This work demonstrates the preparation of high-surface-area activated carbon (AC) from Pisum sativum pods using ZnCl₂ and KOH as activating agents. The influence of CO₂ and N₂ gases during the carbonization process on the porosity of AC were studied. The highest specific surface area of AC was estimated at 1300 to 1500 m²/g, which presented characteristics of microporous materials. SEM micrographs revealed that chemical activation using an impregnation reagent ZnCl₂ increases the porosity of the AC, which in turn leads to an increase in the surface area, and the SEM image showed that particle size diameter ranged between 48.88 and 69.95 nm. The performance of prepared AC for adsorption of Acid Orange 7 (AO7) dye was tested. The results showed that the adsorption percentage by AC (2.5 g/L) was equal to 94.76% after just 15 min, and the percentage of removal increased to be ~100% after 60 min. The maximum adsorption capacity was 473.93 mg g⁻¹. A Langmuir model (LM) shows the best-fitted equilibrium isotherm, and the kinetic data fitted better to the pseudo-second-order and Film diffusion models. The removal of AO7 dye using AC from Pisum sativum pods was optimized using a response factor model (RSM), and the results were reported.

In all farming systems, weeds are the most expensive pest to manage, accounting for 30% of potential losses. In organic farming, the problem may be further amplified by restrictions on herbicides, thus making weeds the main problem faced by organic farmers in the field. In this sense, much research is focusing on the allelopathic potential of plants as an ecological weed control tool. Many plant species can release allelopathic compounds with high phytotoxicity that can be used in weed control. Species belonging to the Lamiaceae family have been studied widely for this purpose, and their essential oils (EOs) appear to be promising bioherbicides. However, there are still many challenges for their development. Considering these aspects, a review of the bioherbicidal effect of EOs from Mediterranean Lamiaceae could help identify the most effective ones and the challenges for their actual development.

The aim of this study was to analyze the effect of ZnO nanoparticles (ZnO NPs) on the biogas production from mechanically treated barley straw and to perform a techno-economic analysis based on the costs assessment and on the results of biogas production. The structural changes of mechanically pretreated barley straw were observed using FTIR, XRD, TGA, and SEM. Additionally, both green ZnO NPs prepared from red alga (Antithamnion plumula) extract and chemically prepared ZnO NPs were characterized by FTIR, XRD, SEM, and TEM, surface area, and EDX. The results revealed that the biogas production was slightly improved by 14.9 and 13.2% when the barley straw of 0.4 mm was mechanically pretreated with 10 mg/L of both green and chemical ZnO NPs and produced 390.5 mL biogas/g VS and 385 mL biogas/g VS, respectively. On the other hand, the higher concentrations of ZnO NPs equal to 20 mg/L had an inhibitory effect on biogas production and decreased the biogas yield to 173 mL biogas/g VS, which was less than the half of previous values. It was also clear that the mechanically treated barley straw of 0.4 mm size presented a higher biogas yield of about 340 mL/g VS, in comparison to 279 mL biogas/g VS of untreated biomass. The kinetic study showed that the first order, modified Gompertz and logistic function models had the best fit with the experimental data. The results showed that the nanoparticles (NPs) of the mechanically treated barely straw are a suitable source of biomass for biogas production, and its yields are higher than the untreated barley straw. The results of the cost-benefit analysis showed that the average levelized cost of energy (LCOE), adopting the best treatments (0.4 mm + 10 mg/L ZnO), is 0.21 €/kWh, which is not competitive with the other renewable energy systems in the Egyptian energy market.