Crumb rubber modified (CRM) asphalt binder has been affirmed to improve resistance to rutting, moisture susceptibility, low-temperature cracking, and asphalt durability. However, CRM has poor compatibility with asphalt since crumb rubber molecules are vulcanized. The objective of this study was to develop a new method to prepare activated crumb rubber using hydrogen peroxide (H₂O₂) solution and to explore the rheological properties of H₂O₂ activated CRM (ACRM) asphalt. Three different percentages of H₂O₂ solution were used to activate crumb rubber. The surface properties of oxidized rubber were analysed using scanning electron microscopy. Moreover, the pore structure in rubber powder was investigated. The rheological properties of bitumen samples obtained from treated and untreated rubber were characterized by conducting dynamic shear rheometer tests. The test results show that the average pore size of the crumb rubber after activation with H₂O₂ solution is significantly smaller than that of the inactivated crumb rubber, and the volume and surface area of the crumb rubber pores change with H₂O₂ solution activation in a certain pattern. With the increase in H₂O₂ solution content, the contact surface between the particles increases, the floccules and pores of the powder increase, and the interface degree between the crumb rubber powder and the asphalt is strengthened. Solubility of the rubber hydrocarbon and the release ability of the carbon black particles from the crumb rubber in the asphalt binder increase, but the mechanical properties of the crumb rubber, including the strength, elasticity, and wear resistance, decrease. As a result, a reduction is observed in the elasticity, viscosity, high-temperature rutting resistance, and elasticity of the ACRM asphalt.

To study different lateral restraints, different constituents of expansion agents, the influence of different steel ratios, and concrete creep properties, we carried out experiments with lateral restraint and without lateral restraint conditions separately on 12 specimens with the expansion agent content accounting for 4%, 8%, and 12% respectively. In addition, the creep tests were performed on specimens with different steel ratios of 0.0%, 3.8%, 6.6%, and 9.2%. The test results show that the lateral restraint improves the strength of the system (concrete-filled steel tubes) which resists further load after the concrete ultimate strength is surpassed and reduces the creep. The creep degree of the concrete-filled steel tube with lateral restraint is about 0.09–0.30 times smaller than that of the tube without lateral restraints. The creep degree of the concrete-filled steel tube increases as the steel ratio decreases. Creep tests with different amounts of expansion agent indicate that the creep degree of the concrete structure increases as expansion agent content decreases. To study the internal mechanism of the creep of concrete-filled steel tubes with different lateral restraints and different expansion agent concentrations, a microscopic pore structure test on the steel core concrete was conducted using the RapidAir457 pore structure instrument. Microscopic studies show that the air content and the length of the bubble chord of the laterally restrained core concrete are lower than those without lateral restraint core concrete. The amount of air content and the length of the bubble chord of core concrete specimens increase as the expansion agent content in the core concrete specimens decreases from 12% to 4%. Under the same external loading conditions, as steel ratio increases, the lateral restraint causes a further reduction of creep. The results of this study suggest that the creep of concrete can be reduced by selecting appropriate lateral restraint conditions and an optimal amount of expansion agent in the mix design of concrete for concrete-filled steel tubes.