Polymer smart materials are a broad class of polymeric materials that can change their shapes, mechanical responses, light transmissions, controlled releases, and other functional properties under external stimuli. A good understanding of the aspects controlling various types of shape memory phenomena in shape memory polymers (SMPs), such as polymer structure, stimulus effect and many others, is not only important for the preparation of new SMPs with improved performance, but is also useful for the optimization of the current ones to expand their application field. In the present era, simple understanding of the activation mechanisms, the polymer structure, the effect of the modification of the polymer structure on the activation process using fillers or solvents to develop new reliable SMPs with improved properties, long lifetime, fast response, and the ability to apply them under hard conditions in any environment, is considered to be an important topic. Moreover, good understanding of the activation mechanism of the two-way shape memory effect in SMPs for semi-crystalline polymers and liquid crystalline elastomers is the main key required for future investigations. In this article, the principles of the three basic types of external stimuli (heat, chemicals, light) and their key parameters that affect the efficiency of the SMPs are reviewed in addition to several prospective applications.

The paper studies new high-temperature thermoplastic impregnated unidirectional carbon fiber composites. The research focuses on the effect of thermal and chemical oxidation of the carbon fibers surface on the interfacial interaction between fibers and polysulfone and polyphenylene sulfide as well as thermal and mechanical properties of the composites. The research reveals the interaction between carbon fibers and the polymer matrix depend both on the type of surface treatment and nature of the polymer. The chemical oxidation of carbon fibers results in good interfacial interaction, and the best mechanical properties were observed for tows impregnated with polyphenylene sulfide.

Interfacial interaction is one of the most important factors that affect the mechanical properties of the fiber reinforced composites. The effect of fabrics′ sizing removal from glass fibers’ surface by thermal treatment on the mechanical characteristics of polyethersulfone based composites at different fiber to polymer weight ratios was investigated. Three fiber to polymer weight ratios of 50/50, 60/40, and 70/30 were studied. Flexural and shear tests were carried out to illustrate the mechanical properties of the composites; the structure was studied using Fourier-transform infrared spectroscopy and scanning electron microscopy. It was shown that solution impregnation of glass fabrics with polyethersulfone before compression molding allows to achieve good mechanical properties of composites. The thermal treatment of glass fabrics before impregnation results in an increase in flexural and shear strength for all the composites due to the improvement of fiber–matrix interaction.

The goal of this study was to create a high-filled composite material based on polysulfone using various graphite materials. Composite material based on graphite-filled polysulfone was prepared using a solution method which allows the achievement of a high content of fillers up to 70 wt.%. Alongside the analysis of the morphology and structure, the thermal conductivity and mechanical properties of the composites obtained were studied. Structural analysis shows how the type of filler affects the structure of the composites with the appearance of pores in all samples which also has a noticeable effect on composites’ properties. In terms of thermal conductivity, the results show that using natural graphite as a filler gives the best results in thermal conductivity compared to artificial and expanded graphite, with the reduction of thermal conductivity while increasing temperature. Flexural tests show that using artificial graphite as a filler gives the composite material the best mechanical load transfer compared to natural or expanded graphite.

In this study, the mechanical and thermophysical properties of carbon fiber-reinforced polyethersulfone are investigated. To enhance the interfacial interaction between carbon fibers and the polymer matrix, the surface modification of carbon fibers by thermal oxidation is conducted. By means of AFM and X-ray spectroscopy, it is determined that surface modification changes the morphology and chemical composition of carbon fibers. It is shown that surface modification dramatically increases the mechanical properties of the composites. Thus, flexural strength and the E-modulus of the composites reinforced with modified fibers reached approximately 962 MPa and 60 GPa, respectively, compared with approximately 600 MPa and 50 GPa for the composites reinforced with the initial ones. The heat deflection temperatures of the composites reinforced with the initial and modified fibers were measured. It is shown that composites reinforced with modified fibers lose their stability at temperatures of about 211 °C, which correlates with the glass transition temperature of the PES matrix. The thermal conductivity of the composites with different fiber content is investigated in two directions: in-plane and transverse to layers of carbon fibers. The obtained composites had a relatively high realization of the thermal conductive properties of carbon fibers, up to 55–60%.