Epoxy resin based on bisphenol A diglycidyl ether/anhydride methyl tetrahydrophthalic/2,4,6-tris(dimethylaminomethyl)phenol (DGEBA/MTHPA/DEH 35) was produced by magnetic stirring; chicken eggshell (ES) was added as cure improver. Thermal stability, cure parameters, mechanical properties, and fracture surface were investigated by thermogravimetry (TGA), differential scanning calorimetry (DSC), tensile experiments, and scanning electron microscopy (SEM). In general, the addition of ES slightly decreased the thermal stability, being T_0.05 5% lower than that of the reference sample. The cure rate increased with the heating rates, while best results were obtained upon addition of neat membrane (M) from ES. Surprisingly, the mechanical properties were significantly improved with ES as well as with M, being the Young’s modulus 18% higher, the tensile strength 50% higher, and the deformation 35% higher than those of epoxy resin. SEM images showed that the synthetic compounds presented a smooth fracture surface, while the compounds with ES and M had a rougher surface with multiplane fractures, suggesting a fracture with higher energy absorption. In conclusion, epoxy/ES composites with better performance were produced, and effective tools are provided to control and attain in the future even better properties with ecological features.

This work aimed to develop and evaluate the influence of processing variables on the morphology and swelling of sulfonated poly(ether ether ketone) (SPEEK) spheres for possible applications as a biomaterial. We used the drip method to obtain spheres with the polymer starting solutions SPEEK-6 (w/v: 6%) and SPEEK-10 (w/v: 10%), drip rates (20 and 30 mL/h), and drip heights (5 and 10 cm) in experimental planning. The samples were characterized by Fourier-transform infrared spectroscopy (FTIR), optical microscopy (OM), the absorption capacity of phosphate-buffered saline (PBS) by swelling (%), and statistical analysis of data through Design of Experiments (DOE). The obtained results evidenced that the processing variables influenced the morphology and swelling. Spheres with a bigger concentration of the polymer solution presented a greater degree of sulfonation (DS). We verified that the diameter of the spheres was directly related to the variable height and the sphericity was associated with the speed and viscosity of the solution. Bigger and more pores in a greater amount were observed in the spheres with a greater DS, influencing the behavior of the swelling in PBS. The better variable combinations with a high DS, regular sphericity, a smaller diameter, and greater swelling were the samples S₂-10-20-5 e S₁₀-10-20-5. The cytotoxicity indicated that the best samples obtained in the experimental planning (S₂-10-20-5 and S₁₀-10-20-5) were not toxic. In that regard, the evaluated spheres presented cell viability and swelling capacity, suggesting their possible applications as biomaterials.

This research paper is about the calculation of the diffusion coefficient and the oxygen concentration profile along polypropylene samples exposed to photooxidation in a dry environment. In this degradation process, oxygen diffusion is anomalous, as it is affected by structural modifications that occur over the exposure time. Thus, the diffusion coefficient starts to depend on time and the common solutions for Fick's 2nd Law for diffusion become inoperative for importante time intervals. In this work, a modification is proposed in the calculation of the diffusivity and, consequently, of the solution for the oxygen concentration profile in diffusion.