Alkali-activation (or geopolymer) technology has gained a great deal of interest for its potential applications in water and wastewater treatment during the last decade. Alkali-activated materials can be prepared via a relatively simple and low-energy process, most commonly by treating aluminosilicate precursors with concentrated alkali hydroxide and/or silicate solutions at (near) ambient conditions. The resulting materials are, in general, amorphous, have good physical and chemical stability, ion-exchange properties, and a porous structure. Several of the precursors are industrial by-products or other readily available low-cost materials, which further enhances the environmental and economic feasibility. The application areas of alkali-activated materials in water and wastewater treatment are adsorbents/ion-exchangers, photocatalysts, high-pressure membranes, filter media, anti-microbial materials, pH buffers, carrier media in bioreactors, and solidification/stabilization of water treatment residues. The purpose of this review is to present a comprehensive evaluation of the rapidly growing prospects of alkali-activation technology in water and wastewater treatment.

In this study, novel and cost-effective alkali-activated materials (AAMs) for catalytic applications were developed by using an industrial side stream, i.e., blast furnace slag (BFS). AAMs can be prepared from aluminosilicate precursors under mild conditions (room temperature using non-hazardous chemicals). AAMs were synthesized by mixing BFS and a 50 wt % sodium hydroxide (NaOH) solution at different BFS/NaOH ratios. The pastes were poured into molds, followed by consolidation at 20 or 60 °C. As the active metal, Fe was impregnated into the prepared AAMs by ion exchange. The prepared materials were examined as catalysts for the catalytic wet peroxide oxidation (CWPO) of a bisphenol A (BPA) aqueous solution. As-prepared AAMs exhibited a moderate surface area and mesoporous structure, and they exhibited moderate activity for the CWPO of BPA, while the iron ion-exchanged, BFS-based catalyst (Fe/BFS30-60) exhibited the maximum removal of BPA (50%) during 3 h of oxidation at pH 3.5 at 70 °C. Therefore, these new, inexpensive, AAM-based catalysts could be interesting alternatives for catalytic wastewater treatment applications.

The growing textile industry produces large volumes of hazardous wastewater containing dyes, which stresses the need for cheap, efficient adsorbing technologies. This study investigates a novel preprocessing method for producing activated carbons from abundantly available softwood bark. The preprocessing involved a continuous steam explosion preconditioning step, chemical activation with ZnCl₂, pyrolysis at 600 and 800 °C, and washing. The activated carbons were subsequently characterized by SEM, XPS, Raman and FTIR prior to evaluation for their effectiveness in adsorbing reactive orange 16 and two synthetic dyehouse effluents. Results showed that the steam-exploded carbon, pyrolyzed at 600 °C, obtained the highest BET specific surface area (1308 m²/g), the best Langmuir maximum adsorption of reactive orange 16 (218 mg g^-1) and synthetic dyehouse effluents (>70 % removal) of the tested carbons. Finally, steam explosion preconditioning could open up new and potentially more sustainable process routes for producing functionalized active carbons.