Selective laser melting technology makes it possible to produce 3D cellular lattice structures with controlled porosity. The paper reflects to machining and examination of structures with predefined distribution, shape and size of the pores. In the study, the porous structures of Ti6Al4V were investigated. The tests were carried out using structures of spatial architecture of Schwarz D TPMS geometry with a total porosity of 60% and 80% and various pore sizes. Dimensional accuracy of additively manufactured structures was measured in relation to the 3D model. Geometry of the final structure differed from the CAD model in the range ± 0.3 mm. The surface morphology and porosity of the solid struts were also checked. The mechanical properties of the structures were determined in a static compression test.

The development of dental implants has significantly advanced due to technological innovations aimed at improving their performance and patient outcomes. This work presents key factors influencing the success of dental implants, including osseointegration, which is the direct connection between living bone and the implant surface, and the various surface modifications that enhance this process. This review highlights the importance of surface roughness, chemical composition, and the use of bioactive coatings to promote better integration with surrounding bone tissue. Innovations such as nanotechnology, 3D printing, and smart surfaces are paving the way for more effective and personalized dental implant solutions. This review underscores the importance of ongoing research and development to improve success rates, enhance patient comfort, and reduce healing times. It focuses on creating cost-effective, reliable methods that integrate multiple functions, such as combining antibacterial and osteoconductive properties to improve overall implant performance.

Three-dimensional printing is a dynamically developing field of industry. Its main advantage is the small amount of waste, no need to use specialized tools, and easy control of the mechanical properties of the printed model. One of the most popular techniques of 3D printing is FDM. The main factor influencing the mechanical properties of 3D-printed materials is the filling density. The aim of this study was to determine the mechanical properties of porous structures with a porosity gradient of PLA samples printed using the FDM technique. The accuracy of mapping the structures by computed tomography was assessed, and then a static compression test was performed. It has been shown that the strength properties increased with the increase in the filling density. The highest value of compression strength, amounting to 41.2 MPa, was observed for samples made of PLA with an 80% filling degree, whereas the lowest value of compression strength was found in PLA-T samples with a filling degree of 10%, reaching only 0.6 MPa. It was found that not only the core filling density, but also the outer layers, influences the mechanical properties. The assessment of spatial architecture allowed for a qualitative and quantitative assessment. The obtained images from the computed tomograph showed that the designed sample models were correctly reproduced in the entire volume.

Titanium Grade 4 (Ti G4) is the most commonly used material for dental implants due to its excellent mechanical properties, chemical stability and biocompatibility. A thin, self-passive oxide layer with protective properties to corrosion is formed on its surface. However, the spontaneous TiO₂ layer is chemically unstable. In this work, the impact of autoclaving time on corrosion resistance of Ti G4 in artificial saliva solution with pH = 7.4 at 37 °C was studied. Ti G4 was sandblasted with white Al₂O₃ particles and autoclaved for 30–120 min. SEM, EDS, 2D roughness profiles, confocal laser scanning microscopy, and a Kelvin scanning probe were used for the surface characterization of the Ti G4 under study. In vitro corrosion resistance tests were conducted using open circuit potential, polarization curves, and electrochemical impedance spectroscopy measurements. It was found that Sa parameter, electron work function, and thickness of the oxide layers, determined based on impedance measurements, increased after autoclaving. The capacitive behavior and high corrosion resistance of tested materials were revealed. The improvement in the corrosion resistance after autoclaving was due to the presence of oxide layers with high chemical stability. The optimal Ti G4 surface for dentistry can be obtained by sandblasting with Al₂O₃ with an average grain size of 53 µm, followed by autoclaving for 90 min.

Construction of metallic implants with a porous structure that mimics the biomechanical properties of bone is one of the challenges of orthopedic regenerative medicine. The selective laser sintering technique (SLS) allows the production of complex geometries based on three-dimensional model, which offers the prospect of preparing porous metal implants, in which stiffness and porosity can be precisely adjusted to the individual needs of the patient. This requires an interdisciplinary approach to design, manufacturing and testing of porous structures manufactured by selective sintering. An important link in this process is the ability to assess the surface topography of the struts of porous structure. The paper presents a qualitative assessment of the surface morphology based on SEM studies and methodology that allows for quantitative assessment of stereometric structure based on micro-tomographic measurements.