Background: Carbon dots (CDs) are of particular interest in numerous applications. However, their efficiency for heavy metal removal from wastewater was not yet reported. Herein, we rationally synthesized CDs from petroleum coke waste via hydrothermal treatment in the presence of ammonia. Results: This drove the formation of outstanding photoluminescent, water-soluble, biocompatible, and high yield of monodispersed sub-5 nm CDs. The CDs are co-doped with high 10% of N and 0.2% of S. The as-prepared CDs possess unprecedented photoluminescent properties over broad pH range making these dots unique efficient pH sensor. Conclusions: Chitosan (CH)–CDs hybrid hydrogel nanocomposite film was further prepared as a platform membrane for the removal Cd²⁺ metal from wastewater. The as-prepared CH–CDs membranes show relatively good mechanical properties, based on stress resistance and flexibility to facilitate handling. The equilibrium state was reached within 5 min. Intriguingly, the UV-light illuminations enhanced the Cd²⁺ removal efficiency of the photoluminescent CDs substantially by four times faster under. It was found that adsorption followed pseudo-second-order kinetic and Langmuir isotherm models. The maximum adsorption capacity at 25 °C was found to be 112.4 mg g⁻¹ at pH 8. This work paves the way to new applications of CDs in water treatment.

Epoxy polymer nanocomposites filled with magnetite (Fe₃O₄) clay (B), named (B-DPA-PANI@Fe₃O₄) have been prepared at different filler loading (0.1, 0.5, 1, 3, 5 wt. %). The surface modification of clay by polyaniline (PANI) is achieved in the presence of 4-diphenylamine diazonium salt (DPA). The effects of the nanofiller loading on Tensile, mechanical and dielectric properties were systematically studied. Improved properties was highlighted for all reinforced samples. The addition of only 3 wt. % of the filler enhanced the tensile strength of the composites by 256%, and the glass transition temperature Tg by 37%. The dielectric spectra over a broad frequency showed a robust interface between the hybrid (B-DPA-PANI@Fe₃O₄) fillers and epoxy matrix. The results showed most significant improvement in corrosion inhibition using electrochemical impedance spectroscopy (EIS) in 3.5 wt % NaCl, as well as a significant response in oil sensing test. High charge transfer resistance of 110 × 10⁶ Ω.cm² using 3-wt % of filler was noted compared to 0.35 × 10⁶ Ω.cm² for the pure epoxy. The results obtained herein will open new routes for the preparation of efficient anticorrosion sensor coatings.

Developing micro- and nanomaterials for environmental pollution remediation is currently a pertinent topic. Among the plethora of strategies, designing supported nanocatalysts for the degradation of pollutants has achieved prominence. In this context, we are addressing one of the UN Sustainable Development Goals by valorizing agrowaste as a source of biochar, which serves as a support for bimetallic nanocatalysts. Herein, olive pit powder particles were impregnated with copper and nickel nitrates and pyrolyzed at 400 °C. The resulting material consists of bimetallic CuNi-decorated biochar. CuNi nanocatalysts were found to be as small as 10 nm and very well dispersed over biochar with zero valent copper and nickel and the formation of copper–nickel solid solutions. The biochar@CuNi (B@CuNi) exhibited typical soft ferromagnet hysteresis loops with zero remanence and zero coercivity. The biochar@CuNi was found to be an efficient catalyst of the reduction in methyl orange (MO) dye, taken as a model pollutant. In sum, the one-pot method devised in this work provides unique CuNi-decorated biochar and broadens the horizons of the emerging topic of biochar-supported nanocatalysts.

Carbon dots and their derivatives with fascinating photoluminescence properties have recently attracted tremendous scientific attention. This work describes the preparation of novel fluorescent bentonite clay (B), modified with carbon dot nanomaterials (CDs), and its usage as a lead removal platform. The CDs were prepared using a hydrothermal method from graphitic waste which served as the carbon source material. The as-obtained CDs were found to be fluorescent, being spherical in shape, positively charged, and smaller than 5 nm. Encouraged by their structure and photoluminescence features, they were used as surface modifiers to make fluorescent bentonite nanocomposites. Bentonite was used as a negatively charged model of aluminosilicate and reacted with the positively charged CDs. XRD, FTIR, XPS, and fluorescence analysis were used to characterize the prepared materials. The results indicate that the CDs intercalated inside the bentonite matrix were stable with excellent optical properties over time. They were finally used as an efficient hybrid platform for lead removal with a removal efficiency of 95% under light conditions, at room temperature, in an alkaline medium, and after only 10 min of reaction, compared to 70% under dark conditions. The pseudo-second-order kinetics and Langmuir isotherm models were better fitted to describe the adsorption process. The maximum adsorption capacity was equal to 400 mg g⁻¹ toward Pb(II) removal, at room temperature and pH = 8, under light conditions. To summarize, we have designed UV light stimuli responsive carbon dot-intercalated clay with high Pb(II) adsorption capacity and long-term stability.