Thermochromic (TC) printing inks change their colouration as a response to a change in temperature. This ability renders them attractive for various applications such as smart packaging, security printing, and marketing, but their application is limited due to their low UV stability, i.e., loss of their thermochromic effect when exposed to UV radiation. In order to improve the UV stability of TC prints, one offset TC printing ink was printed and coated with nanomodified polycaprolactone (PCL) coating. The coating was prepared with the incorporation of 1%, 2%, and 3% mass ratios of ZnO and TiO₂ nanoparticles in the PCL matrix. The prepared nanocomposite coatings were applied onto the TC print and exposed to UV radiation; afterwards, they were characterized by the colour properties of prints, SEM microscopy, FTIR, and fluorescence spectroscopy. SEM microscopy, FTIR, and fluorescence spectroscopy showed higher rates of polymer degradation, and the results of colour stability indicated that 3% TiO₂ in PCL matrix gave the best UV stability and protection of TC prints.

To support circular economy and sustainability, the use of synthetic polymers should be minimized due to their excessive accumulation in the environment and low biodegradation rate which leads to a global waste problem. Thus, the quota of natural resources should be increased, as well as the use of agriculture and industrial waste or by-products as raw materials in industrial processes. Agro-industrial wastes were found to have high cellulose fiber potential which makes them an excellent resource for paper production. This study investigates the influence of artificial aging test on the stability of commercially available fiber based self-adhesive pressure sensitive labels (PSL), in which the facestock is made of 15% agro-industrial byproducts, 40% post-consumer recycled paper and 45% virgin wood pulp and compared to ones made of biobased polyethylene. The results showed that optical brighteners are present in the composition of fiber based PSL. Moreover, the fluorescence and UV-Visible spectroscopy results indicated that by the action of UV irradiation and temperature. The oxidation of cellulose was not found by FTIR spectroscopy, indicating its high stability.

The importance of accurate identification of the edge spread function for the paper-ink system is closely related with the possibility of separating mechanical and optical dot gain. Our approach is based on the precise fit of the edge spread function, ESF. Namely, all of the research so far incorporates symmetric ESF, in contrast to the research reported so far, in which only the symmetric ESF has been considered¸ which is not realistic, due to the presence of dot gain. This approach, based on image analysis, allows us to identify uniquely the domain of impact of each contribution. Six different paper-ink systems are analyzed and discussed, and all of them show a satisfactory correlation with the proposed model.

The ultimate goal of each production process is to optimize all the subprocesses leading to the high quality final product. Within the printing process, dot gain is identified as one of the most important variables to control because of the extremely negative impact to middle tone contrast and the overall reproduction. Dot gain consists of two components, mechanical and optical dot gain, as a result of two different contributions. This article proposes a model for separately analyzing components of dot gain for electrophotography prints using gradient method, where the impact of printing technique and paper type will be examined. It is shown that mechanical dot gain for electrophotography prints can be satisfactorily approximated with Gaussian, whilst optical dot gain is once again confirmed to have the form of a Lorentzian.

Fused deposition modeling (FDM) is widely employed in prototyping due to its cost-effectiveness, speed, and ability to produce detailed and functional prototypes using a variety of materials. Simultaneously, consideration for the use of biodegradable polymers and a general reduction in their usage while enhancing the production of polymer-based products is at the forefront of sustainable practices and environmental consciousness. This study investigates the impact fracture resistance of FDM models fabricated from Polylactic Acid (PLA), examining the influence of infill density (50% and 100% infill) and sample thickness (2 mm, 3 mm, and 5 mm). Optical microscopy, FTIR spectroscopy, and SEM analysis of PLA filament and fractured FDM PLA surfaces in impacted samples were conducted to ascertain the influence of process parameters on impact damage and failure mechanisms. The results indicate that a 100% infill profile with a 2 mm thickness should be avoided due to unpredictable behavior under impact. Conversely, a 5 mm thickness demonstrates significantly higher durability in comparison to a 50% infill profile. Optimal impact strength is observed in samples with a 3 mm thickness, suggesting potential material savings with 50% infill without compromising mechanical properties. The findings contribute valuable insights for refining FDM parameters and advancing the understanding of material behaviors in sustainable manufacturing practices.

Thermochromic inks (TC) have received increasing attention in recent years, particularly in the design and packaging industries. Their stability and durability are crucial for their application. This study highlights the detrimental effects of UV radiation on the lightfastness and reversibility of thermochromic prints. Three commercially available TC inks with different activation temperatures and in different shades were printed on two different substrates, cellulose and polypropylene-based paper. Used inks were vegetable oil-based, mineral oil-based and UV-curable. The degradation of the TC prints was monitored using FTIR and fluorescence spectroscopy. Colorimetric properties were measured before and after exposure to UV radiation. The substrate with a phorus structure exhibited better colour stability, suggesting that the chemical composition and surface properties of the substrate play a crucial role in the overall stability of thermochromic prints. This can be explained by the ink penetration into the printing substrate. The penetration of the ink into the structure (cellulose fibres) protects the ink pigments from the negative effect of the UV radiation. Obtained results suggest that although the initial substrate may appear suitable for printing, its performance after ageing may not be optimal. In addition, the UV curable prints show better light stability than those made of mineral- and vegetable-based inks. In the field of printing technology, understanding the interplay between different printing substrates and inks is critical to achieve high-quality, long-lasting prints.