The paper presents a method of modifying polyacrylonitrile (PAN) fibers using polyaniline (PANI). The PAN fibers were doped with polyaniline that was obtained in two different ways. The first consisted of doping a spinning solution with polyaniline that was synthesized in an aqueous solution (PAN/PANI blended), and the second involved the synthesis of polyaniline directly in the spinning solution (PAN/PANI in situ). The obtained fibers were characterized by the methods: X-ray powder diffraction (XRD), scanning electron microscope (SEM), fourier-transform infrared spectroscopy (FTIR), thermogravimetry (TG) and differential scanning calorimetry (DSC). Analysis of the results showed strong interactions between the nitrile groups of polyacrylonitrile and polyaniline in the PAN/PANI in situ fibers. The results of mechanical strength tests indicated that the performance of the PAN/PANI mixture significantly improved the mechanical parameters of polyaniline, although these fibers had a weaker strength than the unmodified PAN fibers. The fibers obtained as a result of the addition of PANI to PAN were dielectric, whereas the PANI-synthesized in situ were characterized by a mass-specific resistance of 5.47 kΩg/cm².

The paper presents the results and analysis of interdisciplinary research concerning electromagnetic field shielding, conductive polymers printed on textiles and numerical simulation using the finite element method (FEM). The use of conductive, layered textiles for shielding electromagnetic interference (EMI) has been proposed. After establishing the optimal conditions for deposition of polyaniline (PANI) and polypyrrole (PPy) on polyacrylonitrile (PAN) fabric, conductive composites were made by means of reactive inkjet printing. For this purpose, polyacrylonitrile (PAN) fabrics were coated with polyaniline or polypyrrole, obtained by chemical oxidation of aniline hydrochloride and pyrrole by ammonium peroxydisulfate. The morphology of the obtained coatings was observed using a scanning electron microscope (SEM). The conductive properties (surface resistance) of the fabrics were measured using the four-wire method, and the tests of the effectiveness of electromagnetic shielding were carried out using the waveguide method in the frequency range from 2.5 to 18 GHz. The results of experimental shielding effectiveness (SE) tests and numerical simulation showed that the composites of polyacrylonitrile with polyaniline PAN/PANI and polyacrylonitrile with polypyrrole PAN/PPy achieved very good and good EMI shielding efficiency, respectively. Moreover, the obtained measurement results were verified by numerical modeling with the use of FEM–ANSYS HFFS software.

This paper presents a method for the preparation of nanocomposite cellulose fibers doped with silver nanoparticles (AgNPs), as well as the effect of silver nanoparticles on the structure and properties of fibers. The fibers were obtained by an environmentally friendly method using N-Methylmorpholine N-oxide (NMMO) as a solvent, in a non-polluting closed system. Doping with silver nanoparticles was carried out as a direct (in situ) reduction of Ag+ ions in the presence of a stabilizing agent during the preparation of the spinning solution. SEM images of the surface and cross section of the fibers showed that the distribution of nanoparticles in the fibers’ volume was uniform. The fibers exhibited very good antibacterial properties in relation to Staphylococcus aureus, Escherichia coli, Acinetobacter baumannii, and Candida albicans. Flammability analysis showed that the fibers were subjected to a one-stage combustion process and that the silver nanoparticles reduced the heat release rate (HRR) of the fibers by 36%. TG studies showed that the modification of cellulose fibers with silver nanoparticles promoted the formation of mill scale in the combustion of fibers, which was directly related to the reduction of flammability. Tests of the electrical properties showed that the linear resistance of cellulose fibers containing 3 wt % silver was 108 Ω/cm.