A surface modification of polyamide 6 (PA), polyethylene terephthalate (PET) and polypropylene (PP) textiles was performed using zinc oxide to obtain antibacterial layer. ZnO microrods were synthesized on ZnO nanoparticles (NPs) as a nucleus centers by chemical bath deposition (CBD) process. Scanning Electron Microscopy (SEM) and X-ray diffraction (XRD) indicated that wurzite ZnO microrods were obtained on every sample. Differential Scanning Calorimetry (DSC), Fourier Transform Infrared Spectroscopy (FTIR), Atomic Force Microscopy (AFM) and Liquid Absorption Capacity (LAC) analysis indicate that the amount and structure of antibacterial layer is dependent on roughness and wettability of textile surface. The rougher and more hydrophilic is the material, the more ZnO were deposited. All studied textiles show significant bactericidal activity against Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus). A possible mechanism and difference in sensitivity between Gram-negative and Gram-positive bacteria to ZnO is discussed. Considering that antibacterial activity of ZnO is caused by Reactive Oxygen Species (ROS) generation, an influence of surface to volume ratio and crystalline parameters is also discussed.

Surgical meshes were modified with zinc oxide (ZnO) using a chemical bath deposition method (CBD) at 50 °C, 70 °C, or 90 °C, in order to biologically activate them. Scanning electron microscopy (SEM), mass changes, and X-ray diffraction measurements revealed that at low temperatures Zn(OH)₂ was formed, and that this was converted into ZnO with a temperature increase. The antimicrobial activity without light stimulation of the ZnO modified Mersilene™ meshes was related to the species of microorganism, the incubation time, and the conditions of the experiment. Generally, cocci (S. aureus, S. epidermidis) and yeast (C. albicans) were more sensitive than Gram-negative rods (E. coli). The differences in sensitivity of the studied microorganisms to ZnO were discussed. The most active sample was that obtained at 90 °C. The mechanism of antimicrobial action of ZnO was determined by various techniques, such as zeta potential analysis, electron paramagnetic resonance (EPR) spectroscopy, SEM studies, and measurements of Zn(II) and reactive oxygen species (ROS) concentration. Our results confirmed that the generation of free radicals was crucial, which occurs on the surface of crystalline ZnO.

According to recent research, the use of nanoparticles as a gas-sensitive material increases the selectivity and sensitivity and shortens the response time of a sensor. However, the synthesis of SnO₂ nanoparticles presents many difficulties. The following article presents a simple and inexpensive method for the synthesis of SnO₂ nanoparticles. The influence of the surfactant and polymer choice on the size of the resulting nanoparticles was investigated and a mechanism describing their interaction was proposed. It was found that stable colloids of SnO₂ nanoparticles are formed in the presence of both PEI and Triton X-100 surfactants as stabilising agents. However, an additional factor essential for good stabilisation of the nanoparticles was an appropriate acidity level of the solution. Under optimal conditions, nanoparticles having an average diameter of about 10 nm are reproducibly formed.

Gas sensitive structures made of nanowires exhibit extremally large specific surface area, and a great number of chemically active centres that can react with the ambient atmosphere. This makes the use of nanomaterials promising for super sensitive gas sensor applications. Monoclinic β-Ga₂O₃ nanowires (NWs) were synthesized from metallic gallium at atmospheric pressure in the presence of nitrogen and water vapor. The nanowires were grown directly on interdigitated gold electrodes screen printed on Al₂O₃ substrates, which constituted the gas sensor structure. The observations made with transmission electron microscope (TEM) have shown that the nanowires are monocrystalline and their diameters vary from 80 to 300 nm with the average value of approximately 170 nm. Au droplets were found to be anchored at the tips of the nanowires which may indicate that the nanowires followed the Vapor–Liquid–Solid (VLS) mechanism of growth. The conductivity of β-Ga₂O₃ NWs increases in the presence of volatile organic compounds (VOC) even in the temperature below 600 °C. The gas sensor based on the synthesized β-Ga₂O₃ NWs shows peak sensitivity to 100 ppm of ethanol of 75.1 at 760 °C, while peak sensitivity to 100 ppm of acetone is 27.5 at 690 °C.