Lignin-based polyurethane foam was synthesized via a one-pot method and subsequently functionalized with silane to achieve superhydrophobicity. The modified foam demonstrated excellent oil–water separation performance, showcasing its potential for practical applications in environmental remediation.

Biomass energy is becoming increasingly important, owing to the decreasing supply of fossil fuels and growing environmental problems. Hydrothermal carbonization (HTC) is a promising technology for producing solid biofuels from agricultural and forestry residues because of its lower fossil-fuel consumption. In this study, HTC was used to upgrade red jujube branch (RJB) to prepare hydrochar at six temperatures (220, 240, 260, 280, 300, and 320 °C) for 120 min, and at 300 °C for 30, 60, 90, and 120 min. The results showed that the energy recovery efficiency (ERE) reached maximum values of 80.42% and 79.86% at a residence time of 90 min and a reaction temperature of 220 °C, respectively. X-ray diffraction results and Fourier transform infrared spectroscopy measurements show that the microcrystal features of RJB were destroyed, whereas the hydrochar contained an amorphous structure and mainly lignin fractions at increased temperatures. Thermogravimetric analysis shows that the hydrochar had better fuel qualities than RJB, making hydrochar easier to burn.

The fractionation of components of lignocellulosic biomass is important to be able to take advantage of biomass resources. The hydrothermal–ethanol method has significant advantages for fraction separation. The first step of hydrothermal treatment can separate hemicellulose efficiently, but hydrothermal treatment affects the efficiency of ethanol treatment to delignify lignin. In this study, the efficiency of lignin removal was improved by an ultrasonic-assisted second-step ethanol treatment. The effects of ultrasonic time, ultrasonic temperature, and ultrasonic power on the ultrasonic ethanol treatment of hydrothermal straw were investigated. The separated lignin was characterized by solid product composition analysis, FT-IR, and XRD. The hydrolysate was characterized by GC-MS to investigate the advantage on the products obtained by ethanol treatment. The results showed that an appropriate sonication time (15 min) could improve the delignification efficiency. A proper sonication temperature (180 °C) can improve the lignin removal efficiency with a better retention of cellulose. However, a high sonication power 70% (840 W) favored the retention of cellulose and lignin removal.

A nano NiO–Fe ₂ O ₃ /Al ₂ O ₃ Fe-based OC was developed for CLSR hydrogen production experiments in a modified device. Ni promoted Fe-Al2O3 is effective and stable.