Nowadays, the imidazolium-based ionic liquids containing acetate counter-ions are attracting much attention as both highly selective absorbents of the acidic gases and CO₂ carriers in the supported ionic liquid membranes. In this regard, the investigation of the gas transport properties of such membranes may be appropriate for better understanding of various factors affecting the separation performance and the selection of the optimal operating conditions. In this work, we have tested CH₄, CO₂ and H₂S permeability across the supported ionic liquid membranes impregnated by 1-butyl-3-methylimidazolium acetate (bmim[OAc]) with the following determination of the ideal selectivity in order to compare the facilitated transport membrane performance with the supported ionic liquid membrane (SILM) that provides solution-diffusion mechanism, namely, containing 1-butyl-3-methylimidazolium tetrafluoroborate (bmim[BF₄]). Both SILMs have showed modest individual gases permeability and ideal selectivity of CO₂/CH₄ and H₂S/CH₄ separation that achieves values up to 15 and 32, respectively. The effect of the feed gas mixture composition on the permeability of acidic gases and permeselectivity of the gas pair was investigated. It turned out that the permeation behavior for the bmim[OAc]-based SILM toward the binary CO₂/CH₄, H₂S/CH₄ and ternary CO₂/H₂S/CH₄ mixtures was featured with high acidic gases selectivity due to the relatively low methane penetration through the liquid phase saturated by acidic gases.

Pervaporation has been applied for tetrahydrofuran (THF) dehydration with novel composite membranes advanced by a thin selective layer composed of chitosan (CS) modified by copolymerization with vinyl monomers, acrylonitrile (AN) and styrene, in order to improve the chemical and mechanical stability of CS-based membranes. Composite membranes were developed by depositing a thin selective layer composed of CS copolymers onto a commercially-available porous support based on aromatic polysulfonamide (UPM-20^®). The topography and morphology of the obtained materials were studied by atomic force microscopy (AFM), scanning electron microscopy (SEM) and X-ray diffraction analysis (XRD). Thermal properties and stability were determined by coupled evolved gas analysis (EGA-MS). Transport properties were estimated in pervaporation dehydration of THF. The effect of operating parameters for the pervaporation dehydration of THF such as feed compositions and temperatures (295, 308 and 323 K) was evaluated. It was shown that CS modification with different vinyl monomers led to a difference in physical and transport properties. The composite membrane with the thin selective layer based on CS-PAN copolymer demonstrated optimal transport properties and exhibited the highest water content in the permeate with a reasonably high permeation flux.

CO₂ separation was found to be facilitated by transport membranes based on novel chitosan (CS)–poly(styrene) (PS) and chitosan (CS)–poly(acrylonitrile) (PAN) copolymer matrices doped with methylimidazolium based ionic liquids: [bmim][BF₄], [bmim][PF₆], and [bmim][Tf₂N] (IL). CS plays the role of biodegradable film former and selectivity promoter. Copolymers were prepared implementing the latest achievements in radical copolymerization with chosen monomers, which enabled the achievement of outstanding mechanical strength values for the CS-based membranes (75–104 MPa for CS-PAN and 69–75 MPa for CS-PS). Ionic liquid (IL) doping affected the surface and mechanical properties of the membranes as well as the gas separation properties. The highest CO₂ permeability 400 Barrers belongs to CS-b-PS/[bmim][BF₄]. The highest selectivity α (CO₂/N₂) = 15.5 was achieved for CS-b-PAN/[bmim][BF₄]. The operational temperature of the membranes is under 220 °C.

The effect of the morphology and content of zinc oxide nanoparticles (ZnO-NPs) on the physicochemical, mechanical, and gas transport properties of the polyurethane (PU) mixed matrix membranes (MMMs) with respect to CO₂ recovery from CH₄, O₂, and N₂ was studied. The MMMs based on PU with spherical and rod-shaped ZnO-NPs at various loadings, namely, 0.05, 0.1, 0.5, 1, and 2 wt. %, were prepared with membrane density control and studied using AFM, wettability measurements, surface free energy calculation, gas separation and mechanical testing. To evaluate the resistance of the ZnO-NPs to agglomeration in the polymer solutions, zeta potential was determined. The ZnO-NPs with average cross sectional size of 30 nm were obtained by plasma-enhanced chemical vapor deposition (PECVD) from elemental high-purity zinc in a zinc-oxygen-hydrogen plasma-forming gas mixture. It was established that the spherical ZnO-NPs are promising to improve the gas performance of PU-based MMMs for CO₂ recovery from natural gas, while the rod-shaped NPs better demonstrate their potential in capturing CO₂ in flue gases.

The current investigation is focused on the development of composite membranes based on polymeric ionic liquids (PILs) containing imidazolium and pyridinium polycations with various counterions, including hexafluorophosphate, tetrafluoroborate, and bis(trifluoromethylsulfonyl)imide. A combination of spectroscopic methods was used to identify the synthesized PILs and characterize their interaction with carbon dioxide. The density and surface free energy of polymers were performed by wettability measurements, and the results are in good agreement with the permeability and selectivity obtained within the gas transport tests. It was shown that the membranes with a selective layer based on PILs exhibit relatively high permeability with CO₂ and high ideal selectivity CO₂/CH₄ and CO₂/N₂. Additionally, it was found that the type of an anion significantly affects the performance of the obtained membranes, with the most pronounced effect from bis-triflimide-based polymers, showing the highest permeability coefficient. These results provide valuable insights into the design and optimization of PIL-based membranes for natural and flue gas treatment.