The study is devoted to the development and testing of technological principles for the manufacture of solid end mills from ceramics based on a powder composition of α-SiAlON, β-SiAlON, and TiN additives, including spark plasma sintering powder composition, diamond sharpening of sintered ceramic blanks for shaping the cutting part of mills and deposition of anti-friction Si-containing diamond-like carbon (DLC) coatings in the final stage. A rational relationship between the components of the powder composition at spark plasma sintering was established. The influence of optimum temperature, which is the most critical sintering parameter, on ceramic samples’ basic physical and mechanical properties was investigated. DLC coatings’ role in changing the surface properties of ceramics based on SiAlON, such as microrelief, friction coefficient, et cetera, was studied. A comparative analysis of the efficiency of two tool options, such as developed samples of experimental mills made of SiAlON/TiN and commercial samples ceramic mills based on SiAlON, doped with stabilizing additives containing Yb when processing nickel alloys (NiCr20TiAl alloy was used as an example). DLC coatings’ contribution to the quantitative indicators of the durability of ceramic mills and the surface quality of machined products made of nickel alloy is shown.

The study aims at investigation of structure, properties and machinability rate of raw and thermal treated titanium-based powder material used to produce the thin-walled components by one of the most widespread additive manufacturing technologies, electron beam melting (EBM). The microstructure and material properties of raw EBM parts in horizontal cross-section and in vertical ones are different, i. e. the raw EBM samples structure and properties are anisotropic. To reduce anisotropy by modifying microstructure of EBM parts, a thermal treatment (hot isostatic pressing, HIP) was applied. In addition, when using additive manufacturing, the part surface roughness is quite coarse while the dimensions may be out of tolerance. Thus, making the end product after additive manufacturing often requires a finishing cutting operation. Examining the quality of end product in terms of geometric tolerance and thin walls thickness stability is also included in this study. In particular, when milling thin-walled parts produced by EBM technology, the form accuracy and the surface roughness are the functions of variable wall stiffness which is estimated in a local cutting zone. This fact must be taken into account when selecting the cutting conditions. For this purpose, a specially designed measuring information system has been used to control the vibrations during machining process

Small-size cutting inserts for assembly cutters are widely used to manufacture a variety of parts for the aerospace, automotive and mechanical engineering industries. Due to their high hardness and chemical stability, cutting Al₂O₃-TiC ceramics significantly outperform hard alloys in machining heat-resistant and difficult-to-machine materials. However, grinding on CNC machines, the most common technology for manufacturing ceramic inserts, is associated with numerous issues when it comes to manufacturing small-size cutting inserts. For example, high cutting forces and high grinding wheel wear rates cause a rapid loss of dimensional accuracy and deterioration of the quality of the surface being machined, while the interference of the grinding wheel with the surface being treated imposes serious limitations on the geometry of the small-size ceramic inserts to be grinded. Here we show that Wire Electrical Discharge Machining (WEDM), which is a contactless and, thus, a more flexible method in terms of the size and geometrical properties of a workpiece to be machined, can be used as a replacement for grinding operations in machining small ceramic inserts. A composite of 70% aluminum oxide and 30% titanium carbide was chosen as a ceramic material because a further increase in the TiC fraction causes a marked decrease in wear resistance, while its decrease results in an undesirable loss of electrical conductivity. While in order to replace grinding with WEDM, WEDM has to be stable in the sense of occurring without frequent wire breakages, achieving WEDM stability is not an easy task due to the low electrical conductivity of Al₂O₃-TiC ceramics and high operational temperatures, which promote the diffusion of dielectric and electrode products in the surface layer of the cutting inserts being machined. These factors may lower the quality of the final product due to damage to the insert surface, marked increases in the roughness RA and in diffusion in the surface layer, which increases the friction coefficient and, hence, reduces the life of the manufactured cutting inserts. We have increased stability of the WEDM process by identifying and applying rational process conditions that lead to a reduced, by a factor of 2.63, roughness Ra and also a reduced, by a factor of 1.3, depth of craters. Performing a chemical and structural analysis, we found that the application of high energies combined with an increasing interelectrode gap (IG) (technological parameter SSol, a complex indicator that determines the speed of the wire electrode depending on the number of pulses per unit of time and the IG size, is set at 80, EDM3 technology) causes increased surface damage and contamination, while a small IG (SSol = 45, EDM1 technology) reduces the material removal rate due to contamination of the working zone between the surface being machined and the electrodes. After reducing the IG by lowering SSol from 80 to 45, the roughness Ra of 0.344 µm was achieved, which allows for replacing grinding operations with WEDM in machining hardening chamfers, front surfaces and, to a lesser degree, the rear and support surfaces of cutting inserts. In this case, when the IG is reduced to SSol = 45, the electroerosion products in the dielectric promote local breakdowns, which in turn produce a large number of deep craters which adversely affect the performance of cutting inserts. However, we found that a slight increase in SSol from 45 to 55 (EDM3 technology) significantly reduces the number of craters and lowers their depth from 50 μm to 37 μm. Although in this case the roughness grows to 0.534 μm due to increased discharge energy, the improved flushing of the IG and the reduced occurrence of local high-temperature breakdowns—evidenced by a decrease in the depth and number of deep craters formed due to current localization during short circuits—significantly reduced contamination of the surface layer and the crater formation rate. Therefore, WEDM can be recommended for use in machining reinforcing chamfers and, to a lesser degree, front surfaces. These considerations lead us to conclude that WEDM is a viable alternative to grinding in machining Al₂O₃-TiC ceramic cutting inserts of a small size and a complex shape, and that its application to manufacturing cutting inserts from poorly conductive cutting ceramics should be studied further.

