This paper presents the testing of the durability of concrete where a part of cement was replaced with ground panel cathode ray tube glass (CRT) finer than 63 µm. The percentage of cement replaced with glass is 5%, 10%, 15%, 20%, and 35%, by mass. The highest percent share of mineral admixtures in CEM II (Portland-composiste cement) cement was chosen as the top limit of replacement of cement with glass. In terms of the concrete durability, the following tests are performed: freeze-thaw resistance, freeze-thaw resistance with de-icing salts-scaling, resistance to wear according to the Böhme test, sulfate attack resistance, and resistance to penetration of water under pressure. A compressive strength test is performed, and shrinkage of concrete is monitored. In order to determine the microstructure of concrete, SEM (Scanning Electron Microscopy) and EDS (Energy Dispersive X-ray Spectroscopy) analyses were performed. The obtained research results indicate that the replacement of a part of cement with finely ground CRT glass up to 15% by mass has a positive effect on the compressive strength of concrete in terms of its increase without compromising the durability of concrete. The results obtained by experimental testing unequivocally show that concrete mixtures made with partial replacement (up to 15%) of cement with finely ground CRT glass have the same freeze-thaw resistance, resistance to freeze/thaw with de-icing salt, resistance to wear by abrasion, and resistance to sulfate attack as the reference concrete. In terms of environmental protection, the use of CRT glass as a component for making concrete is also very significant.

The potential to use waste glass, including cathode ray tube (CRT) glass, for making new products or as an admixture to existing ones is being intensively investigated. This kind of research intensified particularly in the period after CRT TV sets and computer monitors were replaced in the market by the advanced technology of thin film transistor (TFT) and liquid crystal display (LCD) screens. Cathode ray tube glass represents a considerable part of electronic waste (e-waste). E-waste globally increases at a far higher rate than other solid waste materials. There is a possibility to recycle cathode ray tube glass and use it in the construction industry. This paper shows the test results of physical and mechanical properties of blocks and paving flags. The reference specimen was made with quartz sand, while the other product employed a combination of quartz sand and ground panel cathode ray tube glass. The glass was ground to the fraction 0.25/1.00 mm, which corresponds to quartz sand fineness. The following tests were performed: shape and dimensions, resistance to freeze/thaw and de-icing salts, water absorption, splitting tensile strength and tensile strength by bending. Special attention was paid to the tests of Böhme wear resistance, slip resistance of the top surface of CRT products using a pendulum, radioactivity and leaching. The texture of the experimental concrete products was observed by SEM (scanning electron microscopy) and analyzed. The results obtained by experimental testing unequivocally show that CRT glass can successfully be used for making concrete blocks and paving flags.

The topic of this paper is experimental and numerical analysis of the impact strength of unreinforced concrete slabs. Impact strength of concrete is significant in case of some accidental loads during exploitation. Impact strength can be determined experimentally, using Drop-weight test, Charpy test, Projectile impact test, Explosive test, etc. In this research, a numerical model for determining the impact strength of concrete slabs based on Finite element method (FEM) and high-end engineering software has been proposed. Modelling approach to this problem was applying the Explicit dynamics FEM analysis. Thereat, two different existing material models for concrete were enforced: Concrete damage plasticity model – CDP (implemented in ABAQUS/Explicit software), and the Riedel-Hiermaier-Thoma model – RHT (implemented in ANSYS Workbench software). Analysis parameters for both material models, necessary as input data, have been determined through a series of FEM analyses and validated by performed experiments, using drop-weight test. Results of the numerical analyses have been compared with the experimental ones, as well as mutually. Advantages and drawbacks of both material models are highlighted, as well as the reliability of the proposed numerical models. The proposed numerical FE models, confirmed by experiments, can be successfully used for determining impact strength of concrete slabs in further research.

Numerous factors influence the complexity of environmental and waste management problems, and the most significant goal is the reuse of materials that have completed their “life cycle” and the reduction in the use of new resources. In order to reduce impact of waste slag on the environment, in the present study, waste slag, generated in heating plants after lignite combustion, was characterized in detail and tested for application as a replacement for cement in mortar or concrete production. For physical–chemical characterization of slag, different experimental and instrumental techniques were used such as chemical composition and determination of the content of heavy metals, investigation of morphological and textural properties, thermal analysis, X-ray, and infrared spectroscopy. Physical–mechanical characterization of slag was also performed and included determination of activity index, water requirement, setting time and soundness. A leaching test was also performed. Presented results show that waste slag may be used in mortar and concrete production as a partial cement replacement, but after additional combustion at 650 °C and partial replacement of slag with silica fume in the minimal amount of 12%. The maximal obtained cement replacement was 20% (17.8% slag and 2.2% of silica fume).

The demand of the contemporary society for renewable energy sources lead to the increase of the bio-power plants. Accordingly, the amount of ash generated by burning the biomass is increased, and its disposal becomes a large...

This paper presents the results of testing the physical and mechanical properties and durability of geopolymer mixtures. Fly ash was used as the basic binder, while its replacement was performed with wood biomass ash.The initial and final setting tim...