The polyamide (PA)-12 material used for additive manufacturing was studied in aspects of morphology and their structural properties for basic stages received during 3D laser printing. Samples were real, big-scale production powders. The structure of polymer was evaluated from the crystallinity point of view using XRD, FTIR, and DSC methods and from the surface properties using specific surface evaluation and porosity. Scanning electron microscopy was used to observe morphology of the surface and evaluate the particle size and shape via image analysis. Results were confronted with laser diffraction particles size measurement along with an evaluation of the specific surface area. Fresh PA12 powder was found as inhomogeneous in particle size of material with defective particles, relatively high specific surface, high lamellar crystallite size, and low crystallinity. The scrap PA12 crystallinity was about 2% higher than values for fresh PA12 powder. Particles had a very low, below 1 m²/g, specific surface area; particles sintered as twin particles and often in polyhedral shapes.

Infectious stomatitis represents the most common oral cavity ailments. Current therapy is insufficiently effective because of the short residence time of topical liquid or semisolid medical formulations. An innovative application form based on bioadhesive polymers featuring prolonged residence time on the oral mucosa may be a solution to this challenge. This formulation consists of a mucoadhesive oral film with incorporated nanocomposite biomaterial that is able to release the drug directly at the target area. This study describes the unique approach of preparing mucoadhesive oral films from carmellose with incorporating a nanotechnologically modified clay mineral intercalated with chlorhexidine. The multivariate data analysis was employed to evaluate the influence of the formulation and process variables on the properties of the medical preparation. This evaluation was complemented by testing the antimicrobial and antimycotic activity of prepared films with the aim of finding the most suitable composition for clinical application. Generally, the best results were obtained with sample containing 20 mg of chlorhexidine diacetate carried by vermiculite, with carmellose in the form of nonwoven textile in its structure. In addition to its promising physicomechanical, chemical, and mucoadhesive properties, the formulation inhibited the growth ofStaphylococcusandCandida; the effect was prolonged for tens of hours.

Infection with pathogenic microorganisms is of great concern in many areas, especially in healthcare, but also in food packaging and storage, or in water purification systems. Antimicrobial polymer nanocomposites have gained great popularity in these areas. Therefore, this study focused on new approaches to develop thin antimicrobial films based on biodegradable polycaprolactone (PCL) with clay mineral natural vermiculite as a carrier for antimicrobial compounds, where the active organic antimicrobial component is antifungal ciclopirox olamine (CPX). For possible synergistic effects, a sample in combination with the inorganic antimicrobial active ingredient zinc oxide was also prepared. The structures of all the prepared samples were studied by X-ray diffraction, FTIR analysis and, predominantly, by SEM. The very different structure properties of the prepared nanofillers had a fundamental influence on the final structural arrangement of thin PCL nanocomposite films as well as on their mechanical, thermal, and surface properties. As sample PCL/ZnOVER_CPX possessed the best results for antimicrobial activity against examined microbial strains, the synergic effect of CPX and ZnO combination on antimicrobial activity was proved, but on the other hand, its mechanical resistance was the lowest.