During the construction of concrete structures, it is often useful to know compressive strength at an early age. This is an amount of strength required for the safe removal of formwork, also known as stripping strength. It is certainly helpful to determine this strength non-destructively, i.e., without any invasive steps that would damage the structure. Second only to the ultrasonic pulse velocity test, the rebound hammer test is the most common NDT method currently used for this purpose. However, estimating compressive strength using general regression models can often yield inaccurate results. The experiment results show that the compressive strength of any concrete can be estimated using one’s own newly created regression model. A traditionally constructed regression model can predict the strength value with 50% reliability, or when two-sided confidence bands are used, with 95% reliability. However, civil engineers usually work with the so-called characteristic value defined as a 5% quantile. Therefore, it appears suitable to adjust conventional methods in order to achieve a regression model with 95% one-sided reliability. This paper describes a simple construction of such a characteristic curve. The results show that the characteristic curve created for the concrete in question could be a useful tool even outside of practical applications.

The modulus of elasticity is a property of concrete, which is known for its high variability of values. A high enough value of the modulus of elasticity is a critical requirement in complicated concrete structures and in order to attain it, a number of factors must be taken into account, as it is subject to many. Curing is one of the most important influences. It can be described as an effort to maintain the temperature of concrete within the correct limits, prevent loss of water and the shrinkage connected with this. This paper describes an experiment focused on the observation of the development of the dynamic and static modulus of elasticity in dependence on the method of curing. The experiment worked with air-entrained as well as non-air-entrained concrete of the C 30/37 strength class. The results show that the curing method strongly affects not only the development, but also the final values of the concrete modulus of elasticity

The paper deals with the experimental determination of shrinkage development during concrete ageing. Three concrete mixtures were made. They differed in the amount of cement in the fresh mixture, 300, 350, and 400 kg/m³. In order to determine the influence of plasticiser on the progress of volume changes, another three concrete mixtures were prepared with plasticiser in the amount of 0.25% by cement mass. Measurements were performed with the goal of observing the influence of cement and plasticiser content on the overall development of volume changes in the concrete. Changes in length and mass losses of the concrete during ageing were measured simultaneously. The continuous measurement of concrete mass losses caused by drying of the specimen’s surface proved useful during the interpretation of results obtained from the concrete shrinkage measurement. During the first 24 hours of ageing, all the concrete mixtures exhibited swelling. Its magnitude and progress were influenced by cement, water, and plasticiser content. However, a loss of mass caused by water evaporation from the surface of the specimens was also recorded in this stage. The measured progress of shrinkage corresponded well to the progress of mass loss.

This manuscript deals with a complex analysis of acoustic emission signals that were recorded during freeze-thaw cycles in test specimens produced from air-entrained concrete. An assessment of the resistance of concrete to the effects of freezing and thawing was conducted on the basis of a signal analysis. Since the experiment simulated testing of concrete in a structure, a concrete block with the height of 2.4 m and width of 1.8 m was produced to represent a real structure. When the age of the concrete was two months, samples were obtained from the block by core drilling and were subsequently used to produce test specimens. Testing of freeze-thaw resistance of concrete employed both destructive and non-destructive methods including the measurement of acoustic emission, which took place directly during the freeze-thaw cycles. The recorded acoustic emission signals were then meticulously analysed. The aim of the conducted experiments was to verify whether measurement using the acoustic emission method during Freeze-thaw (F-T) cycles are more sensitive to the degree of damage of concrete than the more commonly employed construction testing methods. The results clearly demonstrate that the acoustic emission method can reveal changes (e.g., minor cracks) in the internal structure of concrete, unlike other commonly used methods. The analysis of the acoustic emission signals using a fast Fourier transform revealed a significant shift of the dominant frequency towards lower values when the concrete was subjected to freeze-thaw cycling.

The paper deals with an experimental analysis focusing on the utilization of a specific measurement technique for determining the development of shrinkage and for monitoring structural changes in fine-grained cement-based composites during their ageing. Advanced measurement equipment and procedure allowing simultaneous measurement of length changes, mass losses, acoustic responses, and temperature development were designed and verified by the experimental investigation. The main scope of the experiments performed was focused on finding the relationships between the characteristics being investigated while maintaining a uniform test setup. For the purpose of the experimental measurement, three fine-grained cement composite mixtures were designed and manufactured. The mixtures differed in the water-to-cement ratio (w/c) and in the amount of plasticizer. The measurement outputs are presented in the form of diagrams showing the relations between the studied parameters, such as relative length changes, mass losses, temperature progress, and acoustic emission (AE) activity during solidification of the composites. The measurement results showed close relations between the examined characteristics. The progress of relative length changes together with the progress of mass losses and temperature development is reflected in the AE activity. The advanced measurement procedure and technique provided valuable information about the behaviour of cement-based composites during early setting and long-term hardening.