This review article proposes the identification and basic concepts of materials that might be used for the production of high-performance concrete (HPC) and ultra-high-performance concrete (UHPC). Although other reviews have addressed this topic, the present work differs by presenting relevant aspects on possible materials applied in the production of HPC and UHPC. The main innovation of this review article is to identify the perspectives for new materials that can be considered in the production of novel special concretes. After consulting different bibliographic databases, some information related to ordinary Portland cement (OPC), mineral additions, aggregates, and chemical additives used for the production of HPC and UHPC were highlighted. Relevant information on the application of synthetic and natural fibers is also highlighted in association with a cement matrix of HPC and UHPC, forming composites with properties superior to conventional concrete used in civil construction. The article also presents some relevant characteristics for the application of HPC and UHPC produced with alkali-activated cement, an alternative binder to OPC produced through the reaction between two essential components: precursors and activators. Some information about the main types of precursors, subdivided into materials rich in aluminosilicates and rich in calcium, were also highlighted. Finally, suggestions for future work related to the application of HPC and UHPC are highlighted, guiding future research on this topic.

The fresh and rheological properties of alkali mortars activated by blast furnace slag (BFS) were investigated. Consistency tests, squeeze flow, dropping ball, mass density in the hardened state, incorporated air, and water retention were performed. Mortars were produced with the ratio 1:2:0.45 (binder:sand:water), using not only ordinary Portland cement for control but also BFS, varying the sodium content of the activated alkali mortars from 2.5 to 15%. The results obtained permitted understanding that mortars containing 2.5 to 7.5% sodium present a rheological behavior similar to cementitious mortars by the Bingham model. In turn, the activated alkali mortars containing 10 to 15% sodium showed a very significant change in the properties of dynamic viscosity, which is associated with a change in the type of model, starting to behave similar to the Herschel–Bulkley model. Evaluating the properties of incorporated air and water retention, it appears that mortars containing 12.5% and 15% sodium do not have compatible properties, which is related to the occupation of sodium ions in the interstices of the material. Thus, it is concluded that the techniques used were consistent in the rheological characterization of activated alkali mortars.

Construction and demolition activities consume large amounts of natural resources, generating 4.5 bi tons of solid waste/year, called construction and demolition waste (C&DW) and other wastes, such as ceramic, polyethylene terephthalate (PET), glass, and slag. Furthermore, around 32 bi tons of natural aggregate (NA) are extracted annually. In this scenario, replacing NA with recycled aggregate (RA) from C&DW and other wastes can mitigate environmental problems. We review the use of RA for concrete production and draw the main challenges and outlook. RA reduces concrete’s fresh and hardened performance compared to NA, but these reductions are often negligible when the replacement levels are kept up to 30%. Furthermore, we point out efficient strategies to mitigate these performance reductions. Efforts must be spent on improving the efficiency of RA processing and the international standardization of RA.