The metabolites of the fungal strain Rhizopus oryaze were used as a biocatalyst for the green-synthesis of magnesium oxide nanoparticles (MgO-NPs). The production methodology was optimized to attain the maximum productivity as follows: 4 mM of precursor, at pH 8, incubation temperature of 35 °C, and reaction time of 36 h between metabolites and precursor. The as-formed MgO-NPs were characterized by UV-Vis spectroscopy, TEM, SEM-EDX, XRD, DLS, FT-IR, and XPS analyses. These analytical techniques proved to gain crystalline, homogenous, and well-dispersed spherical MgO-NPs with an average size of 20.38 ± 9.9 nm. The potentiality of MgO-NPs was dose- and time-dependent. The biogenic MgO-NPs was found to be a promising antimicrobial agent against the pathogens including Staphylococcus aureus, Bacillus subtilis, Pseudomonas aeruginosa, Escherichia coli, and Candida albicans with inhibition zones of 10.6 ± 0.4, 11.5 ± 0.5, 13.7 ± 0.5, 14.3 ± 0.7, and 14.7 ± 0.6 mm, respectively, at 200 μg mL^–1. Moreover, MgO-NPs manifested larvicidal and adult repellence activity against Culex pipiens at very low concentrations. The highest decolorization percentages of tanning effluents were 95.6 ± 1.6% at 100 µg/ 100 mL after 180 min. At this condition, the physicochemical parameters of tannery effluents, including TSS, TDS, BOD, COD, and conductivity were reduced with percentages of 97.9%, 98.2%, 87.8%, 95.9%, and 97.3%, respectively. Moreover, the chromium ion was adsorbed with percentages of 98.2% at optimum experimental conditions.

The peel aqueous extract of Punica granatum was utilized to fabricate zinc oxide nanoparticles (ZnO-NPs) as a green approach. The synthesized NPs were characterized by UV-Vis spectroscopy, Fourier transform infrared (FT-IR), X-ray diffraction (XRD), transmission electron microscopy (TEM), and scanning electron microscopy, which was attached to an energy dispersive X-ray (SEM-EDX). Spherical, well arranged, and crystallographic structures of ZnO-NPs were formed with sizes of 10–45 nm. The biological activities of ZnO-NPs, including antimicrobial and catalytic activity for methylene blue dye, were assessed. Data analysis showed that the antimicrobial activity against pathogenic Gram-positive and Gram-negative bacteria, as well as unicellular fungi, was observed to occur in a dose-dependent manner, displaying varied inhibition zones and low minimum inhibitory concentration (MIC) values in the ranges of 6.25–12.5 µg mL^–1. The degradation efficacy of methylene blue (MB) using ZnO-NPs is dependent on nano-catalyst concentration, contact time, and incubation condition (UV-light emission). The maximum MB degradation percentages of 93.4 ± 0.2% was attained at 20 µg mL⁻¹ after 210 min in presence of UV-light. Data analysis showed that there is no significant difference between the degradation percentages after 210, 1440, and 1800 min. Moreover, the nano-catalyst showed high stability and efficacy to degrade MB for five cycles with decreasing values of 4%. Overall, P. granatum-based ZnO-NPs are promising tools to inhibit the growth of pathogenic microbes and degradation of MB in the presence of UV-light emission.

Herein, the aqueous extract of Portulaca oleracea has been used as a safe, cheap, eco-friendly, and applicable scale-up method to bio-fabricate copper oxide nanoparticles (CuO-NPs). The character of CuO-NPs were determined using UV-vis spectroscopy, Fourier transform infrared (FT-IR), X-ray diffraction (XRD), Transmission electron microscopy (TEM), Energy dispersive X-ray(EDX), Dynamic light scattering (DLS), and zeta potential. Spherical and crystalline CuO-NPs with a size range of 5–30 nm at a maximum surface plasmon resonance of 275 nm were successfully fabricated. The main components of the green-synthesized particles were Cu and O with weight percentages of 49.92 and 28.45%, respectively. A Zeta-potential value of −24.6 mV was recorded for CuO-NPs, indicating their high stability. The plant-based CuO-NPs showed promising antimicrobial and catalytic activity in a dose-dependent manner. Results showed that the synthesized CuO-NPs had the efficacy to inhibit the growth of pathogens Staphylococcus aureus, Bacillus subtilis, Escherichia coli, Pseudomonas aeruginosa, and Candida albicans with low MIC values in the ranges of 6.25–25 µg/mL. The highest decolorization percentages of tanning wastewater were attained under sunlight irradiation conditions at a concentration of 2.0 mg/mL after 200 min with percentages of 88.6 ± 1.5% compared to those which were recorded under dark conditions (70.3 ± 1.2%). The physicochemical parameters of tanning wastewater including total suspended solids (TSS), total dissolved solids (TDS), chemical oxygen demand (COD), biological oxygen demand (BOD), and conductivity under optimum conditions were significantly decreased with percentages of 95.2, 86.7, 91.4, 87.2, and 97.2%, respectively. Interestingly, the heavy metals including cobalt (Co), lead (Pb), nickel (Ni), cadmium (Cd), and chromium (Cr (VI)) decreased with percentages of 73.2, 80.8, 72.4, 64.4, and 91.4%, respectively, after treatment of tanning wastewater with CuO-NPs under optimum conditions. Overall, the plant-synthesized CuO-NPs that have antimicrobial and catalytic activities are considered a promising nano-catalyst and environmentally beneficial to wastewater treatment.