Due to the presence of cationic units interpolyelectrolyte complexes (IPECs) can be used as a universal basis for preparation of biocidal coatings on different surfaces. Metallopolymer nanocomposites were successfully synthesized in irradiated solutions of polyacrylic acid (PAA) and polyethylenimine (PEI), and dispersions of non-stoichiometric IPECs of PAA–PEI containing silver ions. The data from turbidimetric titration and dynamic light scattering showed that pH 6 is the optimal value for obtaining IPECs. Metal polymer complexes based on IPEC with a PAA/PEI ratio equal to 3/1 and 1/3 were selected for synthesis of nanocomposites due to their aggregative stability. Studies using methods of UV–VIS spectroscopy and TEM have demonstrated that the size and spatial organization of silver nanoparticles depend on the composition of polymer systems. The average sizes of nanoparticles are 5 nm and 20 nm for complexes with a molar ratio of PAA/PEI units equal to 3/1 and 1/3, respectively. The synthesized nanocomposites were applied to the glass surface and exhibited high antibacterial activity against both gram-positive (Staphylococcus aureus) and gram-negative bacteria (Salmonella). It is shown that IPEC-Ag coatings demonstrate significantly more pronounced biocidal activity not only in comparison with macromolecular complexes of PAA–PEI, but also coatings of PEI and PEI based nanocomposites.

In order to control pathogenic microorganisms, three polymer compositions were prepared and tested. First, a water-soluble positively charged polycomplex was synthesized via the electrostatic binding of anionic polyacrylic acid to an excess of polyethylenimine to enhance the biocidal activity of the polycation. Second, an aqueous solution of AgNO₃ was added to the polycomplex, thus forming a ternary polycation-polyanion-Ag¹⁺ complex with an additional antimicrobial effect. Third, the resulting ternary complex was subjected to UV irradiation, which ensured the conversion of Ag¹⁺ ions into Ag nanoparticles ranging in size mainly from 10 to 20 nm. Aqueous solutions of the polymer compositions were added to suspensions of the Gram-positive bacteria S. aureus and the Gram-negative bacteria P. aeruginosa, with the following main results: (a) Upon the addition of the binary polycomplex, 30% or more of the cells survived after 20 h. (b) The ternary complex killed S. aureus bacteria but was ineffective against P. aeruginosa bacteria. (c) When the ternary complex with Ag nanoparticles was added, the percentage of surviving cells of both types did not exceed 0.03%. The obtained results are valuable for the development of antibacterial formulations.