Lignin-based carbon fibers (LCFs) from the renewable resource softwood kraft lignin were synthesized via oxidative thermostabilization of pure melt-spun lignin and carbonization at different temperatures from 1000°C to 1700°C. The resulting LCFs were characterized by tensile testing, scanning electron microscopy (SEM), X-ray diffraction (XRD) and confocal Raman spectroscopy. The microstructure is mainly amorphous carbon with some nanocrystalline domains. The strength and stiffness are inversely proportional to the carbonization temperature, while the LCFs carbonized at 1000°C exhibit a strength of 628 MPa and a stiffness of 37 GPa. Furthermore, the application potential of LCFs was evaluated as negative electrodes in a lithium-ion battery (LIB) by electrochemical cycling at different current rates in a half-cell setup. The capacity drops with the carbonization temperature and the LCFs carbonized at 1000°C have a capacity of 335 mAh g⁻¹. All LCFs showed good cycling stability. Because of the mechanical integrity and conductivity of the LCFs, there is no need to apply current collectors, conductive additives or binders. The advantage is an increased gravimetric energy density compared to graphite, which is the most common negative electrode material. LCFs show a promising multifunctional behavior, including good mechanical integrity, conductivity and an ability to intercalate lithium for LIBs.

The article delves into the synthesis and characterization of MoS₂-carbon-based materials, holding promise for applications in supercapacitors and ion batteries. The synthesis process entails the preparation of MoS₂ and its carbon hybrids through exfoliation, hydrothermal treatment, and subsequent pyrolysis. Various analytical techniques were employed to comprehensively examine the structural, compositional, and morphological properties of the resulting materials. The article explores the electrochemical performance of these electrode materials in supercapacitors and ion batteries (LiB, SiB, KiB). Electrochemical measurements were conducted in aqueous electrolyte for supercapacitors and various aprotic electrolytes for ion batteries. Results highlight the impact of the synthesis process on electrochemical performance, emphasizing factors such as capacitance, rate capability, and charge/discharge cycle performance. Hydrothermally treated MoS₂-carbon exhibited a specific capacitance of approximately 150 F g^-1 in supercapacitors, attributed to its high surface area and efficient charge storage mechanisms. Additionally, for Li-ion battery materials without hydrothermal treatment showed impressive capacity retention of around 88% after 500 charge-discharge cycles, starting with an initial specific capacity of about 920 mAh/g. Long-term stability was demonstrated in both supercapacitors and lithium-ion batteries, with minimal capacitance degradation even after extensive charge-discharge cycles. This research underscores the potential of MoS₂-based materials as effective energy storage solutions.