Ever since the discovery of SrAl₂O₄:Eu,Dy persistent afterglow material, that can intensively glow up to 20 h, the mechanism of long-lasting luminescence has been a popular area of research. The research is focused on discovering the mechanism of persistent luminescence in order to prolong the duration and intensity of afterglow in a controlled way. Although most researchers agree on the general things, there are still many unclarities and ambiguities to discuss upon. This review paper briefly sketches in the highlights of past research on the luminescence mechanism in SrAl₂O₄:Eu,Dy, mainly focusing on the research conducted in the past decade dedicated to clearing these ambiguities. This paper provides an overview of the latest persistent luminescence mechanisms offered by researchers.

In the current study, the antibacterial activity of positively and negatively charged spherical hematite (α-Fe₂O₃) nanoparticles (NPs) with primary size of 45 and 70 nm was evaluated against clinically relevant bacteria Escherichia coli (gram-negative) and Staphylococcus aureus (gram-positive) as well as against naturally bioluminescent bacteria Vibrio fischeri (an ecotoxicological model organism). α-Fe₂O₃ NPs were synthesized using a simple green hydrothermal method and the surface charge was altered via citrate coating. To minimize the interference of testing environment with NP’s physic-chemical properties, E. coli and S. aureus were exposed to NPs in deionized water for 30 min and 24 h, covering concentrations from 1 to 1000 mg/L. The growth inhibition was evaluated following the postexposure colony-forming ability of bacteria on toxicant-free agar plates. The positively charged α-Fe₂O₃ at concentrations from 100 mg/L upwards showed inhibitory activity towards E. coli already after 30 min of contact. Extending the exposure to 24 h caused total inhibition of growth at 100 mg/L. Bactericidal activity of positively charged hematite NPs against S. aureus was not observed up to 1000 mg/L. Differently from positively charged hematite NPs, negatively charged citrate-coated α-Fe₂O₃ NPs did not exhibit any antibacterial activity against E. coli and S. aureus even at 1000 mg/L. Confocal laser scanning microscopy and flow cytometer analysis showed that bacteria were more tightly associated with positively charged α-Fe₂O₃ NPs than with negatively charged citrate-coated α-Fe₂O₃ NPs. Moreover, the observed associations were more evident in the case of E. coli than S. aureus, being coherent with the toxicity results. Vibrio fischeri bioluminescence inhibition assays (exposure medium 2% NaCl) and colony forming ability on agar plates showed no (eco)toxicity of α-Fe₂O₃ (EC₅₀ and MBC > 1000 mg/L).