In three-dimensional (3D) printing, one of the main parameters influencing the properties of 3D-printed materials is the infill density (ID). This paper presents the influence of ID on the microstructure, mechanical, and thermal properties of carbon fiber-reinforced composites, commercially available, manufactured by the Fused Filament Fabrication (FFF) process. The samples were manufactured using FFF by varying the infill density (25%, 50%, 75%, and 100%) and were subjected to tensile tests, three-point bending, and thermal analyses by Differential Scanning Calorimetry (DSC) and Thermogravimetric Analysis (TGA). It was shown that the samples with 100% ID had the highest values of both tensile, 90.8 MPa, and flexural strengths, 114 MPa, while those with 25% ID had the lowest values of 56.4 MPa and 62.2 MPa, respectively. For samples with infill densities of 25% and 50%, the differences between the maximum tensile and flexural strengths were small; therefore, if the operating conditions of the components allow, a 25% infill density could be used instead of 50%. After DSC analysis, it was found that the variation in the ID percentage determined the change in the glass transition temperature from 49.6 °C, for the samples with 25% ID, to 32.9 °C, for those with 100% ID. TGA results showed that the samples with IDs of 75% and 100% recorded lower temperatures of onset degradation (approximately 344.75 °C) than those with infill densities of 25% and 50% (348.5 °C, and 349.6 °C, respectively).

Fused Filament Fabrication (FFF) is one of the frequently used material extrusion (MEX) additive manufacturing processes due to its ability to manufacture functional components with complex geometry, but their properties depend on the process parameters. This paper focuses on studying the effects of process parameters, namely infill density (25%, 50%, 75%, and 100%), on the mechanical and thermal response of the samples made of poly(lactic acid) (PLA) reinforced with short glass fibers (GF) produced using FFF process. To perform a comprehensive analysis, tensile, flexural, compression, differential scanning calorimetry (DSC), and thermal gravimetric analysis (TGA) tests were used. The paper also aims to manufacture by FFF process of composite structures of the fuselage section type, as structural elements of an unmanned aerial vehicle (UAV), and their testing to compression loads. The results showed that the tensile, flexural and compression strength of the additive manufactured (AMed) samples increased with the increase of infill density and therefore, the samples with 100% infill density provides the highest mechanical characteristics. The AMed samples with 50% and 75% infill density exhibited a higher toughness than samples with 100% infill. DSC analyses revealed that the glass transition (Tg), and melting (Tm) temperature increases slightly as the infill density increases. Thermogravimetric analyses (TGA) show that PLA-GF filament loses its thermal stability at a temperature of about 311 °C and the increase in fill density leads to a slight increase in thermal stability and the complete degradation temperature of the AMed material. The compression tests of the fuselage sections manufactured by FFF made of PLA-GF composite showed that their stiffening with stringers oriented at an angle of ±45° ensures a higher compression strength than the stiffening with longitudinal stringers.

The additive processes used in the manufacture of components for unmanned aerial vehicles (UAVs), from composite filaments, have an important advantage compared to classical technologies. This study focused on three-dimensional design, preliminary aerodynamic analysis, fabrication and assembly of thermoplastic extruded composite components, flight testing and search-rescue performance of an UAV. The UAV model was designed to have the highest possible structural strength (the fuselage has a structure with stiffening frames and the wing is a tri-spar), but also taking into account the limitations of the thermoplastic extrusion process. From the preliminary aerodynamic analysis of the UAV model, it was found that the maximum lift coefficient of 1.2 and the maximum drag coefficient of 0.06 were obtained at the angle of attack of 12°. After conducting flight tests, it can be stated that the UAV model, with components manufactured by the thermoplastic extrusion process, presented high stability and maneuverability, a wide range of speeds and good aerodynamic characteristics. The lack of this type of aircraft, equipped with electric motors, a traffic management system, and a thermal module designed for search-and-rescue missions, within the additive manufacturing UAV market, validates the uniqueness of the innovation of the UAV model presented in the current paper.

The utilization of polymer-based materials is quickly expanding. The enterprises of today are progressively seeking techniques to supplant metal parts with polymer-based materials as a result of their light weight, simple support and modest costs. The ceaselessly developing requirement for composite materials with new or enhanced properties brings about the preparation of different polymer mixes with various arrangements, morphologies and properties. Fused filament fabrication processes such as 3D-printing are nowadays shaping the actual pathway to a full pallet of materials, from art–craft to biomaterials. In this study, the structural and mechanical behavior of three types of commercially available filaments comprised of synthetic poly(acrylonitrile-co-butadiene-co-styrene) (ABS), poly(lactic acid) (PLA) and poly(lactic acid)/polyhydroxyalkanoate reinforced with bamboo wood flour composite (PLA/PHA BambooFill) were assessed through mechanical testing and optical microscopy, aiming to understand how the modifications that occur in the printed models with internal architecture are influencing the mechanical properties of the 3D-printed material. It has been determined that the material printed from PLA presents the highest compression strength, three-point bending and shock resistance, while the ABS shows the best tensile strength performance. A probability plot was used to verify the normality hypothesis of data for the tensile strength, in conjunction with the Anderson–Darling statistic test. The results of the statistic indicated that the data were normally distributed and that there is a marked influence of the internal architecture of the 3D-printed models on the mechanical properties of the printed material.

Additive manufacturing, through the process of thermoplastic extrusion of filament, allows the manufacture of complex composite sandwich structures in a short time with low costs. This paper presents the design and fabrication by Fused Filament Fabrication (FFF) of composite sandwich structures with short fibers, having three core types C, Z, and H, followed by mechanical performance testing of the structures for compression and bending in three points. Flatwise compression tests and three-point bending have clearly indicated the superior performance of H-core sandwich structures due to dense core structures. The main modes of failure of composite sandwich structures were analyzed microscopically, highlighting core shear buckling in compression tests and face indentation in three-point bending tests. The strength–mass ratio allowed the identification of the structures with the best performances considering the desire to reduce the mass, so: the H-core sandwich structures showed the best results in compression tests and the C-core sandwich structures in three-point bending tests. The feasibility of the FFF process and the three-point bending test of composite wing sections, which will be used on an unmanned aircraft, have also been demonstrated. The finite element analysis showed the distribution of equivalent stresses and reaction forces for the composite wing sections tested for bending, proving to validate the experimental results.

In this study, lightweight sandwich structures with honeycomb cores are proposed and their mechanical properties are investigated through experiments and FEA (finite element analysis) simulation. Sandwich structures were fabricated out of Inconel 718 using selective laser melting technique with two different topologies—sandwich structures with perforated skin (SSPS) and sandwich structures with perforated core (SSPC). In addition, the effect of the homogenization heat treatment on the mechanical properties of the sandwich samples subjected to compression and microhardness tests was analyzed. Results showed significant increases of mechanical performance before and after homogenization heat treatment of the Inconel 718 samples. Microstructure analysis was performed to compare the microstructures before and after homogenization heat treatment for Inconel 718 alloys manufactured by selective laser melting (SLM). The accuracy of experimental data were evaluated by modeling of sandwich samples in Ansys software at the end of this study.