Edible coatings are important for horticulture crops preservation and reducing food waste. Application of edible coatings followed by low-temperature storage prolongs the storability, preserves quality, and decreases the overall postharvest losses. This study evaluated the efficacy of two nanoemulsions formulae containing thyme essential oil and whey proteins as coatings for zucchini, with the purpose of extending their shelf-life. The nanoemulsions were rheologically evaluated and the formula with guar and arabic gum mix stabilizer (S) showed a better capacity to restructure after strain compared to the formulae with Tween 20 (T). The S coating material had a better capacity to integrate nanoparticles compared to T. However, when applied on zucchini, T coating was more effective in reducing weight loss showing 16% weight loss compared to 21% in S, after 42 days. At the end of storage at 10 °C, the T-coated zucchini had better firmness (p < 0.05) compared with S and both coatings were superior to control (p < 0.05). POD (peroxidase) activity was high in peel at the end of storage when also CAT (catalase) showed a sudden increase. On the 42nd day of storage, the highest enzymes activity (CAT, POD, and APX (ascorbate peroxidase)) was present in the S-coated zucchini peel. The most abundant volatile in T coating was α-pinene and 4-carene in S. Sensory analysis showed that T coating delayed the appearance of senescence while S exhibited surface cracks.

Whey edible films (EFs) functionalized with essential oils have a high potential to be used on various foods due to their antimicrobial and antioxidant activities. Encapsulation is applied for a better retention of volatiles in EFs; however, the functional properties of EFs are modified. The properties of EFs containing thyme essential oil (TEO) encapsulated by co-precipitation in β-CD, developed in three formulae, with inclusion complexes (EF/IC1, EF/IC2, and EF/IC3, respectively) in 15:85, 26:74, and 35:65 mass ratios were studied. Thymol is the main volatile in the ICs with TEO/β-CD (50%–60% of the total volatiles). In comparison with EF/TEO, all three formulae with EF/ICs had better, but similar, WVPs (p > 0.05). The EF/IC2 displayed a different FTIR profile than EF/IC1 and EF/IC3, suggesting a smaller number of free functional groups. The EF/IC2 showed better transparency in comparison with EF/IC1 and EF/IC3. All EF/ICs moderately inhibited R. glutinis, with the strongest activity registered by EF/IC3 (p < 0.05), but did not inhibit G. candidum, while showing a strong antibacterial activity against B. cereus. All EF/ICs inhibited 65%–70% of the total free radicals. The EF/ICs ensured a gradual release of VOCs in food simulants, with a higher rate in 95% ethanol than in water. These results have demonstrated the properties of EF/ICs with TEO/β-CD as bioactive packaging systems for foods.

Application of high pressure-thermal treatment (600 MPa and 70 °C, 20 min) for obtaining edible films functionalized with thyme extracts have been studied in order to evaluate the antimicrobial capacity of films structure to retain and release the bioactive compounds. The high pressure-thermally treated films (HPT) were compared with the thermally treated (TT) ones (80 ± 0.5 °C, 35 min). The film structures were analyzed and the sorption isotherms, water vapor permeability, antimicrobial activity and the volatile fingerprints by GC/MS were performed. The HPT film presented more binding sites for water chemi-sorption than TT films and displayed significantly lower WVP than TT films (p < 0.05). TT films displayed slightly, but significant higher, antimicrobial activity (p < 0.05) against Geotrichum candidum in the first day and against Bacillus subtilis in the 10th day of storage. The HPT film structure had ~1.5-fold higher capacity to retain volatiles after drying compared to TT films. From the HPT films higher amount of p-cymene and α-terpinene was volatilized during 10 days of storage at 25 °C, 50% RH while from the TT films higher amount of caryophyllene and carvacrol were released. During storage HPT films had a 2-fold lower capacity to retain monoterpenes compared to TT films.