Rice husk biochar was utilized to reinforce high-density polyethylene (HDPE) and to prepare biochar/plastic composites (BPC) by the extrusion method. Morphologies, non-isothermal crystallization behavior, and mechanical properties of the composites were investigated. The SEM (scanning electron microscope) showed that HDPE was embedded into the holes of the rice husk biochar. The DSC (differential scanning calorimeter) showed that biochar could reduce the crystallization rate and the higher the content of rice husk biochar, the slower the crystallization rate. Significantly, the bending and tensile strength of BPC could reach 53.7 and 20 MPa, far beyond WPC (wood plastic composites). With the increase of filler content, BPC were still stronger than WPC, although the impact strength of BPC and WPC all showed a general decline in the trend. The strong interaction was achieved by the utilization of rice husk biochar to reinforce HDPE.

An efficient approach for the synthesis of levulinic acid (LA) by converting cellulose in a biphasic system consisting of molten salt hydrate (MSH), (LiCl·3H₂O) and methyl isobutyl ketone (MIBK) using NbOPO₄/HZSM-5 as the catalyst was reported. A series of molten salt hydrates (LiBr·3H₂O, LiCl·3H₂O, ZnCl₂·3H₂O, CaCl₂·3H₂O and Ca(NO₃)₂·3H₂O) were evaluated in terms of their cellulose dissolvability and catalytic activity without any additional catalyst in the conversion of cellulose to LA. Among them, LiBr·3H₂O, LiCl·3H₂O and ZnCl₂·3H₂O were capable of dissolving and swelling cellulose and demonstrated excellent performance in cellulose conversion to LA even without any additional catalyst. High temperature favors the formation of LA while low temperature is beneficial to saccharides and 5-hydroxymethylfurfural (HMF). Using NbOPO₄/HZSM-5, an efficient conversion of cellulose to LA was achieved in a biphasic system, affording a LA yield as high as 94.0%. The partition coefficient of HMF between the MIBK and LiCl·3H₂O phases increased notably when the temperature was increased, proving that a biphasic solvent restrained the secondary reaction of HMF to humins. The reaction mechanism study based on the investigation of converting glucose, fructose and HMF to LA found that the side reactions of saccharides to humins are the key factors affecting the selectivity of LA in the investigated reaction system. Therefore, it is crucial to match the cellulose hydrolysis reaction with the subsequent reactions to maintain saccharides including glucose and fructose at low concentrations for highly efficient conversion of cellulose to LA.