This research aimed to study the influence of lyocell with incorporated ZnO (CLY) for antibacterial activity and biodegradation of fiber blends composed of viscose (CV), flax (LI), and CLY. Fiber blended samples with an increased weight fraction of CLY fibers were composed, and single CLY, CV and LI fibers were also used for comparison. Antibacterial activity was determined for the Gram-negative Escherichia coli and the Gram-positive Staphylococcus aureus bacteria. The biodegradation of fiber blends was investigated by the soil burial test. The results show that the single CLY fibers exhibited high antimicrobial activity against both E. coli and S. aureus bacteria and that the presence of LI fibers in the blended samples did not significantly affect antibacterial activity against E. coli, but drastically decreased the antibacterial activity against S. aureus. LI fibers strongly promoted the growth of S. aureus and, consequently, impaired the antimicrobial performance of ZnO against this bacterium. The presence of CLY fibers slowed down, but did not prevent, the biodegradation process of the fiber blends, even at the highest ZnO concentration. The soil that was in contact with the fiber blended samples during their burial was not contaminated to such an extent as to affect the growth of sprouts, confirming the sustainability of the fiber blends.

Microcapsules with fragrance in the core were used to produce a scented textile. The wall of microcapsules was based on a melamine-formaldehyde polymer while an essential oil was in the core. They were applied to cotton fabric using screen printing in two ways: over the entire surface and by pattern. The properties of the differently printed samples were analyzed. The fragrance evaluation was performed, mechanical properties were studied, antibacterial activity against Staphylococcus aureus and Escherihia coli was evaluated, and resistance of the samples to soil microorganisms was determined. The amount of formaldehyde on the samples was measured. The results showed that all samples kept the fragrance even after 10 washes. The mechanical properties of the fully printed fabric were different from the properties of the patterned fabric. None of the prints of scented microcapsules provided antibacterial activity. All samples were biodegradable. Less formaldehyde was measured on patterned samples than on fully printed samples. The amount decreased after washing.

Microcapsules with a pressure-sensitive melamine-formaldehyde wall and triclosan core were printed to 100% cotton fabric with screen printing technique. Previous research showed excellent antibacterial activity (estimated for E. Coli and S. Aureus) of such fabric, so our aim in this research was to determine its resistance to the action of microorganisms present in the soil. The soil burial test was conducted. The breaking strength of the buried samples was measured and also the scanning electron microscope analysis was done. The results showed that none of the samples are resistant to decay. It is evident from SEM micrographs that on all of the buried samples greater morphological changes occur due to the functions of the soil microflora. It can be concluded that the samples printed with triclosan microcapsules are biodegradable which is environmentally preferable.

This study presents the development of hydrophobic coatings for textile applications using natural biopolymers. Natural polysaccharides and waxes in the form of microcapsules were incorporated into a polysaccharide matrix to produce a microcapsule-based coating. Several coating formulations were prepared, incorporating varying concentrations of microcapsules and crosslinking agent (including versions without crosslinker) and subsequently applied to cotton and polyester fabrics using the rod-coating process. The coated fabrics were analyzed in order to evaluate the improvement in hydrophobicity and possible changes in physical properties, while the initial washing stability of the coating was analyzed by determining resistance to one domestic washing cycle. The coating increased the water contact angle from a highly hydrophilic to hydrophobic state (above 120°). After washing, the samples largely retained their hydrophobic properties, with some of them still exceeding a water contact angle (WCA) of 120°. The findings indicate that natural biopolymer microcapsule-based coatings, even without crosslinker, can effectively impart stable hydrophobic properties to textiles, thereby offering a safer alternative to conventional coatings containing per- and polyfluoroalkyl substances (PFAS).