Additive manufacturing processes have been investigated for some years, and are commonly used industrially in the field of plastics for small- and medium-sized series. The use of metallic deposition material has been intensively studied on the laboratory scale, but the numerical prediction is not yet state of the art. This paper examines numerical approaches for predicting temperature fields, distortions, and mechanical properties using the Finite Element (FE) software MSC Marc. For process mapping, the filler materials G4Si1 (1.5130) for steel, and AZ31 for magnesium, were first characterized in terms of thermo-physical and thermo-mechanical properties with process-relevant cast microstructure. These material parameters are necessary for a detailed thermo-mechanical coupled Finite Element Method (FEM). The focus of the investigations was on the numerical analysis of the influence of the wire feed (2.5–5.0 m/min) and the weld path orientation (unidirectional or continuous) on the temperature evolution for multi-layered walls of miscellaneous materials. For the calibration of the numerical model, the real welding experiments were carried out using the gas-metal arc-welding process—cold metal transfer (CMT) technology. A uniform wall geometry can be produced with a continuous welding path, because a more homogeneous temperature distribution results.

In this investigation, the fabrication of functionally graded structures of SS316L to Ni-based alloys were studied, using the novel technique 3D plasma metal deposition. Two Ni-based alloys were used, a heat resistance alloy Ni80-20 and the solid-solution strengthened Ni625. Different configurations were analyzed, for the Ni80-20 a hard transition and a smooth transition with a region of 50% SS316L/50% Ni80-20. Regarding the structures with Ni625, a smooth transition configuration and variations in the heat input were applied. The effect of the process parameters on the geometry of the structures and the microstructures was studied. Microstructure examinations were carried out using optical and scanning electron microscopy. In addition, microhardness analysis were made on the interfaces. In general, the smooth transition of both systems showed a gradual change in the properties. The microstructural results for the SS316L (both systems) showed an austenite matrix with δ-phase. For the mixed zone and the Ni80-20 an austenite (γ) matrix with some M₇C₃ precipitates and laves phase were recognized. The as-built Ni625 microstructure was composed of an austenite (γ) matrix with secondary phases laves and δ-Ni3Nb, and precipitates M₇C₃. The mixed zone exhibited the same phases but with changes in the morphology.

Advanced high-performance filler metals for wire arc additive manufacturing (WAAM) exist on the market already. Nevertheless, these high-strength steels are not yet widely used in industrial applications due to limited knowledge of cold-cracking susceptibility, welding residual stresses, and therefore sufficient safety in terms of manufacturing and operation. High residual stresses promote cold-cracking risk, especially in the welding of high-strength steels, as the result of a complex interaction between the applied material, process conditions, and component design. The focus of the present investigation was the determination of the influence of the process parameters on the ∆t_8/5 cooling time, mechanical properties, and residual stresses to correlate, for the first time, heat control, cooling conditions, and residual stress for WAAM of high-strength filler materials. This contributed to the knowledge regarding the safe avoidance of cold cracking. In addition to a thermophysical simulation using a dilatometer of different high-strength steels with subsequent tensile testing, reference WAAM specimens (open hollow cuboids) were welded while utilizing a high-strength filler metal (ultimate tensile strength > 790 MPa). The heat control was varied by means of the heat input and interlayer temperature such that the ∆t_8/5 cooling times corresponded to the recommended processing range (approx. 5 s to 20 s). For the heat input, significant effects were exhibited, in particular on the local residual stresses in the component. Welding with an excessive heat input or deposition rate may lead to low cooling rates, and hence to unfavorable microstructure and component properties, but at the same time, is intended to result in lower tensile residual stress levels. Such complex interactions must ultimately be clarified to provide users with easily applicable processing recommendations and standard specifications for an economical WAAM of high-strength steels. These investigations demonstrated a major influence of the heat input on both the cooling conditions and the residual stresses of components manufactured with WAAM using high-strength filler materials. A higher heat input led to longer cooling times (∆t_8/5) and approx. 200 MPa lower residual stresses in the surface of the top layer.

High-strength steels offer potential for weight optimization due to reduced wall thicknesses in modern constructions. Additive manufacturing processes such as Wire Arc Additive Manufacturing (WAAM) enable the resource-efficient production of structures. In the case of defects occurring in weld seams or WAAM components due to unstable process conditions, the economical solution is local gouging or machining and repair welding. It is important to understand the effects of machining steps on the multiaxial stress state in conjunction with the design-related shrinkage restraints. Research into how welding and slot milling of welds and WAAM structures affects residual stresses is still lacking. For this reason, component-related investigations with high-strength steels with yield strengths ≥790 MPa are carried out in our research. In-situ digital image correlation (DIC) and ex-situ X-ray diffraction (XRD) were used to analyze the stresses and strains induced on specimens during and after milling. The systematic analyses revealed a significant interaction of the stiffness and microstructure of the specimens with the initial residual stresses induced by welding. Subsequent repair welds can result in significantly higher residual stresses.

Market demands coating processes with high-performance, high reliability, high flexibility for processing of complex geometries and multi-material depositions, as well as increased deposition rates. The systematic coupling of two plasma transferred arc welding systems that interact in the same melt pool to form a tandem Plasma Transferred Arc (PTA) system accomplishes these tasks. Previous research has shown that the deposition rate with the tandem PTA method reaches 240 percent when comparing to the conventional single torch PTA method. Within one layer, up to four different powders and powder fractions can be combined at the same time. This allows for the creation of multi-material coatings that are suitable for sustaining high mechanical loads and wear- and temperature-resistant surfaces by use of tungsten carbides (WC). This study examines and analyzes defined functionally graded structures made from super duplex steel 1.4410 and corrosion resistant austenitic steel 1.4404. The mechanical-chemical properties of the tandem PTA system can be precisely controlled by changing the powder feeding positions. Furthermore, an additively manufactured specimen from previous studies is examined and evaluated. A direct comparison with conventional single torch PTA was performed to demonstrate the benefits of the tandem PTA-process.