Despite intensive research on material properties of non-metallic technical textiles for internal reinforcement in concrete, the long-term durability is not yet fully understood. In this work, results of preloaded long-term durability tensile tests on carbon-reinforced concrete specimens under environmental factors of stress, temperature, moisture and alkalinity are presented. Based on investigations of non-metallic glass fiber reinforcements with polymer matrices, where strength losses occur over time, it was planned to derive a time to failure curve and to determine a reduction factor for the tensile strength of the carbon textile reinforcement. However, no loss of strength was discovered in residual capacity tests due to the high material resistance and therefore no reduction factor due to the environmental factors could be derived. After more than 5000 h of testing, the residual capacity tests showed an increase in the ultimate failure stress in comparison with the short-term tests. In addition to the long term-durability tests, the influence of the preloading was investigated. The preload was applied to the long-term tests and led to a straighter alignment and loading of the filaments and thus to an increase in the ultimate capacity.

Most shear tests are performed as standard three- or four-point bending tests, i.e., on one-way simply supported specimens subjected to concentrated loads. The major disadvantage is that these conditions usually do not correspond to the support and load condition of real structures. Structural members such as beams or slabs, are often multi-span components and subjected to distributed loads. As a consequence, the complex shear behavior, including crack kinematics, shear transfer mechanisms, and shear capacity, is studied almost only simply supported members with concentrated load. Positive impacts on the shear behavior resulting from continuous systems and distributed loads are thus neglected in the derivation of calculation models and in the development of design specifications. To incorporate the effect of continuous members and distributed loading conditions, more experimental investigations are necessary. Therefore, a total of 16 bending shear tests on CFRP reinforced concrete members without shear reinforcement were carried out. The tests specimens were tested as simply supported beams or as simply supported beams with loaded cantilever to simulate the continuous system with concentrated and distributed loads. Furthermore, the shear slenderness was varied by using different span lengths and degrees of restraint in the systems with intermediate support. All test specimens were made of high-strength concrete and were reinforced with a multilayer grid-like CFRP reinforcement in longitudinal direction. There was no shear reinforcement installed in the investigated shear span. This paper focuses the influence of the support conditions and load arrangements on crack development as well as on shear strength.