The aim of this research was to develop advanced lipid nanocarriers based on renewable vegetable resources (rice bran oil and raspberry seed oil) that possess self-antioxidative properties, having advantages in terms of minimal side effects and exhibiting the ability to simultaneously co-encapsulate and co-release two active compounds. The focus has been oriented towards developing safe cosmetic formulations with broad-spectrum photoprotection based on these new lipid nanocarriers that contain large amounts of vegetable oils and low concentrations of synthetic UVA and UVB filters (butyl-methoxydibenzoylmethane – BMDBM and octocrylene – OCT). The lipid nanocarriers have a spherical shape and show good physical stability, with a zeta potential in the range of −25.5 to −32.4 mV. Both vegetable oils play a key role in the preparation of efficient nanocarriers, leading to a less ordered arrangement of the lipid core that offers many spaces for the entrapment of large amounts of BMDBM (79%) and OCT (90%), as wells as improved antioxidant activity and UV absorption properties, particularly for the lipid nanocarriers prepared from rice bran oil. By formulating the lipid nanocarriers into creams containing only 3.5% of the UV filters and 10.5% of the vegetable oils, the resulting sunscreens exhibited improved photoprotection, reflecting up to 91% and 93% of UVA and UVB rays, respectively. A new direction of research achieved by this study is the multiple release strategy of both UV filters from the same lipid nanocarrier. After 24 hours, a slow release of BMDBM (less than 4%) and OCT (17.5%) was obtained through a Fick diffusion process. This study demonstrates a significant advance in the areas of both nanotechnology and cosmetics, developing safer cosmetic formulations that possess broad antioxidant, photoprotective and co-release effectiveness due to the existence of a high content of nanostructured vegetable oils combined with a low amount of synthetic UV filters in the same carrier system.

The objective of this investigation was to develop solid lipid nanoparticles (SLNs) of umbelliferone by means of a high shear homogenization technique and to evaluate the efficiency of SLN systems in preserving and enhancing antioxidant activity of the flavonoid active component. The aqueous SLN dispersions combine two structural types of lipid compounds and different types of emulsifiers including a mixture of monoalkyl polyoxyethylene sorbitan with a block copolymer and lecithin. The assessment of umbelliferone stability in aqueous SLN dispersions, the size distribution of lipid nanoparticles loaded with umbelliferone (by DLS technique), as well as the structural changes (FT-IR spectroscopy and differential scanning calorimetry) of these lipid nanomatrices have been investigated. Moreover, the influence of umbelliferone concentration onto entrapment efficiency and antioxidant properties were clearly evidenced on four kinds of lipid nanoparticles. The umbelliferone-loaded SLN prepared with polyethylene glycol sorbitan monostearate shown a mean particle size of 173.4 nm ± 3.279, as well as good entrapment efficiency (EE = 60.70%) and antioxidant properties (AA = 75%).

The efficiency of a cosmetic product depends not only on the active ingredients, but also on the carrier system devoted to improve its bioavailability. This article aims to encapsulate two couples of UV molecular absorbers, with a blocking action on both UV-A and UV-B domains, into efficient lipid nanoparticles. The effect of encapsulation on the specific properties such as sun protection factor and photostability behaviour has been demonstrated. The lipid nanoparticles with size range 30-350 nm and a polydispersity index between 0.217 and 0.244 are obtained using a modified high shear homogenisation method. The nanoparticles had spherical shapes with a single crystallisation form of lipid matrices characteristic for the least ordered crystal structure (α-form). The in vitro determination of photoprotection has led to high SPF ratings, with values of about 20, which assure a good photoprotection and filtering about 95% of UV radiation. The photoprotection effect after irradiation stage was observed to be increased more than twice compared to initial samples as a result of isomerisation phenomena. All the results have shown that good photoprotection effect and improved photostability could be obtained using such sunscreen couples, thus demonstrating that UV absorbers-solid lipid nanoparticles are promising carriers for cosmetic formulations.

The aim of this investigation was to obtain lipid nanoparticles loaded with different sunscreen agents in order to achieve enhanced photoprotection and to decrease the amount of UV – absorbers, with preserving at the same time a high sun protection factor. The developed formulations combined different types of additives including a mixture of non-ionic surfactant and lechitine with two lipids as solid matrix to obtain favourable stable lipid formulations. The research work could be concluded as successefully production of lipid nanoparticles loaded with UV-A and UV-B absorbers (with average size less than 100 nm) that may represent useful UV-blocking systems in sunscreen products for cosmetical purpose.

Novel cross-linked hydrogels were synthesized as potential materials for the development of smart biofertilizers. For this purpose, hydrogels were prepared using collagen hydrolysate recovered from tannery waste. The water-soluble polymer poly(sodium 4-styrenesulfonate-co-glycidyl methacrylate) (P(SSNa-co-GMAx)) was among others used for the cross-linking reaction that combined hydrophilic nature with epoxide groups. The synthetic procedure was thoroughly investigated in order to ensure high percentage of epoxide groups in combination with water-soluble behavior. The copolymer did not show cytotoxicity against normal lung, skin fibroblasts, or nasal polyps fibroblasts. Through the present work, we also present the ability to control the properties of cross-linked hydrogels by altering copolymer’s composition and cross-linking parameters (curing temperature and time). Hydrogels were then studied in terms of water-uptake capacity for a period up to six days. The techniques Proton Nuclear Magnetic Resonance (¹H NMR), Thermogravimetric Analysis (TGA), Size Exclusion Chromatography (SEC), and Attenuated Total Reflection Fourier Transform Infrared Spectroscopy (ATR-FTIR) were applied for the characterization of the synthesized copolymers and the cross-linked hydrogels. Three samples of biofertilizers based on collagen hydrolysate functionalized with P(SSNa-co-GMAx) and starch and having nutrients encapsulated (N, P, K) were prepared and characterized by physical–chemical analysis and Energy Dispersive X-ray analysis-Scanning Electron Microscope (EDAX-SEM) in terms of microstructure. Preliminary tests for application as fertilizers were performed including the release degree of oxidable organic compounds.