In this study, the possibility of using sawdust, a by-product of primary wood processing, as a filler (WF) for rigid polyurethane (PUR) foams was investigated. The effects of the addition of 5, 10, 15 and 20% of WF particles to the polyurethane matrix on the foaming process, cell structure and selected physical-mechanical properties such as density, thermal conductivity, dimensional stability, water absorption, brittleness, compressive and bending strengths were evaluated. Based on the results, it was found that the addition of WF in the amount of up to 10% does not significantly affect the kinetics of the foam foaming process, allowing the reduction of their thermal conductivity, significantly reducing brittleness and maintaining high dimensional stability. On the other hand, such an amount of WF causes a slight decrease in the compressive strength of the foam, a decrease in its bending strength and an increase in water absorption. However, it is important that in spite of the observed decrease in the values of these parameters, the obtained results are satisfactory and consistent with the parameters of insulation materials based on rigid PUR foam, currently available on the market.

A significant part of the work carried out so far in the field of production of biocomposite polyurethane foams (PUR) with the use of various types of lignocellulosic fillers mainly concerns rigid PUR foams with a closed-cell structure. In this work, the possibility of using waste wood particles (WP) from primary wood processing as a filler for PUR foams with open-cell structure was investigated. For this purpose, a wood particle fraction of 0.315–1.25 mm was added to the foam in concentrations of 0, 5, 10, 15 and 20%. The foaming course of the modified PUR foams (PUR-WP) was characterized on the basis of the duration of the process’ successive stages at the maximum foaming temperature. In order to explain the observed phenomena, a cellular structure was characterized using microscopic analysis such as SEM and light microscope. Computed tomography was also applied to determine the distribution of wood particles in PUR-WP materials. It was observed that the addition of WP to the open-cell PUR foam influences the kinetics of the foaming process of the PUR-WP composition and their morphology, density, compressive strength and thermal properties. The performed tests showed that the addition of WP at an the amount of 10% leads to the increase in the PUR foam’s compressive strength by 30% (parallel to foam’s growth direction) and reduce the thermal conductivity coefficient by 10%.

The paper evaluated the possibility of manufacturing wood-based boards from the material left over from sawmill processing of wood. The boards were made from chips created during cant preparation for cutting and sawdust generated during further sawnwood preparation. They were made as one- and three-ply boards with face layers containing industrial microchips. Mechanical properties determined for one-ply boards in a bend test were used as guidelines for manufacturing three-ply boards. The outcomes were much better when the core layer comprised a mix of chips and sawdust than the chips alone. The study also showed that for the assumed technological parameters it is possible to produce three-ply boards with properties meeting the criteria for P2 furniture boards.

This research evaluated the possibility of using sawmill by-products from the roundwood-processing line in the production of wood-based panels. Due to its number of favorable properties, interesting chemical composition and large reserves resulting from the lack of industrial applications, the research focused particularly on the use of bark. Manufactured variants of boards differed in the proportions of wood chips to bark (70:30, 60:40, 50:50). Moreover, the boards containing only wood chips and a mixture of chips and sawdust were used as references. Urea-formaldehyde adhesive mixed with ammonium nitrate as a hardener was applied as a binding agent for the boards. Based on the mechanical properties (modulus of elasticity, modulus of rupture, internal bonding), physical properties (density, thickness swelling, water absorption) and content and emission of formaldehyde, it was found that it is possible to produce boards characterized by good properties from sawmill by-products without advanced processing. Moreover, the use of bark instead of sawdust in order to increase the homogeneity of the cross-section allows one to obtain panels with significantly lower formaldehyde emission and water uptake.

In this study, the possibility of using adhesives of natural origin for the manufacture of wood fiber-based lightweight panels was investigated. The boards, of a density ranging from 150 to 250 kg/m³, were glued together using commercial urea–formaldehyde resin (control board), solutions of rye flour and potato starch and two types of starch: oxidized and gelatinized. The density and density profile, compressive strength, modulus of elasticity, acoustic properties and thermal conductivity were determined in the produced boards. These studies show that when food components are used as binding agents in the manufacture of lightweight wood fiberboards, the properties obtained can be comparable with those of commercial boards manufactured using synthetic agents.