The degradation of organic pollutants in wastewaters assisted by oxide semiconductor nanostructures has been the focus of many research groups over the last decades, along with the synthesis of these nanomaterials by simple, eco-friendly, fast, and cost-effective processes. In this work, porous zinc oxide (ZnO) nanostructures were successfully synthesized via a microwave hydrothermal process. A layered zinc hydroxide carbonate (LZHC) precursor was obtained after 15 min of synthesis and submitted to different calcination temperatures to convert it into porous ZnO nanostructures. The influence of the calcination temperature (300, 500, and 700 °C) on the morphological, structural, and optical properties of the ZnO nanostructureswas investigated. All ZnO samples were tested as photocatalysts in the degradation of rhodamine B (RhB) under UV irradiation and natural sunlight. All samples showed enhanced photocatalytic activity under both light sources, with RhB being practically degraded within 60 min in both situations. The porous ZnO obtained at 700 °C showed the greatest photocatalytic activity due to its high crystallinity, with a degradation rate of 0.091 and 0.084 min⁻¹ for UV light and sunlight, respectively. These results are a very important step towards the use of oxide semiconductors in the degradation of water pollutants mediated by natural sunlight.

The impact of a parylene top-coating layer on the illumination and bias stress instabilities of indium-gallium-zinc oxide thin-film transistors (TFTs) is presented and discussed. The parylene coating substantially reduces the threshold voltage shift caused by continuous application of a gate bias and light exposure. The operational stability improves by 75%, and the light induced instability is reduced by 35%. The operational stability is quantified by fitting the threshold voltage shift with a stretched exponential model. Storage time as long as 7 months does not cause any measurable degradation on the electrical performance. It is proposed that parylene plays not only the role of an encapsulation layer but also of a defect passivation on the top semiconductor surface. It is also reported that depletion-mode TFTs are less sensitive to light induced instabilities. This is attributed to a defect neutralization process in the presence of free electrons.

Semiconductor nanowires are mostly processed by complex, expensive and high temperature methods. In this work, with the intent of developing zinc tin oxide nanowires (ZTO NWs) by low-cost and low-complexity processes, we show a detailed study on the influence of chemical parameters in the hydrothermal synthesis of ZTO nanostructures at temperatures of only 200 °C. Two different zinc precursors, the ratio between zinc and tin precursors, the concentration of the surfactant agent and of the mineralizer were studied. The type and the crystallinity of the nanostructures was found to be highly dependent on the used precursors and on the concentration of each reagent. Conditions for obtaining different ZTO nanostructures were achieved, namely Zn₂SnO₄ nanoparticles and ZnSnO₃ nanowires with length ≈ 600 nm, with the latter being reported for the first time ever by hydrothermal methods without the use of seed layers. Optical and electrical properties were analyzed, being obtained band gaps of 3.60 and 3.46 eV, for ZnSnO₃ and Zn₂SnO₄, respectively, and a resistivity of 1.42 kΩ∙cm for single ZnSnO₃ nanowires, measured using nanomanipula-tors after localized deposition of Pt electrodes by e-beam assisted gas decomposition. The low-temperature hydrothermal methods explored here proved to be a low-cost, reproducible and highly flexible route to obtain multicomponent oxide nanostructures, particularly ZTO NWs. The diversity of the synthetized ZTO structures have potential application in next-generation nanoscale devices such as field effect nanotransistors, nanogenerators, resistive switching memories, gas sensors and photocatalysis.

Poly(p-xylylene) derivatives, widely known as Parylenes, have been considerably adopted by the scientific community for several applications, ranging from simple passive coatings to active device components. Here, we explore the thermal, structural, and electrical properties of Parylene C, and further present a variety of electronic devices featuring this polymer: transistors, capacitors, and digital microfluidic (DMF) devices. We evaluate transistors produced with Parylene C as a dielectric, substrate, and encapsulation layer, either semitransparent or fully transparent. Such transistors exhibit steep transfer curves and subthreshold slopes of 0.26 V/dec, negligible gate leak currents, and fair mobilities. Furthermore, we characterize MIM (metal–insulator–metal) structures with Parylene C as a dielectric and demonstrate the functionality of the polymer deposited in single and double layers under temperature and AC signal stimuli, mimicking the DMF stimuli. Applying temperature generally leads to a decrease in the capacitance of the dielectric layer, whereas applying an AC signal leads to an increase in said capacitance for double-layered Parylene C only. By applying the two stimuli, the capacitance seems to suffer from a balanced influence of both the separated stimuli. Lastly, we demonstrate that DMF devices with double-layered Parylene C allow for faster droplet motion and enable long nucleic acid amplification reactions.