLA) matrix: cellulose nanofibrils produced from softwood kraft pulp (CNF) and dissolving pulp (CNFSD), enzymatically prepared high-consistency nanocellulose (HefCel) and microcellulose (MC) together with long alkyl chain dispersion-improving agents. We observed increased impact strength with HefCel and MC addition of 5% and increased tensile strength with CNF addition of 3%. The addition of a reactive dispersion agent, epoxy-modified linseed oil, was found to be favorable in combination with HefCel and MC.