Methoxyl-capped MQ silicone resin (MMQ) was first synthesized by the hydrosilylation of vinyl-containing MQ silicone resin and trimethoxysilane and then used in condensed room-temperature vulcanized (RTV) silicone rubber as a self-reinforced cross-linker. Results show that modified silicone rubber exhibits good light transmission. Compared with unmodified silicone rubber, the hardness, tensile strength and elongation of MMQ at the break are increased by 26.4 A, 2.68 MPa and 65.1%, respectively. In addition, the characteristic temperature of 10% mass loss is delayed from 353.5 °C to 477.1 °C, the temperature at maximum degradation rate is also delayed from 408.9 °C to 528.4 °C and the residual mass left at 800 °C is increased from 1.2% to 27.7%. These improved properties are assigned to the synergistic effect of the rigid structure of MMQ, the formation of a dense cross-linking structure in polymers and the uniform distribution of MMQ cross-linking agent in RTV silicone rubber.

With developments of the electronics industry, more components are being included in electronic devices, which has led to challenges in thermal management. Using reduced graphene oxide embedded with MQ silicone resin (RGO/MQ) nano-aggregates as the composite filler and silicone rubber (SR) as the matrix, a simple approach is designed to prepare RGO/MQ/SR composites. Reduced graphene oxide (RGO) was first used as a substrate for the growth of MQ silicone resin by hybridization, forming sandwich-like micro structured RGO/MQ nano-aggregates successfully. Then, RGO/MQ was integrated into α,ω-dihydroxylpolydimethylsiloxane based on the in situ solvent-free blending method, followed by condensation and vulcanization, fabricating the final RGO/MQ/SR composites. The effective strategy could enhance the adaptability between graphene and silicone matrix under external stimuli at room temperature by embedding nanoscale MQ into the interface of graphene/silicone as the buffer layer. Obvious improvements were found in both thermal conductivity and mechanical properties due to excellent dispersion and interfacial compatibility of RGO/MQ in the host materials. These attractive results suggest that this RGO/MQ/SR composite has potential as a thermal interface material for heat dissipation applications.

Microfibril cellulose (MFC), which is detrimental to soil cultivation and environmental protection, is derived from waste pineapple leaves. Hexagonal boron nitride (h-BN) was modified with polydopamine (PDA)—PDA@h-BN named pBN, and then combined with MFC to prepare a novel hybrid powder. The effect of PDA on h-BN and the binding effect between pBN and MFC were characterized by X-ray photoelectron spectroscopy (XPS), Thermogravimetric (TG), scanning electron microscopy (SEM), and Fourier Transform-Infrared (FT-IR). Poly (vinyl alcohol) (PVA) was used as an eco-friendly polymeric matrix to prepare a pBN-MFC-PVA composite film. The mechanical strength, hydrophobicity, and thermal conductivity of the film were studied and the results confirmed that h-BN was chemically modified with PDA and was uniformly distributed along the MFC. The thermal conductivity of the pBN-MFC-PVA composite film increased with the addition of a pBN-MFC novel powder. MFC acted as “guides” to mitigate the h-BN agglomerate. In addition to the possible usage in the pBN-MFC-PVA composite film itself, the pBN-MFC hybrid powder may be a potential filler candidate for manufacturing thermal interface materials and wearable devices or protective materials.

As a new kind of functionalized polysiloxane with chemical reactivity, bio-phenol polysiloxane was synthesized through facile heterogeneous catalytic route. Bio-phenol polysiloxane/polycarbonate (Si/PC) block copolymer was synthesized via a three-step approach, and the effect of the amount of bio-phenol polysiloxane on the properties of Si/PC copolymer was then studied. The structure and morphology of Si/PC copolymer were characterized, showing that, when the amount of bio-phenol polysiloxane reached 20%, the pyrolysis temperature of Si/PC copolymer at 5% weight loss was 450.8 °C which was 76.1 °C higher than pure PC. The oxygen permeability of 20%Si/PC copolymer membrane was 502.65 cm³/m²·24h·0.1MPa, which was increased by 128.4% compared with pure PC membrane. The mechanical property and hydrophobicity of Si/PC copolymer had been improved.

Eugenol, used as bio-phenol, was designed to replace the hydrogen atom of hydrogenterminated siloxane by hydrosilylation reaction under the presence of alumina-supported platinum catalyst (Pt-Al₂O₃), silica-supported platinum catalyst (Pt-SiO₂) and carbon nanotube-supported platinum catalyst (Pt-CNT), respectively. The catalytic activities of these three platinum catalysts were measured by nuclear magnetic resonance hydrogen spectrometer (¹H NMR). The properties of bio-phenol siloxane were characterized by Fourier transform infrared spectrometer (FT–IR), UV-visible spectrophotometer (UV) and thermogravimeter (TGA), and its antibacterial property against Escherichia coli was also studied. The results showed that the catalytic activity of the catalyst Pt-CNT was preferable. When the catalyst concentration was 100 ppm, the reaction temperature was 80 °C and reaction time was 6 h, the reactant conversion rate reached 97%. After modification with bio-phenol, the thermal stability of the obtained bio-phenol siloxane was improved. For bio-phenol siloxane, when the ratio of weight loss reached 98%, the pyrolysis temperature was raised to 663 °C which was 60 °C higher than hydrogenterminated siloxane. Meanwhile, its autonomic antibacterial property against Escherichia coli was improved significantly.

Graphene (GR) was used to blend with eugenol polysiloxane-polycarbonate (Si-PC) copolymer to prepare a Si-PC/GR nanocomposite via a solution blending method and the impact of graphene on the properties of Si-PC/GR nanocomposite was investigated. The morphology and structure of the Si-PC/GR nanocomposite were characterized. Combining morphology and property analysis, the result showed that when the graphene dispersed uniformly in the Si-PC matrix, the mechanical properties, thermostability and barrier property of Si-PC/GR nanocomposite were enhanced. Compared with Si-PC copolymer, the pyrolytic temperature of Si-PC/2.5%GR nanocomposite at 5% weight loss was 434.3 °C, which was 20.6 °C higher than Si-PC copolymer; and the oxygen barrier value of Si-PC/1.5%GR nanocomposite decreased to 160.2 cm³/m² 24 h 0.1 MPa, which was 53.2 less than pure Si-PC. The mechanical properties of Si-PC/GR nanocomposite were enhanced with an appropriate additive amount of graphene. The hydrophobicity also had been enhanced at the meantime.