Biodentine® is a bioactive calcium silicate-based material, with better strength parameters, an easier application method and a shorter setting time than mineral trioxide aggregate (MTA). The bond strength between Biodentine and the composite material is essential for the durability of the layered restoration. The objective of this study was to evaluate the bond strength of Biodentine to a resin-based composite at various acid etching times and with different adhesive strategies. In the 1st part of the experiment, the specimens were divided into 2 groups: the adhesive was applied in the total-etch (TE) and self-etch (SE) techniques. In the TE group, 37% orthophosphoric acid was applied after 30 s (TE 30) and 240 s (TE 240). In the SE group, the SE system was applied for 30 s (SE 30) and 240 s (SE 240). In the 2nd part, the SE systems Clearfil® SE Bond and Clearfil S3 Bond Plus were evaluated (the CSE and CS3 groups, respectively). In each group, the adhesive system was applied in 1 (the CSE 1 and CS3 1 subgroups) or 2 layers (the CSE 2 and CS3 2 subgroups). The specimens were subjected to a shear bond strength (SBS) test in a universal testing machine. Shear bond strength was higher after a prolonged etching procedure in the TE (TE 30: 2.51 MPa, TE 240: 9.39 MPa) and SE techniques (SE 30: 5.92 MPa, SE 240: 7.89 MPa). A statistically significant influence was detected in relation to 30 s of surface preparation time for Clearfil S3 Bond Plus (p < 0.001). Greater bond strength was revealed after the application of 1 layer of the Clearfil S3 Bond Plus single-bottle system (CS3 1: 6.42 MPa). The SBS of Biodentine to the composite depends on both the etching time and the mode of application of the adhesive systems. Higher bond strength was obtained for the SE adhesive in a shorter application time.

This study investigated the effect of saliva contamination on chemical changes of ceramic surface as well as the influence of saliva cleaning methods on ceramic-resin bond strength. Saliva was used to contaminate leucite (LGC) and lithium disilicate (LDGC) glass ceramic surfaces. The following cleaning methods were tested: water spray, cleaning with orthophosphoric acid, universal cleaning paste, ultrasonic cleaning with water, re-etching with hydrofluoric acid. Non-contaminated ceramic sample served as control. Chemical analysis of ceramic surfaces was performed using time-of-flight secondary ion mass spectrometry (TOF-SIMS). Shear bond strength (SBS) of ceramics to resin material was tested after 24-hour water storage and after thermocycling. The most effective cleaning method of saliva-contaminated ceramic surface was cleaning LGC surface with orthophosphoric acid or re-etching the LDGC surface with hydrofluoric acid. The application of the following methods resulted in obtaining reliable bond strength.

Successful orthodontic therapy, apart from a proper treatment plan, depends on optimal bracket–enamel adhesion. Among numerous factors affecting adhesion, the type of bracket and preparation of the tooth’s surface are crucial. The aim of this study was to compare the shear bond strength (SBS) of metal and ceramic brackets to the enamel’s surface using direct bonding. Forty extracted human premolars were divided into four groups according to the etching method (etch-and-rinse and self-etch) and bracket type. The SBS and adhesive remnant index (ARI) were determined. The ceramic brackets achieved the highest SBS values both in the self-etch (SE) and etch-and-rinse (ER) protocols. Higher SBS values for ceramic and metallic brackets were found in the ER protocol. In all tested groups, the achieved SBS value was satisfactory to withstand orthodontic and occlusal forces. There was no significant difference in the ARI score between study groups (p = 0.71). The fracture occurred between the bracket base and adhesive material in both types of brackets, which decreased the risk of enamel damage during debonding.

Aim of the study was to evaluate mechanical properties of light-curing composite materials modified with the addition of calcium fluoride. The study used one experimental light-curing composite material (ECM) and one commercially available flowable light-curing composite material (FA) that were modified with 0.5–5.0 wt% anhydrous calcium fluoride. Morphology of the samples and uniformity of CaF₂distribution were analyzed using Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS). Mechanical properties were tested after 24-hour storage of specimens in dry or wet conditions. Stored dry ECM enriched with 0.5–1.0 wt% CaF₂showed higher tensile strength values, while water storage of all modified ECM specimens decreased their tensile strength. The highest Vickers hardness tested after dry storage was observed for 2.5 wt% CaF₂content in ECM. The addition of 2.0–5.0 wt% CaF₂to FA caused significant decrease in tensile strength after dry storage and overall tensile strength decrease of modified FA specimens after water storage. The content of 2.0 wt% CaF₂in FA resulted in the highest Vickers hardness tested after wet storage. Commercially available composite material (FA), unmodified with fluoride addition, demonstrated overall significantly higher mechanical properties.

The composite consisting of a mixture of bis-GMA/UDMA/HEMA/TEGDMA monomers forming a polymer matrix filled with silanized silica (45 wt%) was modified with CTAB or DODAB quaternary ammonium salts (0.5‒2.0 wt%). The hardness, flexural strength and diametrical tensile strength of the composite before and after modification were tested. The type and amount of salt affect the hardness, flexural strength and shrinkage stress, but it does not affect the diametrical tensile strength of the tested composites.

Secondary caries is one of the main reasons for dental filling replacement. There is a need to obtain dental restorative material that is able to act against caries-inducing microorganisms. This study explores the antimicrobial properties of cetyltrimethylammonium bromide (CTAB) or dimethyldioctadecylammonium bromide (DODAB)-modified photo-cured experimental dental composites against Escherichia coli, Streptococcus mutans, and Candida albicans. The antimicrobial activity against Escherichia coli, Streptococcus mutans, and Candida albicans was assessed by using an Accuri C6 flow cytofluorimeter, and then analyzed using BD CSampler software (1.0.264). Bacterial/yeast surface colonization was carried out by using an GX71 inverted-optics fluorescence microscope equipped with a DP 73 digital camera. For bactericidal surface analysis of each sample type, simultaneous standardization was performed using a positive control (live cells) and a negative control (dead cells). A positive correlation between the increasing concentration of CTAB or DODAB and the dead cell ratio of Escherichia coli, Streptococcus mutans, and Candida albicans was revealed. In particular, CTAB at a 2.0 wt% concentration exhibits superior efficiency against pathogens (65.0% dead cells of Escherichia coli, 73.9% dead cells of Streptococcus mutans, and 23.9% dead cells of Candida albicans after 60 min). However, Candida albicans is more resistant to used salts than bacteria. A CTAB- or DODAB-modified experimental dental composite exhibits antimicrobial potential against Escherichia coli, Streptococcus mutans, and Candida albicans after 10 and 60 min of incubation, and the antimicrobial efficiency increases with the wt% of QAS in the tested material.