Laser-induced graphene (LIG) has the advantages of one-step fabrication, prominent mechanical performance, as well as high conductivity; it acts as the ideal material to fabricate flexible strain sensors. In this study, a wearable flexible strain sensor consisting of three-dimensional (3D) wavy LIG and silicone rubber was reported. With a laser to scan on a polyimide film, 3D wavy LIG could be synthesized on the wavy surface of a mold. The wavy-LIG strain sensor was developed by transferring LIG to silicone rubber substrate and then packaging. For stress concentration, the ultimate strain primarily took place in the troughs of wavy LIG, resulting in higher sensitivity and less damage to LIG during stretching. As a result, the wavy-LIG strain sensor achieved high sensitivity (gauge factor was 37.8 in a range from 0% to 31.8%, better than the planar-LIG sensor), low hysteresis (1.39%) and wide working range (from 0% to 47.7%). The wavy-LIG strain sensor had a stable and rapid dynamic response; its reversibility and repeatability were demonstrated. After 5000 cycles, the signal peak varied by only 2.32%, demonstrating the long-term durability. Besides, its applications in detecting facial skin expansion, muscle movement, and joint movement, were discussed. It is considered a simple, efficient, and low-cost method to fabricate a flexible strain sensor with high sensitivity and structural robustness. Furthermore, the wavy-LIG strain senor can be developed into wearable sensing devices for virtual/augmented reality or electronic skin.

Multi-needle electrospinning technology is a method for mass production of nanofibers, which can improve the production efficiency of nanofibers by increasing the number and density of needles for multi-needle electrospinning. However, when the arrangement density of the needle is high, the electric field of the needle tip is not uniform, causing instability such as jet dripping and broken jet. In this paper, the electric field uniformity optimization problem of multi-needle electrospinning technology is used to simulate the needle tip electric field by using COMSOL finite element analysis software. The influence of the needle size and the dielectric material on the electric field of the tip was studied. Finally, the method of using dielectric material on the tip of the middle part of the needle is beneficial to the electric field uniformity. The uniformity of the needle tip electric field in the case of high-density arrangement of the needle is realized, and the nozzle is provided for mass production of nanofibers by multi-needle electrospinning.

The electrospinning electric field is the main factor responsible for the jet stretching force. Previous studies showed that nonhomogeneous electric field would affect the jets formed during the multi-needles electrospinning. Therefore, a multitude of methods were explored to optimize the electric field in multi-needles electrospinning, such as adjusting the supplied voltage on each needle, varying the space of the needles and spatial distribution of the needles. In this paper, three categories of needles distribution were explored for a homogeneous electric field and the design of a higher needles density of electrospinning head. The theoretical and experimental results showed that the homogeneous electric field formed with the trapezoidal head at 15mm distance while the others’ head required over 30mm. Hence, the trapezoidal arrangement is a better multi-needles distribution for electrospinning head, and has much more significance for high yield of electrospinning nanofibers.

Micro/nanofibers prepared by direct-writing using an electrospinning (ES) technique have drawn more attention recently owing to their intriguing physical properties and great potential as building blocks for micro/nanoscale devices. In this work, a wavy direct-writing (WDW) process was developed to directly write serpentine micro/nano structures suitable for the fabrication of micro devices. This fabrication ability will realize the application of electrospun-nanofiber-based wiring of structural and functional components in microelectronics, MEMS, sensor, and micro optoelectronics devices, and, especially, paves the way for the application of electrospinning in printing serpentine interconnector of large-area organic stretchable electronics.

Wavy fibers fabricated by electrohydrodynamic jet printing (E-J-P) have been used in many applications, such as sensors, electromechanical systems, stretchable electronics products, and flexible displays. Auxiliary electrodes (A-E) were initially used to control the deposited morphology of the wavy fibers in this study. A polyethylene oxide solution was electrospun with an applied voltage of 1 kV and an alternating current power (ACP) supplied to A-E. The experimental results show that the amplitude can be controlled by the voltage of the ACP, and the generated frequency of the wavy fiber is the same as the frequency of the ACP.

Electrospinning technology is considered to be one of the efficient, convenient, and low-cost technologies for preparing nanofibers, which can be applied in various industries, including filtration, catalysis, and energy. Here, aiming at the performance requirements of the nanometer fiber filter membrane for filtering PM2.5, the preparation of the nanofiber filter membrane was realized based on multi-needle electrospinning equipment. Meanwhile, by adding silver nitrate to the spinning solution, a polyvinylidene fluoride antibacterial nanofiber filter layer with high filtration efficiency and low resistance was successfully prepared on the traditional air conditioning filter meshes. We found that four key factors affecting the filtration performance include ambient humidity, substrate meshes, voltage, and production rate. Among them, voltage and production rate are the key factors affecting the filtration performance. According to the development trend of multifunctional nanofiber membranes, the preparation of air conditioning filters with nanofibers as the main filter material was realized, producing air conditioning filter membranes with antibacterial and deodorizing functions. This article provides a reliable experimental basis and empirical reference for the preparation of nanofiber membranes based on multi-needle electrospinning technology.