Epoxy resin based on bisphenol A diglycidyl ether/anhydride methyl tetrahydrophthalic/2,4,6-tris(dimethylaminomethyl)phenol (DGEBA/MTHPA/DEH 35) was produced by magnetic stirring; chicken eggshell (ES) was added as cure improver. Thermal stability, cure parameters, mechanical properties, and fracture surface were investigated by thermogravimetry (TGA), differential scanning calorimetry (DSC), tensile experiments, and scanning electron microscopy (SEM). In general, the addition of ES slightly decreased the thermal stability, being T_0.05 5% lower than that of the reference sample. The cure rate increased with the heating rates, while best results were obtained upon addition of neat membrane (M) from ES. Surprisingly, the mechanical properties were significantly improved with ES as well as with M, being the Young’s modulus 18% higher, the tensile strength 50% higher, and the deformation 35% higher than those of epoxy resin. SEM images showed that the synthetic compounds presented a smooth fracture surface, while the compounds with ES and M had a rougher surface with multiplane fractures, suggesting a fracture with higher energy absorption. In conclusion, epoxy/ES composites with better performance were produced, and effective tools are provided to control and attain in the future even better properties with ecological features.

Ceramic membranes are of great industrial interest in separation processes. They are characterized by high chemical and thermal stabilities and filtration capacity at high temperatures (>500 °C) in a wide range of pH values. However, the major disadvantage of ceramic membranes is the high-cost of production involving synthetic raw materials, usually alumina and zirconia. In this work, low-cost ceramic membranes were prepared by solid-state reactive firing using a mixture of kaolinite clay and sugarcane bagasse ash. Particle size distribution, thermal, mineralogical, and chemical composition analyses were carried out to study the raw materials. Technological properties and water permeability were investigated in samples fired between 800 and 1000 °C. The filtration efficiency was measured by comparative analyses between the raw water and the filtrate. The mean pore size ranging from 2.5 to 6.0 μm makes the sugarcane bagasse ash derived ceramic membranes suitable for microfiltration processes.

Compounds of poly(3-hydroxybutyrate) (PHB) and titanium dioxide (TiO₂) with filler content between 1% and 10% were prepared in a laboratory internal mixer. The effect of heating and cooling rates on the crystallization and melting of PHB/TiO₂ compounds was investigated by differential scanning calorimetry (DSC). Melt and cold crystallization rates rise with increasing cooling/heating rates. A higher cooling rate translates to a lower melt crystallization temperature, while a higher heating rate results in a higher cold crystallization temperature. TiO₂ promotes melt crystallization of PHB, behaving as a nucleant agent. The total crystallinity developed after melt and cold crystallization decreases for low levels of TiO₂, i.e. 2% per weight, and is almost independent of the heating/cooling rate. The melting temperatures and rates are minimally affected by both the heating rate and filler content. The results suggest that the desired PHB microstructure can be controlled by filler content and adjusted heating/cooling rate.