A novel pectin was acid extracted from chickpea husk (CHP). CHP presented a 67% (w/w) of galacturonic acid, an intrinsic viscosity of 374 mL/g and a viscosimetric molecular weight of 110 kDa. Fourier transform infrared spectroscopy spectrum of CHP indicated a degree of esterification of about 10%. The CHP-calcium system formed ionic gels with a storage (G’) modulus of 40 Pa and gel set time (G’ > G’’) of 3 min at 1% (w/v), and a G’ of 131 Pa and gel set time of 1 min at 2% (w/v). The G’ of CHP gels was not greatly affected by temperature. The results attained suggest that chickpea husk can be a potential source of a gelling pectin material.

Homogeneous and thin porous membranes composed of oriented fibers were obtained from wheat gluten (WG) using the electrospinning technique. SEM micrographs showed an asymmetric structure and some porosity, which, in addition to a small thickness of 40 mm, are desirable characteristics for the membranes’ potential application in release systems. The membranes were loaded with urea to obtain pastilles. FT-IR and DSC studies confirmed the existence of interactions via hydrogen bonding between urea and WG proteins. The pastilles were studied as prolonged-released systems of urea in water. The release of urea during the first 10 min was very fast; then, the rate of release decreased as it reached equilibrium at 300 min, with a total of »98% urea released. TGA analysis showed that the release system obtained is thermally stable up to a temperature of 117 °C. It was concluded that a prolonged-release system of urea could be satisfactorily produced using WG fibers obtained by electrospinning for potential application in agricultural crops.