Joining the laser welding club: Laser welding is an integral part of modern manufacturing, but it fractures ceramic materials. Penilla et al. developed two methods for welding ceramics using ultrafast lasers. One method tunes the ceramic properties, allowing the laser to transit through the ceramic and weld at the interface between pieces. The other method optimizes a gap between pieces to efficiently deposit energy. Both methods leverage short but energetic pulses to create a melt pool that allows ceramics to be joined, without the high temperature used for traditional ceramic welds. Science , this issue p. 803

Traditionally accepted design paradigms dictate that only optically isotropic (cubic) crystal structures with high equilibrium solubilities of optically active ions are suitable for polycrystalline laser gain media. The restriction of symmetry is due to light scattering caused by randomly oriented anisotropic crystals, whereas the solubility problem arises from the need for sufficient active dopants in the media. These criteria limit material choices and exclude materials that have superior thermo-mechanical properties than state-of-the-art laser materials. Alumina (Al₂O₃) is an ideal example; it has a higher fracture strength and thermal conductivity than today’s gain materials, which could lead to revolutionary laser performance. However, alumina has uniaxial optical proprieties, and the solubility of rare earths (REs) is two-to-three orders of magnitude lower than the dopant concentrations in typical RE-based gain media. We present new strategies to overcome these obstacles and demonstrate gain in a RE-doped alumina (Nd:Al₂O₃) for the first time. The key insight relies on tailoring the crystallite size to other important length scales—the wavelength of light and interatomic dopant distances, which minimize optical losses and allow successful Nd doping. The result is a laser gain medium with a thermo-mechanical figure of merit of R_s~19,500 Wm⁻¹ a 24-fold and 19,500-fold improvements over the high-energy-laser leaders Nd:YAG (R_s~800 Wm⁻¹) and Nd:Glass (R_s~1 Wm⁻¹), respectively. Moreover, the emission bandwidth of Nd:Al₂O₃ is broad: ~13 THz. The successful demonstration of gain and high bandwidth in a medium with superior R_s can lead to the development of lasers with previously unobtainable high-peak powers, short pulses, tunability, and high-duty cycles.

Developing predictive thermal property models for liquids based on microscopic principles has been elusive. The difficulty is that liquids have gas-like and solid-like attributes that are at odds when considering the frameworks of microscopic models: Models for gases are simple due to randomness and low density, whereas models for crystalline solids rely on symmetry and long-range order for easier calculation. The short-range order in liquids does, however, provide structure to neighboring molecules similar to amorphous solids, and there have been recent advances indicating that collective vibrational modes store heat in liquids. Models combining Debye approximations from solid-state physics and Frenkel’s theory of liquids can accurately predict the heat capacity of liquids. Phonon-like dispersions in liquids have also been widely observed in neutron scattering experiments. These developments motivate us to propose a model where high-frequency vibrational modes, which travel at the speed of sound and have a mean free path on the order of the average intermolecular distance, conduct heat in liquids. We use this liquid phonon gas model to calculate the thermal conductivity of liquids with varying intermolecular interaction energies from strongest to weakest—Coulomb, hydrogen-bonding, Keesom, and London dispersion energy. Generally, the model is more accurate as the intermolecular interaction energy and density of liquids increase. The calculated thermal conductivity of Coulombic-bound molten sodium nitrate and hydrogen-bonded water is within 1.46% and 2.98% of the experimentally measured values, respectively, across their entire temperature ranges. Further modal analysis of the velocity and the mean free path of collective vibrations could establish the liquid phonon gas model as an accurate model for weakly interacting liquids as well.

We present a synthesis/processing method for fabricating ferrimagnetic insulator (Bi-doped yttrium iron garnet) thin films with tunable magnetic anisotropy. Since the desired magnetic properties rely on controllable thickness and successful doping, we pay attention to the entire synthesis/processing procedure (nanopowder synthesis, nanocrystalline target preparation and pulsed laser deposition (PLD)). Atomically flat films were deposited by PLD on (111)-orientated yttrium aluminum garnet. We show a significant enhancement of perpendicular anisotropy in the films, caused by strain-induced anisotropy. In addition, the perpendicular anisotropy is tunable by decreasing the film thickness and overwhelms the shape anisotropy at a critical thickness of 3.5 nm. GRAPHICAL ABSTRACT IMPACT STATEMENT Strain-induced perpendicular magnetic anisotropy (PMA) in heavily Bi substituted YIG films for ferrimagnetic insulator based spintronic studies and devices.