Technological developments in construction have led to an increase in the use of 3D modelling using CAD environments. The popularity of this approach has increased in tandem with developments in industry branches which use 3D printers to print concrete based printing materials in construction, as these allow freedom in shaping the dimensions of supporting elements. One of the biggest challenges for researchers working on this highly innovative technology is that of cement material shrinkage. This article presents the findings of research on an original method of measuring deformations caused by shrinkage in 3D-printed concrete elements. It also discusses the results of tests on base mixes, as well as comparisons between the influence of internal and external curing methods on the development of deformations and their final outcomes. Furthermore, the article discusses differences between deformations formed after seven days of hardening without curing, with those which occur when two common, traditional concrete curing methods are used: foil insulation and shrinkage reducing admixtures. In addition, the article examines the effects of internal curing on the 1, 7, 14, 21 and 28 day mechanical properties of concrete, in accordance with EN 196-1 and EN 12390-2. Studies have shown that the optimal amount of shrinkage reducing admixtures is 4% (in relation to the mass of cement), resulting in a reduction in total shrinkage of 23%. The use of a shrinkage reducing admixture in 3D-printed concrete does not affect their strength after 28 days, but slows the strength development during the first 7 days.

Developments in the automation of construction processes, observable in recent years, is focused on speeding up the construction of buildings and structures. Additive manufacturing using concrete mixes are among the most promising technologies in this respect. 3D concrete printing allows the building up of structure by extruding a mix layer by layer. However, the mix initially has low capacity to transfer loads, which can be particularly troublesome in cases of external components that need to be placed on top such as precast lintels or floor beams. This article describes the application of additive manufacturing technology in the fabrication of a building wall model, in which the door opening was finished with automatic lintel installation. The research adjusts the wall design and printing process, accounting for the rheological and mechanical properties of the fresh concrete, as well as design requirements of Eurocode. The article demonstrates that the process can be planned precisely and how the growth of stress in fresh concrete can be simulated, against the strength level developed. The conclusions drawn from this research will be of use in designing larger civil structures. Furthermore, the adverse effects of concrete shrinkage on structures is also presented, together with appropriate methods of control.

The influence of four naturally occurring mineral additives (zeolite, diatomite, trass and bentonite) on the hydration and properties of cement pastes and mortars was investigated. The materials change the phase composition, heat of hydration (determined by calorimetry) and mechanical properties of composites. After 28 days, the amount of Ca(OH)₂ was reduced by up to 23% and up to 35% more C-S-H was formed, as proved by TG measurements. Differences were observed in the kinetics of heat release, especially for 25% of the addition. In the calorimetric curves, an additional exothermic effect is observed, related to the alteration in the hydration of C₃A in cement. From the point of view of beneficial influence on mechanical properties of mortars, the additives could be ranked as follows: bentonite < diatomite, zeolite < trass after 2 days and bentonite < diatomite < trass < zeolite after 28 days of curing. The highest compressive strength (58.5 MPa) was observed for the sample with a 10% addition of zeolite. Zeolite, trass, bentonite and diatomite are all pozzolanic materials; however, their activity varies to an extent due to the differences in their specific surface area and the content of the amorphous phase, responsible for the pozzolanic reaction.

Foundation piles that are made by concrete 3D printers constitute a new alternative way of founding buildings constructed using incremental technology. We are currently observing very rapid development of incremental technology for the construction industry. The systems that are used for 3D printing with the application of construction materials make it possible to form permanent formwork for strip foundations, construct load-bearing walls and partition walls, and prefabricate elements, such as stairs, lintels, and ceilings. 3D printing systems do not offer soil reinforcement by making piles. The paper presents the possibility of making concrete foundation piles in laboratory conditions using a concrete 3D printer. The paper shows the tools and procedure for pile pumping. An experiment for measuring pile bearing capacity is described and an example of a pile deployment model under a foundation is described. The results of the tests and analytical calculations have shown that the displacement piles demonstrate less settlement when compared to the analysed shallow foundation. The authors indicate that it is possible to replace the shallow foundation with a series of piles combined with a printed wall without locally widening it. This type of foundation can be used for the foundation of low-rise buildings, such as detached houses. Estimated calculations have shown that the possibility of making foundation piles by a 3D printer will reduce the cost of making foundations by shortening the time of execution of works and reducing the consumption of construction materials.