A surface acoustic wave (SAW) sensor was investigated for its application in C-reactive protein (CRP) detection. Piezoelectric lithium niobate (LiNbO₃) substrates were used to study their frequency response characteristics in a SAW sensor with a CRP sensing area. After the fabrication of the SAW sensor, the immobilization process was performed for CRP/anti-CRP interaction. The CRP/anti-CRP interaction can be detected as mass variations in the sensing area. These mass variations may produce changes in the amplitude of sensor response. It was clearly observed that a CRP concentration of 0.1 μg/mL can be detected in the proposed SAW sensor. A good fitting linear relationship between the detected insertion loss (amplitude) and the concentrations of CRP from 0.1 μg/mL to 1 mg/mL was obtained. The detected shifts in the amplitude of insertion loss in SAW sensors for different CRP concentrations may be useful in the diagnosis of risk of cardiovascular diseases.

Accurate identification of tissue types in surgical margins is essential for ensuring the complete removal of cancerous cells and minimizing the risk of recurrence. The objective of this study was to explore the clinical utility of Raman spectroscopy for the detection of oral squamous cell carcinoma (OSCC) in both tumor and healthy tissues obtained from surgical resection specimens during surgery. This study enrolled a total of 64 patients diagnosed with OSCC. Among the participants, approximately 50% of the cases were classified as the most advanced stage, referred to as T4. Raman experiments were conducted on cryopreserved tissue samples collected from patients diagnosed with OSCC. Prominent spectral regions containing key oral biomarkers were analyzed using the partial least squares–support vector machine (PLS–SVM) method, which is a powerful multivariate analysis technique for discriminant analysis. This approach effectively differentiated OSCC tissue from non-OSCC tissue, achieving a sensitivity of 95.7% and a specificity of 93.3% with 94.7% accuracy. In the current study, Raman analysis of fresh tissue samples showed that OSCC tissues contained significantly higher levels of nucleic acids, proteins, and several amino acids compared to the adjacent healthy tissues. In addition to differentiating between OSCC and non-OSCC tissues, we have also explored the potential of Raman spectroscopy in classifying different stages of OSCC. Specifically, we have investigated the classification of T1, T2, T3, and T4 stages based on their Raman spectra. These findings emphasize the importance of considering both stage and subsite factors in the application of Raman spectroscopy for OSCC analysis. Future work will focus on expanding our tissue sample collection to better comprehend how different subsites influence the Raman spectra of OSCC at various stages, aiming to improve diagnostic accuracy and aid in identifying tumor-free margins during surgical interventions.

A metalorganic vapor phase epitaxy-grown InGaN/GaN multiple-quantum-well (MQW) with three graded-thickness wells (the first-grown well had the greatest width) near the n-GaN was used as the active layer of an LED. For LEDs with an asymmetric quantum well (AQW), high-resolution X-ray diffraction and transmission electron microscopic reveal that the modified MQWs with a reasonable crystalline quality were coherently strained on the underlying GaN epilayers without any relaxation. In addition, the slight increase of indium segregation in the LED with an AQW may be attributed to variations in indium contents experienced during epitaxial growth of the wide well-containing MQWs. By preventing the energetic electrons from accumulating at the topmost quantum well nearest the p-GaN, the presence of light intensity roll-off in the LED with an AQW is shifted to higher currents and the corresponding maximum light output power is increased with a ratio 7.9% higher than that of normal LEDs. Finally, similar emission wavelengths were observed in the electroluminescence spectra of both LEDs, suggesting that light emitted mostly from the top quantum wells (near the p-GaN) while the emissions from the AQW region were insignificant.

InGaN light-emitting diodes (LEDs) grown with an asymmetric multiple quantum well (MQW) are proposed for use in an optical link with an avalanche photodiode (APD) based receiver. In contrast to the high photoresponse of red AlGaInP LEDs in APDs, the proposed blue LEDs provide improved light output and enhanced system bandwidth for directed line-of-sight optical links passing through a 100-cm-long water tank. This improvement is due to the nonuniform carrier distribution within the InGaN MQWs being mitigated by using a thin GaN barrier near the n-GaN to facilitate hole transport capacity. In addition, bandwidth degradation resulting from APD module saturation can also be avoided by using these blue LEDs, successfully establishing a 300 Mbit/s LED-based underwater data link. The proposed InGaN LEDs (zero bias) under illumination exhibit a peak responsivity of 0.133 at λ = 370 nm, an ultraviolet (UV)-to-visible rejection ratio of 4849 and a 3-dB cut-off frequency of 33.3 MHz. Using violet UV laser diodes and the proposed LEDs respectively as the optical transmitter and receiver, an underwater optical link (L = 100 cm) with a data transmission rate of up to 130 Mbit/s and a bit error rate of 4.2 × 10 ⁻⁹ is also demonstrated.