Poly(ε-caprolactone) (PCL) and poly(lactic acid) (PLA) blends were compatibilized by reactive blending and by copolymers formed during reaction in the solution. The reactive blending of PCL/PLA was performed using di-(2-tert-butyl-peroxyisopropyl)benzene (BIB) or dicumyl peroxide (DCP) as radical initiator. PCL-g-PLA copolymers were prepared using 1.0 wt. % of DCP or BIB via reaction in solution, which was investigated through a Fourier transform infrared spectrometry (FTIR) and nuclear magnetic resonance (NMR) in order to better understand the occurring mechanisms. The effect of different additions such as PCL-g-PLA copolymers, DCP, or BIB on the properties of PCL/PLA blends was studied. The unmodified PCL/PLA blends showed a sea-island morphology typical of incompatible blends, where PLA droplets were dispersed in the PCL matrix. Application of organic peroxides improved miscibility between PCL and PLA phases. A similar effect was observed for PCL/PLA blend compatibilized by PCL-g-PLA copolymer, where BIB was used as initiator. However, in case of application of the peroxides, the PCL/PLA blends were cross-linked, and it has been confirmed by the gel fraction and melt flow index measurements. The thermal and mechanical properties of the blends were also investigated by means of differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA), and tensile strength.

Wood-polymer composites technologies are gaining more and more attention in the scientific community, positively affecting the increase in their industrial applications, for example, automotive, building, 3D printing, etc. Many research works are focused on the improvement in matrix–lignocellulosic filler interactions to produce highly filled composites with satisfying performance properties. In this field of research, using isocyanates due to their versatile structure and functionality seems to be a very promising approach. This paper aims at reporting on recent advances in compatibilization strategies of wood-polymer composites by isocyanates. Particular attention is focused on the correlation between isocyanate structure, as well as modification conditions on the matrix–lignocellulosic filler interactions and their impact on the structure–property relationships of wood-polymer composites. Furthermore, limitations and future research trends related to applications of isocyanate to wood-polymer composites technologies are also discussed.

The modification of poly(ε-caprolactone) (PCL) was successfully conducted during reactive processing in the presence of dicumyl peroxide (DCP) or di-(2-tert-butyl-peroxyisopropyl)-benzene (BIB). The peroxide initiators were applied in the various amounts of 0.5 or 1.0 pbw (part by weight) into the PCL matrix. The effects of the initiator type and its concentration on the structure and mechanical and thermal properties of PCL were investigated. To achieve a detailed and proper explication of this phenomenon, the decomposition and melting temperatures of DCP and BIB initiators were measured by differential scanning calorimetry. The conjecture of the branching or cross-linking of PCL structure via used peroxides was studied by gel fraction content measurement. Modification in the presence of BIB in PCL was found to effectively increase gel fraction. The result showed that the cross-linking of PCL started at a low content of BIB, while PCL modified by high DCP content was only partially cross-linked or branched. PCL branching and cross-linking were found to have a significant impact on the mechanical properties of PCL. However, the effect of used initiators on poly(ε-caprolactone) properties strongly depended on their structure and content. The obtained results indicated that, for the modification towards cross-linking/branching of PCL structure by using organic peroxides, the best mechanical properties were achieved for PCL modified by 0.5 pbw BIB or 1.0 pbw DCP, while the PCL modified by 1.0 pbw BIB possessed poor mechanical properties, as it was related to over cross-linking.

Reactive blending is a promising approach for the sustainable development of bio-based polymer blends and composites, which currently is gaining more and more attention. In this paper, biodegradable blends based on poly(ε-caprolactone) (PCL) and poly(lactic acid) (PLA) were prepared via reactive blending performed in an internal mixer. The PCL and PLA content varied in a ratio of 70/30 and 55/45. Reactive modification of PCL/PLA via liquid organic peroxides (OP) including 0.5 wt.% of tert-butyl cumyl peroxide (BU), 2,5-dimethyl-2,5-di-(tert-butylperoxy)-hexane (HX), and tert-butyl peroxybenzoate (PB) is reported. The materials were characterized by rotational rheometer, atomic force microscopy (AFM), thermogravimetry (TGA), differential scanning calorimetry (DSC), tensile tests and biodegradability tests. It was found that the application of peroxides improves the miscibility between PCL and PLA resulted in enhanced mechanical properties and more uniform morphology. Moreover, it was observed that the biodegradation rate of PCL/PLA blends reactively compatibilized was lower comparing to unmodified samples and strongly dependent on the blend ratio and peroxide structure. The presented results confirmed that reactive blending supported by organic peroxide is a promising approach for tailoring novel biodegradable polymeric systems with controllable biodegradation rates.

The amount of elastomeric waste, especially from tires is constantly increasing on a global scale. The recycling of these residua should be considered a priority. Compounding the waste rubbers with other polymers can be an excellent alternative to reuse waste materials. This procedure requires solving the issue of the lack of compatibility between the waste rubber particles and other polymers. Simultaneously, there is a claim for introducing biodegradable plastics materials to reduce their environmental impact. In this work, reclaimed rubber/poly(ε-caprolactone) (RR/PCL) blends are proposed to enhance the recycling and upcycling possibilities of waste rubbers. The results show that the addition of PCL to the RR allows obtaining blends with improved mechanical properties, good thermal stability, and enhanced interfacial compatibility between the used components. Structure and properties of the proposed RR/PCL have been studied by means of static and dynamic mechanical testing, Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA)-FTIR analysis.