Post press processes include various types of bonding and adhesives, depending upon the nature of adherends, the end use performance requirements and the adhesive bonding processes. Polyvinyl acetate (PVAc) adhesive is a widely used adhesive in the graphic industry for paper, board, leather and cloth. In this study, the enhancement of PVAc adhesion performance by adding different concentrations (1%, 2% and 3%) of silica (SiO₂) and titanium dioxide (TiO₂) nanoparticles was investigated. The morphology of investigated paper-adhesive samples was analyzed by SEM microscopy and FTIR spectroscopy. In addition, the optimal adhesion at the interface of paper and adhesive was found according to calculated adhesion parameters by contact angle measurements (work of adhesion, surface free energy of interphase, wetting coefficient). According to obtained surface free energy (SFE) results, optimum nanoparticles concentration was 1%. The wettability of the paper-adhesive surface and low SFE of interphase turned out as a key for a good adhesion performance. The end use T-peel resistance test of adhesive joints confirmed enhancement of adhesion performance. The highest strength improvement was achieved with 1% of SiO₂ nanoparticles in PVAc adhesive.

In this study, the influence of physio-chemical properties of four printing substrates, fibrous papers (filter, bulky, recycled), and polymer film (synthetic paper) on the size of the thermochromic (TC) prints microcapsules was investigated. Results indicate that interaction between thermochromic ink and printing substrate determine the print morphology, i.e., porosity and roughness of printing substrate affect dimensions of TC microcapsules of resulting prints, while ink adhesion affects dimensional changes during heating–cooling cycle. Atomic force microscopy (AFM) analysis showed that microcapsules of the prints, on the surface of the smoothest synthetic paper, possess the smallest diameter and height, while, on the most porous and the most roughened surface of F paper, the microcapsules of the prints possess the highest diameter and height. By increasing the temperature to 40 °C, the biggest changes in the shape of the microcapsules (increase in height and decrease in diameter) were obtained using the surface of the hydrophilic filter paper. While using the recycled paper surface, the situation is opposite; the height and diameter of the microcapsules are reduced, and the microcapsules penetrate deeper into the paper structure (due to optimum adhesion). On the bulky paper surfaces, which are more hydrophobic than recycled paper (higher interfacial tension), the increase of temperature does not cause any significant changes in the shape and position of the microcapsules. The same behavior is observed using hydrophobic non-porous synthetic paper.

Thermochromic inks, also known as color changing inks, are becoming increasingly important for various applications that range from smart packaging, product labels, security printing, and anti-counterfeit inks to applications such as temperature-sensitive plastics and inks printed onto ceramic mugs, promotional items, and toys. These inks are also gaining more attention as part of textile decorations and can also be found in some artistic works obtained with thermochromic paints, due to their ability to change color when exposed to heat. Thermochromic inks, however, are known to be sensitive materials to the influence of UV radiation, heat fluctuations, and various chemical agents. Given the fact that prints can be found in different environmental conditions during their lifetime, in this work, thermochromic prints were exposed to the action of UV radiation and the influence of different chemical agents in order to simulate different environmental parameters. Hence, two thermochromic inks with different activation temperatures (one being cold and the other being body-heat activated), printed on two food packaging label papers that differ in their surface properties were chosen to be tested. Assessment of their resistance to specific chemical agents was performed according to the procedure described in the ISO 2836:2021 standard. Moreover, the prints were exposed to artificial aging to determine their durability when exposed to UV radiation. All tested thermochromic prints showed low resistance to liquid chemical agents as the color difference values were unacceptable in all cases. It was observed that the stability of thermochromic prints to different chemicals decreases with decreasing solvent polarity. Based on the results obtained after UV radiation, its influence in terms of color degradation is visible on both tested paper substrates, but more significant degradation was observed on the ultra-smooth label paper.

Thermochromic (TC) printing inks change their colouration as a response to a change in temperature. This ability renders them attractive for various applications such as smart packaging, security printing, and marketing, but their application is limited due to their low UV stability, i.e., loss of their thermochromic effect when exposed to UV radiation. In order to improve the UV stability of TC prints, one offset TC printing ink was printed and coated with nanomodified polycaprolactone (PCL) coating. The coating was prepared with the incorporation of 1%, 2%, and 3% mass ratios of ZnO and TiO₂ nanoparticles in the PCL matrix. The prepared nanocomposite coatings were applied onto the TC print and exposed to UV radiation; afterwards, they were characterized by the colour properties of prints, SEM microscopy, FTIR, and fluorescence spectroscopy. SEM microscopy, FTIR, and fluorescence spectroscopy showed higher rates of polymer degradation, and the results of colour stability indicated that 3% TiO₂ in PCL matrix gave the best UV stability and protection of TC prints.

To support circular economy and sustainability, the use of synthetic polymers should be minimized due to their excessive accumulation in the environment and low biodegradation rate which leads to a global waste problem. Thus, the quota of natural resources should be increased, as well as the use of agriculture and industrial waste or by-products as raw materials in industrial processes. Agro-industrial wastes were found to have high cellulose fiber potential which makes them an excellent resource for paper production. This study investigates the influence of artificial aging test on the stability of commercially available fiber based self-adhesive pressure sensitive labels (PSL), in which the facestock is made of 15% agro-industrial byproducts, 40% post-consumer recycled paper and 45% virgin wood pulp and compared to ones made of biobased polyethylene. The results showed that optical brighteners are present in the composition of fiber based PSL. Moreover, the fluorescence and UV-Visible spectroscopy results indicated that by the action of UV irradiation and temperature. The oxidation of cellulose was not found by FTIR spectroscopy, indicating its high stability.