The field of applied wire electrical discharge machining (WEDM) is rapidly expanding due to rapidly increasing demand for parts made of hard-to-machine materials. Hard alloys composed of WC, TiC and Co are advanced cutting materials widely used in industry due to the excellent combination of hardness and toughness, providing them obvious advantages over other cutting materials, such as cubic boron nitride, ceramics, diamond or high-speed steel. A rational choice of the WEDM modes is extremely important to ensure the dimensional quality of the manufactured cutting inserts, while roughness of the machined surface on the cutting edge is of great importance with regards to the application of wear-resistant coatings, which increases tool life. However, the stock control systems of CNC WEDM machines, which are based on assessment of electrical parameters such as amperage and voltage, are unable to timely detect conditions at which a threat of wire breakage appears and to prevent wire breakage by stopping the electrode feed and flushing out the interelectrode gap (IEG) when hard alloys with high heat resistance and low heat conductivity, such as WC, TiC and Co composites, are being machined, due to the inability to distinguish the working pulses and pulses that expend a part of their energy heating and removing electroerosion products contaminating the working zone. In this paper, the physicomechanical nature of the WEDM of hard alloy WC 88% + TiC 6% + Co 6% was investigated, and the possibility of using acoustic emission parameters for controlling WEDM stability and productivity were explored. Acoustic emission (AE) signals were recorded in octave bands with central frequencies of 1–3 and 10–20 kHz. It was found that at the initial moment, when the dielectric fluid is virtually free of contaminants, the amplitude of the high-frequency component of the VA signal has its highest value. However, as the contamination of the working zone by electroerosion products increases, the amplitude of the high-frequency component of the AE signal decreases while the low-frequency component increases in an octave of 1–3 kHz. By the time of the wire breakage, the amplitude of the high-frequency component in the octave of 10–20 kHz had reduced by more than 5-fold, the amplitude of the low-frequency component in the octave of 1–3 kHz had increased by more than 2-fold, and their ratio, coefficient Kf, decreased by 12-fold. To evaluate the efficiency of Kf as a diagnostic parameter, the quality of the surface being machined was investigated. The analysis of residual irregularities on the surface at the electrode breakage point showed the presence of deep cracks and craters typical of short-circuit machining. It was also found that the workpiece surface was full of deposits/sticks, whose chemical composition was identical to that of the wire material. The presence of the deposits evidenced heating and melting of the wire due to the increased concentration of contaminants causing short circuits. It was also shown that the wire breakage was accompanied by the “neck” formation, which indicated simultaneous impacts of the local heating of the wire material and tensile forces. Due to the elevated temperature, the mechanical properties the wire material are quickly declining, a “neck” is being formed, and, finally, the wire breaks. At the wire breakage point, sticks/deposits of the workpiece material and electroerosion products were clearly visible, which evidenced a partial loss of the pulses’ energy on heating the electroerosion products and electrodes. A further increase in the contamination level led to short circuits and subsequent breakage of the wire electrode. It was shown that in contrast to the conventional controlling scheme, which is based on the assessment of amperage and voltage only, the analysis of VA signals clearly indicates the risk of wire breakage due to contamination of the working zone, discharge localization and subsequent short circuits. The monotonic dependence of WEDM productivity on AE parameters provides the possibility of adaptive adjustment of the wire electrode feed rate to the highest WEDM productivity at a given contamination level. As the concentration of contaminants increases, the feed rate of the wire electrode should decrease until the critical value of the diagnostic parameter Kf, at which the feed stops and the IEG flushes out, is reached. The link between the AE signals and physicomechanical nature of the WEDM of advanced cutting materials with high heat resistance and low heat conductivity in different cutting modes clearly shows that the monitoring of AE signals can be used as a main or supplementary component of control systems for CNC WEDM machines.

The work is devoted to the research of the changes that occur in the subsurface layer of the workpiece during electrical discharge machining of conductive nanocomposite based on alumina with the use of a brass tool. The nanocomposite of Al₂O₃ + 30% of TiC was electroerosively machined in a water and hydrocarbon oil. The process of electrical discharge machining is accompanied by oscillations that were registered by diagnostic means. The obtained surface of the samples was researched by the means of scanning electron microscopy and X-ray photoelectron spectroscopy. The observed surface and subsurface changes provide grounding for the conclusions on the nature of processes and reactions that occur between two electrodes and nanomodification of the obtained surfaces that can be an advantage for a series of applications.