The use of resorbable magnesium alloys in the design of implants represents a new direction in the healthcare domain. Two main research avenues are currently explored for developing or improving metallic biomaterials: (i) increase of their corrosion resistance by designed compositional and structural modifications, and (ii) functionalization of their surfaces by coating with ceramic or polymeric layers. The main objective of this work was to comparatively assess bio-functional coatings (i.e., highly-crystallized hydroxyapatite and silica-rich glass) deposited by radio-frequency magnetron sputtering (RF-MS) on a biodegradable Mg-0.8Ca alloy (0.8 wt.% of Ca). After probing their morphology (by scanning electron microscopy) and structure (by Fourier transform infrared spectroscopy and grazing incidence X-ray diffraction), the corrosion resistance of the RF-MS coated Mg-0.8Ca substrates was electrochemically tested (in synthetic biological media with different degrees of biomimicry), and their cytocompatibility was assessed in osteoblast and fibroblast cell cultures. By collective assessment, the most promising performances, in terms of mass loss (~7% after 12 days), hydrogen release rate (~6 mL/cm² after 12 days), electrochemical corrosion parameters and cytocompatibility, were obtained for the crystalline HA coating.

Development of reproducible, low‐cost fabrication technologies that are readily adaptable to large‐scale production, is one of the main challenges in the field of perovskite solar cells (PSCs). So far, for all the other layers in a solar cell, large‐area deposition methods have been adapted, except for mesoporous fabrication. Herein, the fabrication of mesoporous TiO₂ scaffolds using a large‐area deposition technique, such as spray coating, is shown. Moreover, this technique induces the formation of a very specific reticulated structure with well‐delimited, oval‐shaped cavities. The cavities have irregular dimensions, with diameters in the range of 3–7 μm, ≈350 nm height, resulting in an overall increase in roughness of one order of magnitude, compared with the spin‐coated mesoporous scaffold. Using this rough structured mesoporous TiO₂ in PSCs not only does not affect the efficiency of solar cells but actually improves it from an average of 10% to 12% in comparison with the devices containing a spin‐coated mesoporous scaffold.

Bi-phasic calcium phosphates (BCPs) are considered prominent candidate materials for the fabrication of bone graft substitutes. Currently, supplemental cation-doping is suggested as a powerful path to boost biofunctionality, however, there is still a lack of knowledge on the structural role of such substituents in BCPs, which in turn, could influence the intensity and extent of the biological effects. In this work, pure and Mg- and Sr-doped BCP scaffolds were fabricated by robocasting from hydrothermally synthesized powders, and then preliminarily tested in vitro and thoroughly investigated physically and chemically. Collectively, the osteoblast cell culture assays indicated that all types of BCP scaffolds (pure, Sr- or Sr–Mg-doped) delivered in vitro performances similar to the biological control, with emphasis on the Sr–Mg-doped ones. An important result was that double Mg–Sr doping obtained the ceramic with the highest β-tricalcium phosphate (β-TCP)/hydroxyapatite mass concentration ratio of ~1.8. Remarkably, Mg and Sr were found to be predominantly incorporated in the β-TCP lattice. These findings could be important for the future development of BCP-based bone graft substitutes since the higher dissolution rate of β-TCP enables an easier release of the therapeutic ions. This may pave the road toward medical devices with more predictable in vivo performance.

The issue of heavy metal and radionuclide contamination is still causing a great deal of concern worldwide for environmental protection and industrial sites remediation. Various techniques have been developed for surface decontamination aiming for high decontamination factors (DF) and minimal environmental impact, but strippable polymeric nanocomposite coatings are some of the best candidates in this area. In this study, novel strippable coatings for heavy metal and radionuclides decontamination were developed based on the film-forming ability of polyvinyl alcohol, with the remarkable metal retention capacity of bentonite nanoclay, together with the chelating ability of sodium alginate and with “new-generation” “green” complexing agents: iminodisuccinic acid (IDS) and 2-phosphonobutane-1,2,4-tricarboxylic acid (PBTC). These environmentally friendly water-based decontamination solutions are capable of generating strippable polymeric films with optimized mechanical and thermal properties while exhibiting high decontamination efficiency (DF ≈ 95–98% for heavy metals tested on glass surface and DF ≈ 91–97% for radionuclides ²⁴¹Am, ⁹⁰Sr-Y and ¹³⁷Cs on metal, painted metal, plastic, and glass surfaces).

We investigate how far the hysteresis-free behavior of perovskite solar cells can be reproduced using particular pre-conditioning and measurement conditions. As there are currently more and more reports of perovskite solar cells without J–V hysteresis it is crucial to distinguish between genuine performance improvements and measurement artifacts. We focus on two of the parameters that influence the dynamic J–V scans, namely the bias scan rate and the bias poling voltage, and point out measurement conditions for achieving a hysteresis-free behavior. In this context we discuss the suitability of defining a hysteresis index (HI) for the characterization of dynamic J–V scans. Using HI, aging effects are also investigated, establishing a potential connection between the sample degradation and the variation of the maximal hysteresis on one hand, and the relaxation time scale of the slow process on the other hand. Pre-poling induced recombination effects are identified. In addition, our analysis based on sample pre-biasing reveals potential indications regarding two types of slow processes, with two different relaxation time scales, which provides further insight regarding ionic migration.

The technology of perovskite solar cells (PSC) is getting close to breaching the consumer market. Yet, one of the current challenges is to reduce the toxicity during their fabrication by reducing the use of the toxic solvents involved in the perovskite fabrication process. A good solubilization of lead halides used in hybrid perovskite preparation is required, and it is only possible with polar solvents. A mixture of dimethylformamide (DMF) and dimethyl sulfoxide (DMSO) is the most popular solvent combination for a perovskite precursor solution. DMF is necessary to ensure a good dissolution of lead iodide, but it is also the most toxic solvent. In this paper, we study the replacement of the dimethylformamide with presumably less toxic alternatives, such as N-methyl-2-Pyrrolidone (NMP) and ethyl acetate (EA), for the preparation of the K_0.1FA_0.7MA_0.2PbI_2.8Cl_0.2 (KFAMA) hybrid perovskite. The perovskite thin films were investigated by various characterization techniques: X-ray diffraction, atomic force microscopy, scanning electron microscopy, and UV–vis spectroscopy, while the photovoltaic parameters were determined by measuring the IV curves of the corresponding solar cells. The present study shows that by keeping the same deposition parameters as when only DMF solvent is used, the partial solvent substitution with NMP and EA gives promising results for reducing the toxicity of the fabrication process of KFAMA-based PSCs. Thus, with no specific optimization of the deposition process, and for the maximum possible partial substitution of DMF with NMP and EA solvents, the loss in the power conversion efficiency (PCE) value is only 35% and 18%, respectively, associated with the more structural defects promoted by NMP and EA.