Hot working tool steel (AISI H13) is one of the most common die materials used in casting industries. A die suffers from damage due to friction and wear during its lifetime. Therefore, various methods have been developed for its repair to save costs to manufacture a new one. A great benefit of laser additive manufacturing (cladding) is the 3D high production rate with minimal influence of thermal stresses in comparison with conventional arc methods. Residual stresses are important factors that influence the performance of the product, especially fatigue life. Therefore, the aim of this contribution is to correlate the wide range of results for multilayer cladding of H13 tool steel. X-ray and neutron diffraction experiments were performed to fully describe the residual stresses generated during cladding. Additionally, in-situ tensile testing experiments inside a scanning electron microscope were performed to observe microstructural changes during deformation. The results were compared with local hardness and wear measurements. Because laser cladding does not achieve adequate accuracy, the effect of necessary post-grinding was investigated. According to the findings, the overlapping of beads and their mutual tempering significantly affect the mechanical properties. Further, the outer surface layer, which showed tensile surface residual stresses and cracks, was removed by grinding and surface compressive residual stresses were described on the ground surface.

Knowledge of texture and residual stresses in tungsten heavy pseudoalloys is substantial for the microstructure optimization. These characteristics were determined in cold and warm rotary swaged W/NiCo composite with help of neutron diffraction. The results were discussed in view of the observed microstructure and mechanical properties. The investigated bars consisted of tungsten agglomerates (bcc lattice) surrounded by NiCo-based matrix (fcc lattice). No preferential crystallographic orientation was found in the as-sintered bar. A strong texture was formed in both the tungsten agglomerates ( fiber texture parallel to the swaging axis) and in the NiCo-based matrix ( fiber texture) after rotary swaging. Although usually of double-fiber texture, the fiber of the fcc structures was nearly missing in the matrix. Further, the cold-swaged bar exhibited substantially stronger texture for both phases which corresponds to the higher measured ultimate tensile strength. The residual stress differences were employed for characterization of the stress state of the bars. The largest residual stress difference (≈400 MPa) was found at the center of the bar deformed at room temperature. The hoop stresses were non-symmetrical with respect to the swaging axis, which was likely caused by the elliptical cross section of the as-sintered bar.