The results of research into utilizing grinded beech bark in order to substitute commonly used fillers in urea formaldehyde (UF) adhesive mixtures to bond plywood are presented in the present study. Four test groups of plywood with various adhesive mixtures were manufactured under laboratory conditions and used for experimentation. Plywood made using the same technology, with the common filler (technical flour), was used as a reference material. Three different concentrations of grinded beech bark were used. The thermal conductivity of the fillers used, viscosity and its time dependence, homogeneity and the dispersion performance of fillers were evaluated in the analysis of adhesive mixture. The time necessary for heating up the material during the pressing process was a further tested parameter. The produced plywood was analyzed in terms of its modulus of elasticity, bending strength, perpendicular tensile strength and free formaldehyde emissions. Following the research results, beech bark can be characterized as an ecologically friendly alternative to technical flour, shortening the time of pressing by up to 27%. At the same time, in terms of the statistics, the mechanical properties and stability of the material changed insignificantly, and the formaldehyde emissions reduced significantly, by up to 74%. The utilization of bark was in compliance with long-term sustainability, resulting in a decrease in the environmental impact of waste generated during the wood processing.

This article deals with the laser cutting of wood and wood composites. The laser cutting of wood and wood composites is widely accepted and used by the wood industry (due to its many advantages compared to, e.g., saw cutting). The goal of this research was to optimize the cutting parameters of spruce wood (Pices abies L.) by a low-power CO₂ laser. The influence of three factors was investigated, namely, the effect of the laser power (100 and 150 W), cutting speed (3, 6, and 9 mm·s⁻¹), and number of annual rings (3–11) on the width of the cutting kerf on the top board, on the width of the cutting kerf on the bottom board, on the ratio of the cutting kerf width on the top and bottom of the board, on the width of the heat-affected area on both sides of the cutting kerf (this applies to the top and bottom of the board), and on the degree of charring. Analysis of variance (ANOVA) and correlation and regression analysis were used for developing a linear regression model without interactions and a quadratic regression model with quadratic interactions. Based on the developed models, the optimization of parameter settings of the investigated process was performed in order to achieve the final kerf quality. The improvement in the quality of the part ranged from 3% to more than 30%. The results were compared with other research dealing with the laser cutting of wood and wood composites.

Influence of Urea-formaldehyde Adhesive Modification with Beech Bark on Chosen Properties of Plywood

The effects of using 100% larch bark (Larix decidua Mill) as a raw material for composite boards on the thermophysical properties of this innovative material were investigated in this study. Panels made of larch bark with 4–11 mm and 10–30 mm particle size, with ground bark oriented parallel and perpendicular to the panel’s plane at densities varying from 350 to 700 kg/m³ and bonded with urea-formaldehyde adhesive were analyzed for thermal conductivity, thermal resistivity and specific heat capacity. It was determined that there was a highly significant influence of bulk density on the thermal conductivity of all the panels. With an increase in the particle size, both parallel and perpendicular to the panel´s plane direction, the thermal conductivity also increased. The decrease of thermal diffusivity was a consequence of the increasing particle size, mostly in the parallel orientation of the bark particles due to the different pore structures. The specific heat capacity is not statistically significantly dependent on the density, particle size, glue amount and particle orientation.

The basic thermophysical properties of oriented strand boards were determined experimentally for use in humid conditions (OSB3) depending on the moisture content. The dependency between the thermal conductivity, thermal diffusivity, specific heat capacity, and the moisture content in the range of 0% to 10%, was examined. The non-stationary extended dynamic plane source (EDPS) experimental method was used. EDPS method was modified for anisotropic materials, i.e. with special considerations of heat-loss effect occurring at the edge of measuring samples, finite geometry of the sample and orthotropic thermal conductivity, for use with anisotropic materials. The validity of the experimental method was verified on polymethylmethacrylate (PMMA) samples. The error rate of measurements conducted on PMMA samples was less than 3%, and for OSB3 boards it was less than 5.5%. Based on the experimental results, regression equations of the dependency between the monitored properties and the moisture content were determined. In the case of thermal conductivity and thermal capacity, the determined dependencies showed a high correlation rate.

The results of using the EDPS (extended dynamic plane source) method to determine thermophysical properties of solid wood of coniferous trees growing in Slovakia with 0% and 12% equilibrium moisture content are presented in the paper. Solid wood of two different tree species: Norway spruce (Picea abiesL.) and Scots pine (Pinus sylvestrisL.) was used in the research. The research was carried out independently in three anatomical planes. Coefficients of thermal conductivity, thermal diffusivity, and specific heat capacity were determined following the research. Comparing the research results to the values determined by other authors and already published models to calculate individual parameters, the fact that the data gathered using the EDPS method can be accepted in case of all studied thermophysical properties can be stated.