Moisture-resistant silicone coatings were prepared on the surface of potassium dihydrogen phosphate (KDP) crystal by means of spin-coating, in which hydrophobic-modified SiO₂ nanoparticles were embedded in a certain proportion. The refractive index of such coating can be tuned arbitrarily in the range of 1.21–1.44, which endows the KDP optical component with excellent transmission capability as well as the moisture proof effect. A dual-layer anti-reflective coating system was obtained by covering this silicone coating with a porous SiO₂ coating which is specially treated to enhance the moisture resistance. Transmittance of such a dual-layer coating system could reach 99.60% and 99.62% at 1064 nm and 532 nm, respectively, by precisely matching the refractive index of both layers. Furthermore, the long-term stability of this coating system has been verified at high humidity ambient of 80% RH for 27 weeks.

As an important nonlinear optical material, potassium dihydrogen phosphate (KDP) crystal is used in high-power laser beams as the core element of inertial confinement fusion. It is the most general method of single point diamond fly-cutting (SPDF) to produce high precision and crack-free KDP surfaces. Nevertheless, the cutting mechanism of such material remains unclear, and therefore needs further analysis. Firstly, the stress field, cutting force and cutting temperature under different working conditions are calculated by a KDP crystal cutting simulation model. Then, the rules and the cause of change and interaction mechanisms of force and temperature are analyzed by comparing the measurement experiments with simulations. Furthermore, the causes of chip formation and micro-cracks on the machined surface are analyzed based on thermo-mechanical coupling and chip morphology. The conclusion can be deduced: Although the temperature has not reached the phase transition temperature during the finishing process, under high cutting speeds and large unformed chip thickness, such as semi-finishing and roughing, the temperature can reach up to 180 °C or higher, and KDP crystals are very likely to phase transition—chip morphology also verifies this phenomenon.

Potassium dihydrogen phosphate (KDP) crystals, vital for high-power laser systems, pose significant machining challenges due to their brittleness, low hardness, and hygroscopic properties. Achieving crack-free, high-precision surfaces is essential but complex. Single-point diamond fly-cutting (SPDF) is the primary method, yet it exposes tools to high mechanical stress and heat, accelerating wear. In dry cutting, worn tools develop adhesive layers that detach, causing scratches and degrading surface quality. Traditional wet cutting improves surface finish but leaves residual fluids that contaminate the surface with metal ions, leading to optical degradation and fogging. To address these issues, this study explores mixed-fat-based minimum quantity lubrication (MQL) as a sustainable alternative, comparing two lubricants: biodegradable-base mixed ester lubrication (BBMEL) and hydrocarbon-based synthetic lubricant (HCBSL). A comprehensive evaluation method was developed to analyze surface roughness, tool wear, and subsurface damage under dry cutting, MQL-BBMEL, and MQL-HCBSL conditions. Experimental results show that MQL-BBMEL significantly enhances machining performance, reducing average surface roughness by 27.77% (Sa) and 44.77% (Sq) and decreasing tool wear by 25.16% compared to dry cutting, outperforming MQL-HCBSL. This improvement is attributed to BBMEL’s lower viscosity and higher proportion of polar functional groups, which form stable lubricating films, minimizing friction and thermal effects. Structural analyses confirm that MQL-BBMEL prevents KDP crystal deliquescence and surface fogging. These findings establish MQL-BBMEL as an eco-friendly, high-performance solution for machining brittle optical materials, offering significant advancements in precision machining for high-power laser systems.

A refractive index (RI) tunable polysiloxane coating was fabricated based on the cross-linked network structure embedded with mesoporous silica nanoparticles (MSNs), in which the MSNs were utilized to modulate the RI as well as to support the interior structure of the polysiloxane coating. The Si–O–Si inorganic backbone structure in combination with characteristics from the photopolymerization of active bonds produced the main cross-linked network structure, and controllable embedding of MSNs constructed the network-sphere structure. This approach eliminated the high-temperature post-treatment that was needed to remove the template, which ensures the safe application for temperature-sensitive laser crystal substrates and avoids coating structure collapse. In addition, degradation of the resulting coating can be minimized due to the similar chemical formation between MSN and polysiloxane coating. Hereby, a polysiloxane coating with expected spectral and laser damage-resistant properties can be obtained. This will facilitate the fabrication and application of a laser component with both high-transmission and high-flux capability for a high-power laser system.

In order to improve laser transmission efficiency at 1053 nm and 527 nm, a potassium deuterium phosphate (DKDP) crystal (a key component of high-power laser systems) needs a bi-layer antireflection coating system on its incident surface. UV-curable polysiloxane coatings with a refractive index varying from 1.500 to 1.485 were prepared through the polycondensation of a methacryloxy propyl trimethoxylsilane (MPS) monomer with a controllable degree of hydrolysis. Additionally, the influence rule of the coating structure on the refractive index was intensively studied, and the primary factors that dominate the hydrolysis process were discussed. Further refractive index adjustment was achieved using only a small amount of dopant based on the polysiloxane coating with refractive index of 1.485, allowing for high antireflection of the bi-layer coating system at desired wavelengths to be achieved. In addition, high laser damage resistance and remarkable mechanical properties of the coating were simultaneously realized through the incorporation of a minor quantity of dopants, which benefited from the successful modulation of the intrinsic refractive index of the polysiloxane coating.